Effect on Friction and Wear Behaviour of 45 Steel in Direct Current Constant Magnetic Field

SHANG Jian¹, ZHANG Yong-zhen¹, QIU Ming², XU Yong-zhi²

Author information +

History +

Abstract

The influence of D C constant magnetic field on tribological behaviour of 45 steel pin against disc in atmosphere was investigated.The results indicated that the wear loss decreased and friction coefficient went down,the worn surfaces were smooth and debris were fine obviously with a magnetic field.Microscopic analysis by SEM and EDS showed that more oxide-protective film formed on worn surface in the presence of a magnetic field.Oxidative wear mechanism and lubricated effect of debris were stated,which played an important role during the friction and wear.

Key words

direct current constant magnetic field / friction and wear / magnetic intensity / oxidation

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations

SHANG Jian, ZHANG Yong-zhen, QIU Ming, XU Yong-zhi. Effect on Friction and Wear Behaviour of 45 Steel in Direct Current Constant Magnetic Field[J]. Journal of Materials Engineering, 2009, 0(11): 4-7,13

References

[1] 高彩桥.摩擦金属学[M].哈尔滨:哈尔滨工业大学出版社,1988.78-92.
[2] MUJU M K,GHOSH A.A model of adhesive wear in the presence of a magnetic field[J].Wear,1977,41:103-116.
[3] MUJU M K,RADHAKRISHNA A.Wear of non-magnetic materials in the presence of a magnetic field[J].Wear,1980,58:49-58.
[4] MUJU M K,GHOSH A.Effect of a magnetic field on the diffusive wear of cutting tools[J].Wear,1980,58:137-145.
[5] NEEMA M L,PANDEY P C.The effect of magnetization on the wear of high speed steel tools[J].Wear,1980,59:355-362.
[6] HIRATSUKA K,SASADA T,NOROSE S.The magnetic effect on the wear of metals[J].Wear,1986,110:251-261.
[7] KUMAGAI K,TAKAHASHI M,KAMIYA O.Wear behaviour in the presence of magneticfields for pin-on-disc repeated dry wear tests[J].Tribology International,1992,25 (2):91-98.
[8] KUMAGAI K.Effects of magnetic fields on wear of ferromagnetic material[J].Bull Japan Soc of Prec Engg,1985,19 (1):43-48.
[9] KAZUO,KUMAGAI K,KOSHI SUZUKI,et al.Study on reduction in wear due to magnetization[J].Wear,1993,162-164:196-201.
[10] KAZUO,KUMAGA I K,KAMIYA O.Effects of magnetization on wear[J].Tribology Trasaction,1997,40:621-626.
[11] ZAIDI H,PAN L,PAULMIER D,et al.Influence of a magnetic field on the wear and friction behavior of a nickel/XC 48 steel couple[J].Wear,1995,181-183:799-804.
[12] MANSORI M EL,ZAIDI H,PAULMIER D,et al.Surface modifications of a non-ferro-magnetic copper/ferromagnetic steel XC48 couple in magnetized sliding contact[J].Surface and Coatings Technology,1996,86-87:511-515.
[13] MANSORI M EL,PAULMIER D.Effects of selective transfer on friction and wear of magnetized steel/graphite sliding couple[J].Applied Surface Science,1999,144-145:233-237.
[14] ZAIDI H,SENOUCI A.Influence of magnetic field on surface medication and the friction behavior of sliding couple aluminium/XC48 steel[J].Science Surface and Coatings Technology,1999,120-121:653-658.
[15] CHIN K J,ZAIDI H,NGUYEN M T,et al.Tribological behavior and surface analysis of magnetized sliding contact XC48 steel/XC48 steel[J].Wear,2001,250:470-476.
[16] CHIN K J,ZAIDI H,MATHIA T.Oxide film formation in magnetized sliding steel/steel contact analysis of the contact stress field and film failure mode[J].Wear,2005,259:477-481.
[17] ZAIDI H,AMIRAT M,FRENE J,et al.Magnetotribology of ferromagnetic/ferromagnetic sliding couple[J].Wear,2007,263:1518-1526.
[18] 董祥林,陈金荣,简小刚.磁场对中碳钢滑动摩擦磨损的影响[J].金属学报,1999,35(6):577-580.
[19] 陈金荣,董祥林.直流磁场对载荷变化时磁性材料摩擦磨损的影响[J].中国矿业大学学报,1999,28:35-38.
[20] 简小刚.直流稳恒磁场对铁磁性材料干滑动摩擦磨损影响初探[D].沈阳:中国科学院金属研究所硕士论文,1999.
[21] 李建明.磨损金属学[M].北京:冶金工业出版社,1990.108-109.