材料工程  2014, Vol. 0 Issue (8): 46-50    DOI: 10.11868/j.issn.1001-4381.2014.08.009
  材料与工艺 本期目录 | 过刊浏览 | 高级检索 |
不同稀土元素添加量对K465合金微观组织与力学性能的影响
王定刚, 肖程波, 宋尽霞, 李青, 余乾
北京航空材料研究院 先进高温结构材料重点实验室, 北京 100095
Effects of Rare-earth Elements Content on Microstructure and Mechanical Properties of K465 Superalloy
WANG Ding-gang, XIAO Cheng-bo, SONG Jin-xia, LI Qing, YU Qian
Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China
全文: PDF(3430 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 利用金相技术和扫描电镜(SEM)观察分析了稀土元素(Ce+Y)含量对K465合金微观组织的影响,并测试了合金的室温瞬时拉伸性能和高温持久性能。结果表明:(Ce+Y)含量为0.03%(质量分数,下同)的合金碳化物变质处理后形态良好,高温持久性能大幅提高;(Ce+Y)含量为0.06%的合金枝晶间区大块γ'相的边缘析出富(Ce+Y)相,从而使合金的持久性能明显下降。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
王定刚
肖程波
宋尽霞
李青
余乾
关键词 K465合金稀土元素微观组织力学性能    
Abstract:The effect of (Ce+Y) content on microstructure of K465 superalloy was examined by metallography technique and scanning electron microscope(SEM). The tensile properties at room temperature and the high temperature stress-rupture properties were tested. The results show that the morphology of carbides can be well modified by addition 0.03%(mass fraction) of (Ce+Y) which induces the improvement of high temperature stress-rupture properties. The high temperature stress-rupture properties decrease due to the precipitation of rich (Ce+Y) phases besides the large size γ' phases in the interdendritic area while adding 0.06% of (Ce+Y).
Key wordsK465 superalloy    rare-earth element    microstructure    mechanical property
收稿日期: 2014-04-28      出版日期: 2014-08-20
中图分类号:  TG132.3+2  
通讯作者: 王定刚(1978-),男,硕士,主要从事铸造高温合金方面研究工作,联系地址:北京市81信箱1分箱(100095),E-mail:wangdinggang@163.com     E-mail: wangdinggang@163.com
引用本文:   
王定刚, 肖程波, 宋尽霞, 李青, 余乾. 不同稀土元素添加量对K465合金微观组织与力学性能的影响[J]. 材料工程, 2014, 0(8): 46-50.
WANG Ding-gang, XIAO Cheng-bo, SONG Jin-xia, LI Qing, YU Qian. Effects of Rare-earth Elements Content on Microstructure and Mechanical Properties of K465 Superalloy. Journal of Materials Engineering, 2014, 0(8): 46-50.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2014.08.009      或      http://jme.biam.ac.cn/CN/Y2014/V0/I8/46
[1] 余乾,肖程波,宋尽霞,等.熔体处理时间对铸态镍基高温合金K465组织和力学性能的影响[J].航空材料学报,2005,25(1):1-4.YU Q, XIAO C B, SONG J X, et al. Melt treatment time on microstructure and mechanical properties of as-cast Ni-based superalloy K465[J]. Journal of Aeronautical Materials,2005,25(1): 1-4.
[2] 王定刚,肖程波,张国庆,等.壳型温度对K465合金微观组织和力学性能的影响[J]. 钢铁研究学报,2003,15(7):208-211.WANG D G, XIAO C B, ZHANG G Q, et al. Effect of shell mould temperature on microstructure and mechanical properties of superalloy K465[J]. Journal of Iron and Steel Research,2003,15(7):208-211.
[3] 张宏炜,肖程波,王定刚,等.不同冷却方式对K465合金组织和力学性能的影响[J]. 材料工程,2002,(12):33-35.ZHANG H W, XIAO C B, WANG D G, et al. Effect of cooling ways on the microstructure and mechanical properties of K465 alloy[J]. Journal of Materials Engineering,2002,(12):33-35.
[4] CUEFL R,BUSCAIL H,CAUDRON E,et a1.Oxidation of alumina formers at 1173K:effect of yttrium on implantation and yttrium alloying addition[J].Corrosion Science,2003,45(8):15-18.
[5] 徐志超,马培立.高温合金中微量元素的作用和控制[M].北京:冶金工业出版社.1987.420-438.XU Z C, MA P L. The Effect and Control of Trace Elements in Superalloys[M]. Beijing:Metallurgical Industry Press,1987.420-438.
[6] 郭建亭. 几种微量元素在高温合金中的作用与机理[J]. 中国有色金属学报,2011,21(3):465-475.GUO J T. Effects of several minor elements on superalloys and their mechanism[J]. The Chinese Journal of Nonferrous Metals,2011,21(3):465-475.
[7] RAHMEL A,SCHUTZE M.Mechanical aspects of the rare earth effect[J].Oxidation of Metals,1992,38(3-4):255-266.
[8] 王龙妹,杜挺,卢先利,等.微量稀土元素在钢中的作用机理及应用研究[J].稀土,2001,22(4):37-40.WANG L M, DU T, LU X L, et al. Study of behaviors and application of micro-rare earth elements in steel[J]. Chinese Rare Earths,2001,22(4):37-40.
[9] QIAN Y H, LI M S, DUO S W, et al. Effect of Ce+ ion implantation upon oxidation resistance of superalloy K38G[J]. Journal of Rare Earths,2005,23(1):63-67.
[10] GOLIGHTLY F A, STOTT F H, WOOD G C.The influence of yttrium additions on the oxide-scale adhesion to an iron-chromium-aluminum alloy[J].Oxidation of Metals,1976,10(3):163-187.
[11] FISHER G, DATTA P K, BUMELL-GRAY J S,et a1.The effects of active element additions on the oxidation performance of a platinum aluminide coating at 1100℃[J].Surface & Coatings Technology,1998,110(1):24-30.
[12] CASTELLO P, STOTT F H, GESMUNDO F. Yttrium-promoted selective oxidation of aluminium in the oxidation at 1100℃ of an eutectic Ni-Al-Cr3C2 alloy[J]. Corrosion Science,1999,41(5):90-95.
[13] WANG Rong-ming,HAN Ya-fang,ELIEZER D. Effects of yttrium on the microstructures and interfaces in a low expansion superalloy[J]. Chinese Journal of Aeronautics,2001,14(3):171-177.
[14] 周永军,张国英,王兆阳,等. 稀土对镍基高温合金性能影响的电子理论研究[J]. 稀有金属,2008,32(6):731-734. ZHOU Y J,ZHANG G Y, WANG Z Y,et a1. Study on influence of rare earth elements on properties of Ni-base superalloys through electron theory[J].Chinese Journal of Rare Metals, 2008,32(6):731-734.
[15] 邓波,冯涤,王旭东,等. 稀土元素钇对低膨胀合金GH909组织和性能的影响[J]. 钢铁研究学报,2003,15(7):111-114. DENG B, FENG D, WANG X D, et al. Effect of yttrium on microstructure and property of low expansive superalloy GH909[J]. Journal of Iron and Steel Research,2003,15(7):111-114.
[16] XIAO C B, HAN Y F. Effect of yttrium on performance of directionally solidified Ni3Al base alloy IC6[J].Transactions of Nonferrous Metals Society of China,1999,(Suppl1):335-339.
[17] XIAO C B, HAN Y F, ZHANG X A. Effect of silicon on the microstructure and mechanical properties of yttrium modified Ni3Al base alloy IC6[J].Acta Metallurgica Sinica:English Letters,1998,11(6):437-441.
[1] 赵云松, 张迈, 郭小童, 郭媛媛, 赵昊, 刘砚飞, 姜华, 张剑, 骆宇时. 航空发动机涡轮叶片超温服役损伤的研究进展[J]. 材料工程, 2020, 48(9): 24-33.
[2] 许凤光, 刘垚, 马文江, 张憬. 退火工艺对Zn/AZ31/Zn复合板材界面微观结构及力学性能的影响[J]. 材料工程, 2020, 48(8): 142-148.
[3] 郝思嘉, 李哲灵, 任志东, 田俊鹏, 时双强, 邢悦, 杨程. 拉曼光谱在石墨烯聚合物纳米复合材料中的应用[J]. 材料工程, 2020, 48(7): 45-60.
[4] 唐大秀, 刘金云, 王玉欣, 尚杰, 刘钢, 刘宜伟, 张辉, 陈清明, 刘翔, 李润伟. 柔性阻变存储器材料研究进展[J]. 材料工程, 2020, 48(7): 81-92.
[5] 张梦清, 于鹤龙, 王红美, 尹艳丽, 魏敏, 乔玉林, 张伟, 徐滨士. 感应熔覆原位合成TiB增强钛基复合涂层的微结构与力学性能[J]. 材料工程, 2020, 48(7): 111-118.
[6] 王彦菊, 姜嘉赢, 沙爱学, 李兴无. 新型高温合金材料建模及涡轮盘成形工艺模拟[J]. 材料工程, 2020, 48(7): 127-132.
[7] 赵强, 祝文卉, 邵天巍, 帅焱林, 刘佳涛, 王冉, 张利, 梁晓波. Ti-22Al-25Nb合金惯性摩擦焊接头显微组织与力学性能[J]. 材料工程, 2020, 48(6): 140-147.
[8] 李和奇, 王晓民, 曾宏燕. 热处理对FeCrMnNiCox合金微观组织及力学性能的影响[J]. 材料工程, 2020, 48(6): 170-175.
[9] 李英民, 马鸣檀, 任玉艳, 刘桐宇. 稀土La掺杂Mg2Si的几何结构、弹性性能和电子结构的第一性原理研究[J]. 材料工程, 2020, 48(4): 100-107.
[10] 李淑文, 赵孔银, 陈康, 李金刚, 赵磊, 王晓磊, 魏俊富. TiO2共混丝朊接枝聚丙烯腈过滤膜制备及性能研究[J]. 材料工程, 2020, 48(3): 47-52.
[11] 赵新龙, 金鑫, 丁成成, 俞娟, 王晓东, 黄培. 热处理时间对聚甲基丙烯酰亚胺(PMI)泡沫结构和性能的影响[J]. 材料工程, 2020, 48(3): 53-58.
[12] 叶寒, 黄俊强, 张坚强, 李聪聪, 刘勇. 纳米WC增强选区激光熔化AlSi10Mg显微组织与力学性能[J]. 材料工程, 2020, 48(3): 75-83.
[13] 姚小飞, 田伟, 李楠, 王萍, 吕煜坤. 铜导线表面热浸镀PbSn合金镀层的组织与性能[J]. 材料工程, 2020, 48(3): 148-154.
[14] 刘也川, 张松, 谭俊哲, 关锰, 陶邵佳, 张春华. 机械滚压对A473M钢疲劳性能的影响[J]. 材料工程, 2020, 48(3): 163-169.
[15] 李昊卿, 田玉晶, 赵而团, 郭红, 方晓英. S32750双相不锈钢相界与晶界特征对其力学性能和耐蚀性能的影响[J]. 材料工程, 2020, 48(2): 133-139.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn