材料工程  2006, Vol. 0 Issue (7): 39-42    
  论文 本期目录 | 过刊浏览 | 高级检索 |
热致液晶聚酰胺/尼龙66分子复合材料的结晶行为及其相容性研究
张卓, 张文熊
北京工业大学, 材料科学与工程学院, 北京, 100022
Crystallization and Miscibility of Polyamide TLCP/Nylon66 Molecular Composites
ZHANG Zhuo, ZHANG Wen-xiong
College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
全文: PDF(509 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 用共溶剂法制备了热致液晶聚酰胺/尼龙66分子复合材料。用DSC,WAXD和FTIR对复合材料的结晶行为和相容性进行了综合研究。DSC研究结果显示,不同组成共混物的熔点和结晶温度均发生明显下降,结晶速率和结晶度随液晶含量增加而下降,当液晶含量达到50%(质量分数)时,共混物出现超分子液晶态,体系具有明显的相容特征。WAXD结果显示,面间距随液晶聚酰胺含量增加而增加,说明液晶加入了尼龙66的结晶过程。FTIR结果显示,聚酰胺液晶与尼龙66分子间存在氢键作用,并且参与形成氢键作用官能团的比例随液晶含量的增加而增加。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
张卓
张文熊
关键词 热致液晶相容性尼龙66超分子氢键    
Abstract:TLCP/nylon-66 molecular composites were compounded by solution blend.Crystallization and miscibility were researched by DSC,WAXD and FTIR.DSC results showed that composites melting points and crystallization temperature were reduced due to additional TLCP,and crystallization rate and crystallization degree tended to decrease.Composites demonstrated supramolecular liquid-crystalline behavior in 50%(mass fraction)TLCP ratio.WAXD results showed that distance between crystalline surfaces increased while increasing TLCP concentrations,so it can be certain that TLCP had taken part in nylon-66 crystallization process.According to DSC and WAXD results,TLCP apparently restrain crystallization of nylon-66.FTIR approved that there was intermolecular hydrogen-bonding between molecules of TLCP and nylon66,and intensity of intermolecular hydrogen-bonding increased with increasing TLCP concentrations.
Key wordsTLCP    miscibility    nylon66    supramolecular    hydrogen-bonding
收稿日期: 2005-08-08      出版日期: 2006-07-20
中图分类号:  TB332  
基金资助:北京市自然科学基金资助项目(2002003)
作者简介: 张卓(1972- ),男,在读博士,主要从事含芳香结构聚合物的合成及聚合物多相复合材料体系结构与性能的研究,联系地址:北京工业大学材料科学与工程学院(100022).
引用本文:   
张卓, 张文熊. 热致液晶聚酰胺/尼龙66分子复合材料的结晶行为及其相容性研究[J]. 材料工程, 2006, 0(7): 39-42.
ZHANG Zhuo, ZHANG Wen-xiong. Crystallization and Miscibility of Polyamide TLCP/Nylon66 Molecular Composites. Journal of Materials Engineering, 2006, 0(7): 39-42.
链接本文:  
http://jme.biam.ac.cn/new/CN/      或      http://jme.biam.ac.cn/new/CN/Y2006/V0/I7/39
[1] TAKAYANAGI M.Polymer composite material[P].Brit UK Pat Appl 2008598,1977.
[2] HELMINIAK T E.Aromatic heterocyclic polymer alloys[P].US Pat Appl 902525,1978.
[3] FLORY P J.Statistical thermodynamics of mixtures of rodlike particles 5 mixtures with random coils[J].Macromolecules,1978,11:1138-1141.
[4] GIMESSLEY W W,EDWARDS S F.Entanglement interactions in polymers and the chain contour concentration[J].Polymer,1980,22:1329-1334.
[5] RADMARD B,DADMUN M D.The accessibility of functional groups to intermolecular hydrogen bonding in polymer blends containing a liquid crystalline polymer[J].Polymer,2001,42:1591-1600.
[6] ZHANG Wen-xiong,FUKUJI HIGASHI.Thermotropic copolyamides from polyethyleneglycol bis (4-carboxyphenyl)ethers with different oxyethylene units[J].J Polym Sci Part A:Polym Chem,1993,31:2935-2940.
[7] GOPAKUMAR T G,PONRATHNAM S,LELE A,et al.Insitu compatibilisation of poly(phenylene sulphide)/wholly aromatic thermotropic liquid crystalline polymer blends by reactive extrusion[J].Polymer,1999,40:357-364.
[8] TAKASHI KATO.Supramolecular liquid crystalline materials:molecular self-assembly and self-organization through intermolecular hydrogen bonding[J].Supramolecular Sci,1996,3:53-59.
[9] TJONG S C,ROBERT K Y L.Properties of in situ composites based on semiflexible thermotropic liquid crystalline copolyesteramide and polyamide 66 blends[J].Polym J,2000,32:907-914.
[10] VAN KREVELEN DW.Properties of polymer[M].3rd revised.Amsterdam:Elsevier Science Publishing Co,1990.
[11] YONG H,BO Z,YOSHIO I.Hydrogen bonds in polymer blends[J].Prog Polym Sci,2004,29:1021-1051.
[12] ERIC J M,STEPHEN E H,PAUL C P,et al.On the role of intermolecular hydrogen bonding in miscible polymer blends[J].Macromolecules,1984,17:1671-1678.
[13] CHRISTOPHE L M,DORAB E B,PAUL C P,et al.Hydrogen bonding in ternary polymer blend systems:determination of association parameters[J].Macromolecules,1992,25:7101-7106.
[1] 刘继涛, 钏定泽, 杨泽斌, 陈希亮, 颜廷亭, 陈庆华. 氨基酸/羟基磷灰石复合材料的制备与表征及其在酸蚀牛牙釉质体外再矿化中的应用[J]. 材料工程, 2020, 48(2): 100-107.
[2] 万天, 宋述鹏, 王今朝, 周和荣, 毛雨旭, 熊少聪, 李梦君. 生物医用镁合金腐蚀行为的研究进展[J]. 材料工程, 2020, 48(1): 19-26.
[3] 魏泽昌, 蔡晨阳, 王兴, 付宇. 生物可降解高分子增韧聚乳酸的研究进展[J]. 材料工程, 2019, 47(5): 34-42.
[4] 舒华金, 吴春萱, 杨康, 刘廷武, 李晨, 曹传亮. 快速膨胀海藻酸钠/二氧化硅纤维复合支架的制备及其快速止血功能的应用[J]. 材料工程, 2019, 47(12): 124-129.
[5] 杜军, 宋永明, 张志军, 房轶群, 王伟宏, 王清文. MAH/GMA共接枝聚乳酸对木粉/PLA复合材料性能的影响[J]. 材料工程, 2017, 45(12): 30-36.
[6] 桑伟, 周岚, 冯新星, 张建春. 电子束辐照诱导丙烯酸接枝尼龙66织物的改性研究[J]. 材料工程, 2017, 45(10): 111-116.
[7] 吴江渝, 何紫莹, 李秀辉. 改性高吸水树脂制备吸水膨胀橡胶及其性能[J]. 材料工程, 2014, 0(6): 40-44.
[8] 倪昕晔, 李爱军, 钟萍, 林涛, 熊信柏, 顾卫东. 不同高温处理工艺对C/C复合材料生物相容性的影响[J]. 材料工程, 2014, 0(6): 62-67.
[9] 范海波, 刘艳林, 杨荣杰, 李向梅. 芳炔树脂/POSS固化相容性及热稳定性研究[J]. 材料工程, 2014, 0(3): 1-6.
[10] 张彦飞, 兰艳花, 付一政, 赵贵哲, 胡国胜. PA6/POE共混物的分子动力学与介观动力学模拟[J]. 材料工程, 2013, 0(7): 44-49.
[11] 刘志明, 吴鹏, 谢成, 王海英, 孟围. 聚乙烯醇/纳米纤维素/聚乙烯醇的层层自组装及表征[J]. 材料工程, 2013, 0(1): 45-51.
[12] 江盛玲, 谷晓昱, 张志远. 聚苯硫醚/羟基改性多壁碳纳米管复合材料动态力学行为研究[J]. 材料工程, 2011, 0(6): 77-80.
[13] 安亭, 赵凤起, 高红旭, 马海霞, 郝海霞, 仪建华, 杨勇. 超级铝热剂的制备及其与双基系推进剂组分的相容性[J]. 材料工程, 2011, 0(11): 23-28,34.
[14] 花兴艳, 王源升, 赵培仲, 朱金华. 聚氨酯/环氧树脂互穿聚合物网络半硬泡沫的结构与性能[J]. 材料工程, 2009, 0(10): 32-35,40.
[15] 孙德明, 张勤河, 柴琦, 张明勤, 许崇海. Al2O3/Cr3C2/(W,Ti)C复合材料化学相容性分析[J]. 材料工程, 2007, 0(9): 55-57,61.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn