Abstract：By establishing the intra-granular ferrite nucleation model and conducting a series mathematical calculation, it was found that the nucleation energy of inclusion in irregular shape is lower than that in spherical shape, which is easier to induce the ferrite nucleation. Moreover, the influence factors of intra-granular ferrite nucleation induced by spherical inclusions were also analyzed. The results show that it is adverse to the nucleation of ferrite when the inclusion size is too small, while it has little effect when the size is larger than 0.15μm. Besides, the smaller of the wetting angle, the easier of the nucleation. When the wetting angle is between 70° and 90°, the ferrite is easily induced by spherical inclusions in the form of normal triangular pyramid. However, when the wetting angle is less than 70°, the ferrite is precipitated in the form of spherical. The precipitation rate of ferrite in the form of triangular pyramid is higher than that of spherical. A group of experiments were also verified that irregular inclusions could induce the nucleation of ferrite, while it had little effect when the size is larger than 0.15μm.
 LI X B, MIN Y, YU Z, et al. Effect of Mg addition on nucleation of intragranular acicular ferrite in Al-killed low carbon steel [J]. Journal of Iron and Steel Research International, 2016, 23(5):415-421.
 WANG C, WANG Z D, WANG G D. Effect of hot deformation and controlled cooling process on microstructures of Ti-Zr deoxidized low carbon steel [J]. ISIJ International, 2016, 56(10):1800-1807.
 李鹏, 李光强, 郑万. Al-Ti脱氧对非调质钢中MnS析出行为及组织的影响[J]. 钢铁研究学报, 2013, 25(11):49-56. LI P, LI G Q, ZHENG W. Effect of Al-Ti deoxidation on MnS precipitation and the microstructure of non-quenched and tempered steel[J]. Journal of Iron and Steel Research, 2013, 25(11):49-56.
 万响亮, 吴开明, 王恒辉, 等. 氧化物冶金技术在大线能量焊接用钢的应用[J]. 中国冶金, 2015, 25(6):6-12. WAN X L, WU K M, WANG H H, et al. Applications of oxide metallurgy technology on high heat input welding steel[J]. China Metallurgy, 2015, 25(6):6-12.
 郑万, 吴振华, 李光强, 等. Ti-Mg复合脱氧和硫含量对钢中夹杂物特征及MnS析出行为的影响[J]. 工程科学学报, 2015, 37(3):292-300. ZHENG W, WU Z H, LI G Q, et al. Effect of Ti-Mg complex deoxidation and sulfur content on the characteristics of inclusions and the precipitation behavior of MnS[J]. Chinese Journal of Engineering, 2015, 37(3):292-300.
 阿荣, 潘川, 赵琳, 等. Ti对大线能量焊接焊缝组织和性能的影响[J]. 钢铁研究学报, 2014, 26(6):47-52. A R, PAN C, ZHAO L, et al. Effect of Ti on microstructure and mechanical properties in high heat input welds [J]. Journal of Iron and Steel Research, 2014, 26(6):47-52.
 BOTT I S, RIOS P R. On the effectiveness of inclusions as nucleation sites in weld deposits[J]. Scripta Materialia, 1998, 38(8):1269-1274.
 王巍, 付立铭. 夹杂物/析出相尺寸对晶内铁素体形核的影响[J]. 金属学报, 2008, 44(6):723-728. WANG W, FU L M. Effect of the inclusion/precipitate size on the intragranular ferrite nucleation [J]. Acta Metallurgica Sinica, 2008, 44(6):723-728.
 朱立光, 吴耀光, 张彩军, 等. 夹杂物诱发晶内铁素体形核的动力学模型[J]. 特殊钢, 2014, 35(3):1-4. ZHU L G,WU Y G, ZHANG C J, et al. Dynamics model of intra-granular ferrite nucleation induced by inclusions [J]. Special Steel, 2014, 35(3):1-4.
 余永宁. 冶金学原理习题解答[M]. 北京: 冶金工业出版社, 2004. YU Y N. Guide to Exercises of Principle of Metallurgy [M]. Beijing: Metallurgical Industry Press, 2004.
 朱景川, 来忠红. 固态相变原理[M]. 北京: 科学出版社, 2010. ZHU J C, LAI Z H. Principle of Solid-state Phase Transformation [M]. Beijing: Science Press, 2010.
 国旭明, 钱百年, 王玉. 夹杂物对微合金钢熔敷金属针状铁素体形核的影响[J]. 焊接学报, 2007, 28(12):5-12. GUO X M, QIAN B N, WANG Y. Effects of nonmetallic inclusions on acicular ferrite nucleation in deposited metals of micro-alloyed steel [J]. Transactions of the China Welding Institution, 2007, 28(12):5-12.
 OFFERMAN S E, Van DIJK N H, SIETSMA J, et al. Grain nucleation and growth during phase transformations[J]. Science, 2002, 298(1):1003-1005.
 李占杰. 管线钢焊接热影响区针状铁素体的形成研究[D]. 武汉: 华中科技大学, 2007. LI Z J. Acicular ferrite formation in HAZ of pipeline steel [D]. Wuhan: Huazhong University of Science &Technology, 2007.
 TOMITA Y, SAITO N, TSUZUKI T, et al. Improvement in HAZ toughness of steel by TiN-MnS addition[J]. ISIJ International, 1994, 34(10):829-835.
 Al-HAJERI K F. The grain coarsening and subsequent transformation of austenite in the HSLA steel during high temperature thermomechanical processing[D]. Pittsburgh, PA: University of Pittsburgh, 2005.
 吴开明, 李自刚. 低碳微合金钢中的晶内铁素体及组织控制[J]. 钢铁研究学报, 2007, 19(10):1-5. WU K M, LI Z G. Intragranular ferrite and microstructure control in low carbon microalloyed steels[J]. Journal of Iron and Steel Research, 2007, 19(10):1-5.