材料工程  2004, Vol. 0 Issue (11): 22-27    
  研究与应用 本期目录 | 过刊浏览 | 高级检索 |
化学法细化高温合金K4169的低周疲劳性能研究
黄太文1, 刘林1, 杨爱民2, 熊玉华3, 赵志龙1
1. 西北工业大学凝固技术国家重点实验室, 西安, 710072;
2. 西安石油学院机械系, 西安, 710065;
3. 清华大学机械工程系, 北京, 100084
Effect of Structure Refinement by Addition of Refiner on LCF Properties of Cast Superalloy K4169
HUANG Tai-wen1, LIU Lin1, YANG Ai-min2, XIONG Yu-hua3, ZHAO Zhi-long1
1. State Key Laboratory of Solidification Processing, Northwestern Poly technical University, Xi’an, 710072, China;
2. Department of Mechanical Engineering, Xi’an Petroleum Institute, Xi’an, 710065, China;
3. Department of Mechanical Engineering, Tsinghua University, Beijing, 100084, China
全文: PDF(996 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 采用一种新型中间合金复合细化剂,在常规生产工艺条件下对高温合金K4169铸件进行了晶粒细化.测试了常规工艺和细晶铸造工艺两种试样的常温和中温(700℃)条件下的低周疲劳性能.结果表明,这一新型工艺方法能有效细化高温合金K4169晶粒.细晶试样的室温低周疲劳性能有较大的提高,且数据的分散性有所改善;在中温时,疲劳寿命的优劣和疲劳应变幅有关:在小应变幅条件下,细晶仍然有较高的疲劳寿命,在大应变幅条件下,细晶疲劳寿命比粗晶有所降低,但数据的稳定性较好.
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
黄太文
刘林
杨爱民
熊玉华
赵志龙
关键词 细化剂晶粒细化高温合金低周疲劳性能    
Abstract:The ingots of cast superalloy K4169 was refined with the addition of a trace of intermetallic compounds to the melt under conventional casting condition. The low cycle fatigue(LCF) properties were tested both for normal and refined test bars. The results show that the grains can be refined to ASTM 1.7. As a result, LCF life of refined test bars is 1.2-2 times compared to that of normal ones at room temperature. As a contrast, LCF properties at 700℃ are different, depending on the total strain amplitude. LCF life for refined samples are superior than coarse ones at small total strain amplitude, and inferior at high total strain amplitude. Fatigue data fluctuation is improved of fined grains at all conditions.
Key wordsrefiner    grain refinement    superalloy    LCF
收稿日期: 2004-01-14      出版日期: 2004-11-20
中图分类号:  TG113.25  
  TG146.1  
基金资助:国家重点基础研究计划资助项目(G2000067202)
作者简介: 黄太文(1975- ),男,博士生,主要从事高温合金的组织控制及性能的研究,联系地址:西北工业大学543信箱(710072).
引用本文:   
黄太文, 刘林, 杨爱民, 熊玉华, 赵志龙. 化学法细化高温合金K4169的低周疲劳性能研究[J]. 材料工程, 2004, 0(11): 22-27.
HUANG Tai-wen, LIU Lin, YANG Ai-min, XIONG Yu-hua, ZHAO Zhi-long. Effect of Structure Refinement by Addition of Refiner on LCF Properties of Cast Superalloy K4169. Journal of Materials Engineering, 2004, 0(11): 22-27.
链接本文:  
http://jme.biam.ac.cn/new/CN/      或      http://jme.biam.ac.cn/new/CN/Y2004/V0/I11/22
[1] 刘发信,袁文明.高温合金细晶铸造技术的发展和应用[J].材料工程,1995,(5):7-11.
[2] MONDOLF L F. Grain refinement in the casting of nonferrous Alloys[A].ABBASCHIAN G J, DAVIED S A. Grain Refinement in Casting and Welds [C].New York: The Metallurgical Society of AIME, 1983.3 - 50
[3] DENZINE A F. Advanced casting Technology[A].AGARD Conference Proceeding[C].Paris: Advisory Group for Aerospace Research and Development, 1982.12 - 16.
[4] 熊玉华.K4169高温合金化学法晶粒细化工艺及机理的研究[D].西安:西北工业大学,2000.
[5] WOULDS M,BENSON H Development of a conventional fine grain process[A].GELL M. Superalloy 1984 [C].New York:Met Soc TMS-AIME, 1984.3 - 12.
[6] BOUSE G K. Mechanical properties of microcast-x alloy 718 fine grain investment casting[A].LORIA A. Superalloy 718-Metallurgy and Application[ C].Pittsburgh: TMS, 1989.69 - 73.
[7] DENNISON J P. Grain refinement by the introduction to the melt of oxide particles pre-dispersed in metal strip[A].ABBASCHIAN G J, DAVIED S A. Grain Refinement in Casting and Welds [ C].New York: The Metallurgical Society of AIME, 1983. 139 - 149.
[8] 熊玉华,李培杰.铸造工艺参数和细化剂对K4169高温合金铸态组织的影响,晶粒组织及晶粒细化机理[J].金属学报,2002,38(5):529 533.
[9] 刘林.镍基高温合金铸件的晶粒组织控制-铸造工艺参数的影响[J].航空学报,1994,15(11):1357-1361.
[10] GAUTHIER P, DE RABAUDY H, AUVINET J. Secondary cracking process during fatigue crack propagation [ J].Engineering Fracture Mechanics , 1973, 5(4) :977 - 981.
[11] SYMPOSIUM N P L,STATIONAR H M. The relation between the structure and mechanical properties of metals [ M].London:Her Majesty's Stationary Office , 1963. 122.
[12] NILSSON J O, THORVALDSSON T. Low cycle-fatigue behaviour of alloy 800h at 600℃ -effect of grain size and γ-precipitate dispersion[J].Fatigue & Structures, 1985,8(4):373.
[13] 陈国良.高温合金学[M].北京:冶金工业出版社,1987.142-144.
[14] 陈国祥,许静君.K18高温合金低周疲劳性能影响因素的研究[A].荣科.铸造高温合金进展[C].北京:中国科学技术出版社,1993.188-193.
[1] 李慧中, 杨雷, 王岩, 谭钢, 黄钲钦, 刘敏学. 热挤压态Ni-Co-Cr基粉末高温合金热加工行为[J]. 材料工程, 2020, 48(9): 115-123.
[2] 曲敬龙, 易出山, 陈竞炜, 史玉亭, 毕中南, 杜金辉. GH4720Li合金中析出相的研究进展[J]. 材料工程, 2020, 48(8): 73-83.
[3] 刘欢, 张瑞英, 李金轩, 杨森, 闫晗. TiO2粒径对Al-TiO2-C细化剂组织及细化效果的影响[J]. 材料工程, 2020, 48(8): 126-133.
[4] 王彦菊, 姜嘉赢, 沙爱学, 李兴无. 新型高温合金材料建模及涡轮盘成形工艺模拟[J]. 材料工程, 2020, 48(7): 127-132.
[5] 杨万鹏, 李嘉荣, 刘世忠, 赵金乾, 史振学, 王效光. 一种第三代单晶高温合金中高温横向持久性能[J]. 材料工程, 2020, 48(7): 139-145.
[6] 王旭青, 彭子超, 罗学军, 马国君, 武丹. 时效制度对挤压+锻造工艺路线FGH95粉末高温合金组织和性能的影响[J]. 材料工程, 2020, 48(5): 120-126.
[7] 黄敏, 张功, 王栋, 李辉, 董加胜, 楼琅洪. 复杂镍基单晶铸件显微孔洞的形成机理[J]. 材料工程, 2020, 48(2): 123-132.
[8] 袁继慧, 陈辉明, 谢伟滨, 魏海根, 汪航, 杨斌. Cu-Cr-Ti-Si合金加工软化的机理[J]. 材料工程, 2020, 48(11): 140-146.
[9] 秦健朝, 崔仁杰, 黄朝晖. 小角度晶界对DD5镍基单晶高温合金中、高温条件下力学性能的影响[J]. 材料工程, 2020, 48(10): 114-122.
[10] 董建民, 李嘉荣, 韩梅. 检验腐蚀对镍基单晶高温合金高周疲劳性能的影响[J]. 材料工程, 2020, 48(1): 77-83.
[11] 刘承林, 苏海军, 张军, 刘林, 傅恒志. 静磁场对定向凝固镍基高温合金组织影响的研究进展[J]. 材料工程, 2019, 47(9): 13-20.
[12] 韩梅, 喻健, 李嘉荣, 谢洪吉, 董建民, 杨岩. 喷丸对DD6单晶高温合金拉伸性能的影响[J]. 材料工程, 2019, 47(8): 169-175.
[13] 罗亮, 肖程波, 陈晶阳, 李青, 戴圣龙. 工业燃气轮机涡轮叶片用铸造高温合金研究及应用进展[J]. 材料工程, 2019, 47(6): 34-41.
[14] 韩梅, 谢洪吉, 李嘉荣, 董建民, 岳晓岱, 喻健, 杨亮. 再结晶对DD6单晶高温合金轴向高周疲劳性能的影响[J]. 材料工程, 2019, 47(6): 161-168.
[15] 史振学, 刘世忠, 赵金乾, 王效光, 李嘉荣. 基于不同原始组织预设变形第四代单晶高温合金的再结晶行为[J]. 材料工程, 2019, 47(5): 107-114.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn