The influence of different precursors on the densification rate,microstructures and flexural strength of C/C composites,2-D needle punctured felt infiltrated by novel-ICVI,was investigated.The density of the resultant C/C composites was tested by volume method.The density distribution and the correlation between the density and the infiltration time were studied.The flexural strength was determined by three-point blending tests,and the microstructures of resultant materials and the morphology of fracture surface were observed by polarized light microscopy and scanning electron microscopy respectively.The result show that the densification rate of C/C composites using methane as precursors is lower than that using propylene as precursors before 100h infiltration,while after 100h infiltration the trend is reversed.The density of C/C composites tends to distribute uniformly,the flexural strength is 250.87MPa,the flexural modular is 29.29GPa,and the texture belongs to rough laminar when methane is used as precursor.The density of C/C composites distributes unevenly,the flexural strength is 102.75MPa,the flexural modular is 11.42GPa,and the texture belongs to smooth laminar when propylene is used as precursor.Therefore,the methane is an ideal precursor for novel-ICVI Process.
Key words
C/C composite /
precursor /
ICVI /
densification
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
References
[1] 李贺军.炭/炭复合材料[J].新型炭材料,2001,16(2):79-80.
[2] FITZER E.Effect of surface treatment and sizing of c-fibres on the mechanical properties of cfr thermosetting and thermoplastic polymers[J].Carbon,1987,25(4):455-467.
[3] 熊信柏,李贺军,黄剑锋.一种制备仿生生物活性钙磷涂层的新方法[J].稀有金属材料与工程,2004,3(3):313-316.
[4] ZHANG W G,HU Z J,H(U)TTINGER K J.Chemical vapor infiltration of carbon fiber felt:optimization of densification and carbon microstructure[J].Carbon,2002,40(14):2529-2545.
[5] 白瑞成,李贺军,徐向阳,等.一种制备C/C复合材的高效ICVI工艺[J].航空学报,2005,26(2):254-256.
[6] SAVAGE G.Carbon-carbon Composites[M].London:Chapman and Hall,1992.253-255.
[7] ZHANG W G,HüTTINGER K J.Densification of a 2D carbon fiber perform by isothermal,isobaric CVI:Kinetics and carbon microstructure[J].Carbon,2003,41(12):2325-2337.
[8] DELHAES P.Chemical vapor deposition and infiltration processes of carbon materials[J].Carbon,2002,40(5),641-657.
[9] BENZINGER W,HüTTINGER K J.Chemical vapor infiltration of pyrocarbon:Ⅰ Some kinetics considerations[J].Carbon,1996,34(12):1465-1471.
[10] BECKER A,HüTTINGER K J.Chemistry and kinetics of chemical vapor deposition of pyrocarbon-Ⅳ pyrocarbon deposition from methane in the low temperature regime[J].Carbon,1998,36(3):21-224.
[11] BECKER A,HüTTINGER K J.Chemistry and kinetics of chemical vapor deposition of pyrocarbon-Ⅲ pyrocarbon deposition from propylene and benzene in the low temperature regime[J].Carbon,1998,36(3):201-211.
[12] 白瑞成.炭/炭复合材中热解炭的微观结构与形成机理[J].稀有金属材料与工程,2005,34(Suppl2):274-279.
{{custom_fnGroup.title_en}}
Footnotes
{{custom_fn.content}}
PDF(972 KB)