三醋酸纤维素的结构与性能研究

全文: PDF(1091 KB) HTML()
输出: BibTeX | EndNote (RIS)

摘要采用乙酸酐/乙酸/硫酸体系制备了三醋酸纤维素(CTA),运用IR,化学滴定,¹H-NMR,X射线衍射,DSC等手段对产物的结构及性质进行了表征和测试.结果表明,所合成的CTA结合醋酸质量分数均达到60%以上.与纤维素相比,CTA的晶型发生了明显变化,结晶度也降低到30%左右.同时,所制备的CTA的DSC谱图中都出现了明显而完整的熔融峰.

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王文俊
	李胤
	门爽
	邵自强

关键词 ：三醋酸纤维素, 乙酰基, 取代度分布

Abstract：Cellulose triacetate(CTA)was prepared in the presence of mixture of acetic anhydride/acetic acid/H₂SO₄.The structure and properties of cellulose triacetate acetylation were determined by IR,¹H-NMR,XRD,DSC and chemical analysis.The results showed that acetyl mass fraction of all CTA samples were at least 60%,the most active reaction position on the anhydroglulose unit was C-6.Compared with that of cellulose,the crystallinity of CTA was much lower,but the processability was improved a lot.

Key words： cellulose triacetate acetyl degree of substitution distribution

收稿日期: 2006-05-30 出版日期: 2007-08-20

中图分类号:

O631.1

作者简介: 王文俊(1967- ),女,副教授,从事天然高分子材料的改性研究,联系地址:北京理工大学材料学院(100081).

引用本文:

王文俊, 李胤, 门爽, 邵自强. 三醋酸纤维素的结构与性能研究[J]. 材料工程, 2007, 0(8): 49-52.
WANG Wen-jun, LI Yin, MEN Shuang, SHAO Zi-qiang. Structure and Properties of Cellulose Triacetate. Journal of Materials Engineering, 2007, 0(8): 49-52.

链接本文:

http://jme.biam.ac.cn/CN/ 或 http://jme.biam.ac.cn/CN/Y2007/V0/I8/49

[1] 高洁,汤烈贵.纤维素科学[M].北京:科学出版社,1996.
[2] 王桂花.液晶显示屏(LCD)用三醋酸纤维素(TAC)薄膜的发展现状与前景[J].影像技术,2005,(3):15-18.
[3] 梅洁,欧义芳,陈家楠.醋酸纤维素的高温合成及其性质的研究[J].纤维素科学与技术,2000,8(1):9-16.
[4] 胡继文,沈琳,王晓青,等.13C-NMR研究醋酸纤维素的取代基分布[J].纤维素科学与技术,2003,11(2):14-18.
[5] 梅洁,欧义芳,陈家楠.醋酸纤维索取代基分布与性质的关系[J].纤维素科学与技术,2002,10(1):12-18.

[1]	陈珂龙, 张桐, 崔溢, 王智勇. 超支化聚合物(HBPs)改性环氧树脂的研究进展[J]. 材料工程, 2019, 47(7): 11-18.
[2]	王梦梵, 陈旺, 苏世州, 韩旭, 徐樑华, 曹维宇. PAN纤维炭化过程中缺陷结构的温度效应[J]. 材料工程, 2015, 43(6): 66-70.
[3]	花兴艳, 王源升, 赵培仲, 朱金华. 聚氨酯/环氧树脂互穿聚合物网络半硬泡沫的结构与性能[J]. 材料工程, 2009, 0(10): 32-35,40.
[4]	梁兴泉, 李克文, 卢发燕, 郑安雄, 宋江选. PEG400存在下聚乙烯膜的光氧化降解特性研究[J]. 材料工程, 2008, 0(1): 14-17.