Journal of Materials Engineering ›› 2006, Vol. 0 ›› Issue (4) : 52-55.

Effect of Content of Al on Microstructure and Mechanical Properties of Ni₃Al Base Alloy IC6E

QIAO Min¹, LI Shu-suo¹, MA Wen-you¹, SONG Jin-xia², HAN Ya-fang²

Author information +

History +

Abstract

In order to determine the optimum content of Al,alloys with the different amounts of Al(0%,0.4%,0.6%,0.8%)based on the master alloy composition of Ni-14.0Mo-7.2Al-0.025B(mass fraction/%) were prepared.The tensile strength at room temperature and stress rupture life at 1050℃/90MPa have been determined. The microstructures of the alloys have been studied by scanning electron microscopy.On the basis of the compromise of the microstructures and mechanical properties,the optimum content of Al was determined to be 7.8%.

Key words

Ni₃Al / aluminum content / microstructure / mechanical property

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations

QIAO Min, LI Shu-suo, MA Wen-you, SONG Jin-xia, HAN Ya-fang. Effect of Content of Al on Microstructure and Mechanical Properties of Ni₃Al Base Alloy IC6E[J]. Journal of Materials Engineering, 2006, 0(4): 52-55

References

[1] 肖程波,韩雅芳,殷克勤,等.定向凝固Ni₃Al基合金IC6的高温蠕变行为[J].材料工程,1996,(3):6-8.
[2] 肖程波,韩雅芳,张行安.定向凝固Ni₃Al基高温结构材料IC6A合金的研究[J].材料工程,2001,(6):3-6.
[3] 刘庆泉.Ni₃Al基IC6高温合金工程应用研究[J].航空材料学报,2003,23(增刊):209-214.
[4] 赵希宏,韩雅芳,谭永宁,等.定向凝固Ni₃Al基合金IC6[J].材料工程,1997,(9):13-15.
[5] 韩雅芳,李孙华.定向凝固铸造Ni₃Al基合金IC6[J].燃气涡轮试验与研究,1994,(1):48-51.
[6] 宋尽霞,肖程波,李树索,等.950℃长期时效对Ni₃Al基合金IC6的组织及力学性能的影响[J].金属学报,2002,38(3):250-254.