冷挤压GH4169合金孔结构疲劳性能与断口分析
王欣1,2, 陈星3, 胡仁高4, 胡博4, 许春玲1,2, 汤智慧1,2, 古远兴4
1. 中国航发北京航空材料研究院 表面工程研究所, 北京 100095;
2. 中国航发北京航空材料研究院 航空材料先进腐蚀与防护航空科技重点实验室, 北京 100095;
3. 中国航发北京 航空材料研究院检测研究中心, 北京 100095;
4. 中国航发四川燃气涡轮研究院, 成都 610500
Fatigue property and fracture analysis on cold-expanded hole structure of GH4169 alloy
WANG Xin1,2, CHEN Xing3, HU Ren-gao4, HU Bo4, XU Chun-ling1,2, TANG Zhi-hui1,2, GU Yuan-xing4
1. Surface Engineering Institution, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China;
2. Aviation Key Laboratory of Advanced Corrosion and Protection on Aviation Materials, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China;
3. Testing Research Center, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China;
4. AECC Sichuan Gas Turbine Establishment, Chengdu 610500, China
全文: PDF(2754 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 对GH4169合金中心孔板材进行冷挤压强化,研究其挤压前后825 MPa/600℃/R=0.1疲劳寿命,分析挤压前后表面粗糙度变化和疲劳过程中的残余应力场演化,并细致观察两件挤压试样不同寿命(分别为25105周次和10719周次)断口以分析表面完整性对疲劳过程的作用。结果表明:相比原始试样,冷挤压强化后试样中值疲劳寿命估计量提高了1倍,挤压后较低的表面粗糙度和疲劳过程中稳定的残余应力场是疲劳寿命提高的主要原因。同时,挤压后疲劳寿命标准差增大。由断口定量分析可知,两件试样距疲劳源区0.1 mm之后的扩展寿命相当,而萌生寿命(分别为18786周次和5915周次)却相差巨大。造成孔挤压后寿命分散性大的原因是0.1 mm以内的裂纹萌生寿命差别。为提高孔结构疲劳性能稳定性,挤压时应注意近表层表面完整性的控制。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
王欣
陈星
胡仁高
胡博
许春玲
汤智慧
古远兴
关键词 冷挤压孔结构疲劳断口定量分析    
Abstract:Cold expansion (CE) was applied on the centre-hole plate of GH4169 alloy. The fatigue lives, as received and after CE, were investigated at 825 MPa/600 ℃/R=0.1. Surface roughness before and after CE, residual stress profiles during fatigue cycles were studied. And the influence of surface integrity on fatigue process was analyzed by the careful fracture observation with two CE samples of different lives (25105 cycles and 10719 cycles). The results show that the median fatigue life estimation of specimens after CE doubles compared with as-received. The lower surface average roughness after CE and the stable residual stress profile during fatigue process are the main reasons for fatigue life promotion. However, the standard deviation of fatigue lives increases after CE. The fractographic quantitative analysis shows the propagation lives of two specimens beyond 0.1 mm from fatigue source are considered, but initiation lives (18786 cycles and 5915 cycles, respectively) are of great difference. As a contrast, the reason of the big dispersion about CE fatigue lives is the different initiation life within 0.1 mm from the source. Therefore, the attention should be paid to the surface integrity control of near surface during cold expansion to improve the stability of hole structure fatigue property.
Key wordscold expansion    hole structure    fatigue    fractographic quantitative analysis
收稿日期: 2018-08-31      出版日期: 2020-06-15
中图分类号:  TG668  
通讯作者: 王欣(1983-),男,研究员,研究方向为抗疲劳的表面强化技术,联系地址:北京市81信箱5分箱(100095), rasheed990918@163.com     E-mail: rasheed990918@163.com
引用本文:   
王欣, 陈星, 胡仁高, 胡博, 许春玲, 汤智慧, 古远兴. 冷挤压GH4169合金孔结构疲劳性能与断口分析[J]. 材料工程, 2020, 48(6): 156-162.
WANG Xin, CHEN Xing, HU Ren-gao, HU Bo, XU Chun-ling, TANG Zhi-hui, GU Yuan-xing. Fatigue property and fracture analysis on cold-expanded hole structure of GH4169 alloy. Journal of Materials Engineering, 2020, 48(6): 156-162.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2018.001058      或      http://jme.biam.ac.cn/CN/Y2020/V48/I6/156
[1] 张智轩,石多奇,杨晓光. 含销钉孔边裂纹的某压气机轮盘裂纹扩展分析[J]. 航空动力学报, 2016, 31(3): 567-574. ZHANG Z X, SHI D Q, YANG X G. Analysis of crack propagation for a compressor disk with cracks on pin holes[J]. Journal of Aerospace Power, 2016, 31(3): 567-574.
[2] KOUL A K, BELLINGER N C, GOULD G. Damage-tolerance-based life prediction of aeroengine compressor discs: Ⅱ a probabilistic fracture mechanics approach[J]. International Journal of Fatigue, 1990, 12(5):388-396.
[3] CHINNARAJ K, SATHYA P M,LAKSHMANA R C. Effect of bolt hole residual stresses on fatigue performance of truck frame rail structures[J]. Applied Mechanics and Materials, 2013, 300/301:1089-1098.
[4] 杨伟,徐伟. BR700系列发动机高压压气机设计及结构特征[J]. 燃气涡轮的试验与研究, 2014, 27(3): 30-34. YANG W, XU W. HPC design and structure features of BR700 series engine[J]. Gas Turbine Experiment and Research, 2014, 27(3): 30-34.
[5] 郑旭东,蔚夺魁. 某发动机高压压气机篦齿盘均压孔孔边裂纹故障分析[J]. 航空发动机, 2013, 39(3): 49-54. ZHENG X D, WEI D K. Study of vent hole crack failure for an aeroengine labyrinth seal disk[J]. Aeroengine, 2013, 39(3): 49-54.
[6] 刘庆瑞,刘玉萍. 发动机第四级压气机盘裂纹失效分析[J]. 航空发动机, 1999(2): 38-41. LIU Q R, LIU Y P. Failure analysis of engine 4th stage compressor disc crack[J]. Aeroengine, 1999(2): 38-41.
[7] 陈秋任,郭海丁,刘小刚. 涡轮盘双轴对称异形孔结构建模与优化[J]. 航空动力学报, 2013, 28(6): 1250-1255. CHEN Q R, GUO H D, LIU X G. Modeling and optimization for the structure of biaxial symmetry non-circular hole of turbine disk [J].Journal of Aerospace Power, 2013, 28(6): 1250-1255.
[8] 魏昕. 镍基高温合金工件异形孔加工工艺的研究[J]. 工具技术, 2000, 36(6): 19-23. WEI X.Study on machining process of shaped hole in Ni-base super-heat-resistant alloy workpieces[J]. Tool Engineering, 2000, 36(6): 19-23.
[9] BALL D L, LOWRY D R. Experimental investigation on the effects of cold expansion of fastener holes[J]. Fatigue & Fracture of Engineering Materials & Structures, 1998, 21(1):17-34.
[10] FARHANGDOOST K, HOSSEINI A. Finite element modeling of mandrel speed in cold expansion process[J]. International Journal of Structural Integrity, 2012, 3(4):441-456.
[11] 王欣,胡仁高,胡博,等. 喷丸强化对GH4169合金孔结构高温低周疲劳性能的影响[J]. 中国表面工程, 2015, 28(6): 7-12. WANG X, HU R G, HU B, et al. Effects of shot peening on high-temperature low-cycle fatigue property of GH4169 superalloy with hole structure[J]. China Surface Engineering, 2015, 28(6): 7-12.
[12] 杨兴宇,董立伟,郑小梅,等. 某压气机轮盘均压孔挤压强化数值仿真和挤压头设计[J]. 航空动力学报, 2013, 28(8):1769-1776. YANG X Y, DONG L W, ZHENG X M, et al. Simulation of extrusion strengthening of pressure equalizing hole of an engine compressor disc and design of extrusion heads[J]. Journal of Aerospace Power, 2013, 28(8):1769-1776.
[13] 杨兴宇,孟祥明,董立伟,等. 薄板孔边挤压强化对高周疲劳寿命影响的试验[J]. 航空动力学报, 2011, 26(2):362-369. YANG X Y, MENG X M, DONG L W, et al. High cycle fatigue life experiment of sheet metal with coldworking hole[J]. Journal of Aerospace Power, 2011, 26(2):362-369.
[14] 罗学昆,王欣,胡仁高,等. 孔挤压强化对Inconel 718高温合金疲劳性能的影响[J]. 中国表面工程, 2016, 29(3): 116-122. LUO X K, WANG X, HU R G, et al. Effects of hole cold expansion on fatigue property of Inconel 718 superalloy[J]. China Surface Engineering, 2016, 29(3): 116-122.
[15] 王欣,胡仁高,胡博,等. 孔挤压对于高温合金GH4169孔结构高温疲劳性能的影响[J]. 航空动力学报, 2017, 32(1): 89-95. WANG X, HU R G, HU B, et al. Effect of hole-expansion on high-temperature fatigue property of GH4169 superalloy hole structure [J]. Journal of Aerospace Power, 2017, 32(1): 89-95.
[16] SANGID M D, STORI J A, FERRIERA P M. Process characterization of vibrostrengthening and application to fatigue enhancement of aluminum aerospace components—part Ⅰ experimental study of process parameters[J]. International Journal of Advanced Manufacturing Technology, 2011, 53(5/8):545-560.
[17] SANGID M D, STORI J A, FERRIERA P M. Process characterization of vibrostrengthening and application to fatigue enhancement of aluminum aerospace components—part Ⅱ: process visualization and modeling[J]. International Journal of Advanced Manufacturing Technology, 2011, 53(5/8):561-575.
[18] 陶春虎,习年生,张卫方,等. 断口反推疲劳应力的新进展[J]. 航空材料学报, 2000, 20(3): 158-163. TAO C H, XI N S, ZHANG W F, et al. Resent development of fractographic restrostimation on determining fatigue stress[J]. Journal of Aeronautical Materials, 2000, 20(3): 158-163.
[19] 刘新灵,张峥,陶春虎.疲劳断口定量分析[M].北京:国防工业出版社, 2010. LIU X L, ZHANG Z, TAO C H. Quantitative analysis of fatigue fracture[M]. Beijing: National Defense Industry Press, 2010.
[1] 王欣, 许春玲, 李臻熙, 裴传虎, 汤智慧. 喷丸强度和表面覆盖率对TC4钛合金室温疲劳性能的影响[J]. 材料工程, 2020, 48(9): 138-143.
[2] 王志远, 邢志国, 王海斗, 单德彬. 非金属夹杂物特性对钢铁材料疲劳性能影响的研究进展[J]. 材料工程, 2020, 48(5): 1-12.
[3] 赵慧生, 陈国清, 盖鹏涛, 李志强, 周文龙, 付雪松. 拉-拉疲劳载荷下钛合金湿喷丸的残余应力松弛及再次喷丸工艺[J]. 材料工程, 2020, 48(5): 136-143.
[4] 刘也川, 张松, 谭俊哲, 关锰, 陶邵佳, 张春华. 机械滚压对A473M钢疲劳性能的影响[J]. 材料工程, 2020, 48(3): 163-169.
[5] 董建民, 李嘉荣, 韩梅. 检验腐蚀对镍基单晶高温合金高周疲劳性能的影响[J]. 材料工程, 2020, 48(1): 77-83.
[6] 刘凯, 崔荣洪, 侯波, 何宇廷, 牛欢. PVD薄膜传感器裂纹检测概率测定与分析[J]. 材料工程, 2019, 47(9): 160-166.
[7] 刘石双, 仇平, 蔡建明, 李娟, 黄旭, 于辉, 刘利刚. Ti60钛合金室温保载疲劳性能及断裂行为[J]. 材料工程, 2019, 47(7): 112-120.
[8] 郭军, 杨卯生, 卢德宏, 李新宇. Cr4Mo4V轴承钢旋转弯曲疲劳寿命及疲劳裂纹萌生机理[J]. 材料工程, 2019, 47(7): 134-143.
[9] 韩梅, 谢洪吉, 李嘉荣, 董建民, 岳晓岱, 喻健, 杨亮. 再结晶对DD6单晶高温合金轴向高周疲劳性能的影响[J]. 材料工程, 2019, 47(6): 161-168.
[10] 张先炼, 何晓聪, 邢保英, 曾凯. TA1纯钛与1420铝锂合金异质薄板自冲铆接微动疲劳特性[J]. 材料工程, 2019, 47(4): 143-151.
[11] 周航, 张峥. AlSi10Mg(Cu)铸铝合金的热疲劳裂纹萌生及早期扩展行为[J]. 材料工程, 2019, 47(3): 131-138.
[12] 山泉, 张亚峰, 张哲轩, 李祖来, 蒋业华, 王鹏飞. 钨含量对WCP/钢基表层复合材料压缩性能及热疲劳行为的影响[J]. 材料工程, 2019, 47(2): 115-121.
[13] 赵玲, 刘光磊, 张思源, 李茂军, 刘简宁, 李明辉. 固溶时效深冷复合处理对ZCuAl10Fe3Mn2合金微观组织和热疲劳性能的影响[J]. 材料工程, 2019, 47(12): 63-70.
[14] 许良, 黄双君, 回丽, 王磊, 周松, 赵晴. TB6钛合金疲劳小裂纹扩展行为[J]. 材料工程, 2019, 47(11): 171-177.
[15] 赵景云, Bamber BLACKMAN, 颜悦, 张旋, 张晓雯. YB-DM-10航空定向有机玻璃疲劳裂纹扩展性能[J]. 材料工程, 2018, 46(8): 156-162.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn