材料工程  1991, Vol. 0 Issue (6): 30-33    
  工艺 本期目录 | 过刊浏览 | 高级检索 |
55Al-Zn合金镀层耐蚀机理的研究
虞万钟, 张长桥
山东工业大学
Corrosion Mechanism of 55 Al-Zn Hot Dip Coating
Yu Wanzhong, Zhang Changqiao
Shandong Polytechnical University
全文: PDF(319 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 通过对热浸镀铝锌合金层在不同介质中的腐蚀产物的表面电阻测量、交流阻抗法测Rp及Cd、X-射线衍射等试验,从宏观到微观得出相互一致的结论,即55Al-Zn层在各种介质的腐蚀产物为一层致密的、不易导电的异相薄膜,它主要由含结晶水的硫酸铝锌的非晶体物质组成。它的生成有助于提高55Al-Zn层的耐蚀性。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
虞万钟
张长桥
Abstract:Based on the determination of surface resistance, alternative impedence, X-ray diffraction analysis and etc., we have proved that the corrosion product is a protective film composed of aluminum compound with densitive structure and low electrical conductivity, which may act as barrier to further attack.
Key wordsHot dip coating    Protective film    Alternative Impedence
     出版日期: 1991-12-20
引用本文:   
虞万钟, 张长桥. 55Al-Zn合金镀层耐蚀机理的研究[J]. 材料工程, 1991, 0(6): 30-33.
Yu Wanzhong, Zhang Changqiao. Corrosion Mechanism of 55 Al-Zn Hot Dip Coating. Journal of Materials Engineering, 1991, 0(6): 30-33.
链接本文:  
http://jme.biam.ac.cn/new/CN/      或      http://jme.biam.ac.cn/new/CN/Y1991/V0/I6/30
No related articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn