Ti(C,N)基金属陶瓷的烧结工艺研究
严永林1, 郑勇1, 刘文俊2, 承新1, 赵能伟1
1. 南京航空航天大学, 材料科学与技术学院, 南京, 210016;
2. 三峡大学, 机械与材料工程学院, 湖北, 宜昌, 443002
Study on Sintering Process of Ti(C,N)-based Cermets
YAN Yong-lin1, ZHENG Yong1, LIU Wen-jun2, CHENG Xin1, ZHAO Neng-wei1
1. College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;
2. College of Mechanical and Materials Engineering, China Three Gorges University, Yichang 443002, Hubei, China
全文: PDF(1316 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 采用真空烧结工艺制备了Ti(C,N)基金属陶瓷,研究了烧结温度和保温时间对Ti(C,N)基金属陶瓷显微组织和力学性能的影响,并用SEM观察其断口形貌.结果表明:随着烧结温度的升高,金属陶瓷的组织逐渐变得均匀,硬质颗粒逐渐球化,且其环形相逐渐变得完整;温度过高,保温时间过长,晶粒都会明显长大,环形相变厚,导致材料性能下降.经1440℃烧结,保温60min,可获得较佳的性能,其抗弯强度达1914.2MPa,硬度HRA达90.1.
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
严永林
郑勇
刘文俊
承新
赵能伟
关键词 Ti(C,N)基金属陶瓷烧结温度保温时间显微组织力学性能    
Abstract:Ti(C,N)-based cermets were produced by vacuum sintering.The effect of sintering temperature and holding time on the microstructure and mechanical properties of Ti(C,N)-based cermets was studied,and the fracture morphology was investigated by scanning electron microscope.The results show that,with the increasing of the sintering temperature,the microstructure of cermets became uniformity,and the ceramic grains got rounded,and the rim phase structure was completeness gradually.When the sintering temperature was too high or the holding time was too long,the rim phase was modified thicken,and the growing phenomenon of grains was abvious,the properties was decreased.The cermets sintered at 1440℃ for 60min showed the best mechanical properties.Their transverse rupture strength reached 1914.2MPa,and the hardness reached 90.1.
Key wordsTi(C,N)-based cermet    sintering temperature    holding time    microstructure    mechanical property
收稿日期: 2007-08-28      出版日期: 2008-01-20
中图分类号:  TF125.3  
基金资助:国家自然科学基金资助项目(50674057)
作者简介: 严永林(1980- ),男,硕士研究生,主要从事金属基复合材料及表面技术研究,联系地址:南京航空航天大学238#信箱(210016).E-mail:xinyu1062@163.com
引用本文:   
严永林, 郑勇, 刘文俊, 承新, 赵能伟. Ti(C,N)基金属陶瓷的烧结工艺研究[J]. 材料工程, 2008, 0(1): 49-53.
YAN Yong-lin, ZHENG Yong, LIU Wen-jun, CHENG Xin, ZHAO Neng-wei. Study on Sintering Process of Ti(C,N)-based Cermets. Journal of Materials Engineering, 2008, 0(1): 49-53.
链接本文:  
http://jme.biam.ac.cn/CN/      或      http://jme.biam.ac.cn/CN/Y2008/V0/I1/49
[1] CLARK E B,ROEBUCK B.Extending the application areas for titanium carbonitride cermets[J].International Journal of Re fractory Metals and Hard Materials,1992,11(1):23-33.
[2] VIATTE T,BOLOGNINI S,GUTARD T,et al.Investigation into the potential of a composite combining toughness and plastic deformation resistance[J].International Journal of Refractory Metals and Hard Materials,1999,17:79-89.
[3] ETTMAYER P,KOLASKA H,LENGAUER W,et al.Ti(C,N)cermets-metallurgy and properties[J].International Journal of Refractory Metals and Hard Materials,1995,13:343-351.
[4] BOLOGNINI S,FEUSIER G,MARI D,et al.High temperature mechanical behaviour of Ti(C,N)-Mo-Co cermets[J].International Journal of Refractory Metals and Hard Materials,1998,16:257-268.
[5] 丰平,郑勇,刘文俊,等.N含量对超细Ti(C,N)基金属陶瓷显微组织和力学性能的影响[J].稀有金属材料与工程,2005,34:479-481.
[6] RUSSIAS J,CARDINAL S,AGUNI Y,et al.Influence of titanium nitride addition on the microstructure and mechanical prop erties of TiC-based cermets[J].International Journal of Refractory Metals and Hard Materials,2005,23:358-362.
[7] BELLOSI A,MEDRI V,MONTEVERDE F.Processing and properties of Ti(C,N)WC based materials[J].Journal of the American Ceramic Society,2001,84(11):2669-2676.
[8] ZHENG Y,WANG S X,YOU M,et al.Fabrication of nanocomposite Ti(C,N)-based cermet by spark plasma sintering[J].Materials Chemistry and Physics,2005,92:64-70.
[9] NI X J,QI L H,WAN G W,et al.Study of Ti(C,N)-based cermets fabricated by pressureless-HIP sintering[J].Key Engineering Materials,2005,280-283:1417-1420.
[1] 赵云松, 张迈, 郭小童, 郭媛媛, 赵昊, 刘砚飞, 姜华, 张剑, 骆宇时. 航空发动机涡轮叶片超温服役损伤的研究进展[J]. 材料工程, 2020, 48(9): 24-33.
[2] 许凤光, 刘垚, 马文江, 张憬. 退火工艺对Zn/AZ31/Zn复合板材界面微观结构及力学性能的影响[J]. 材料工程, 2020, 48(8): 142-148.
[3] 郝思嘉, 李哲灵, 任志东, 田俊鹏, 时双强, 邢悦, 杨程. 拉曼光谱在石墨烯聚合物纳米复合材料中的应用[J]. 材料工程, 2020, 48(7): 45-60.
[4] 唐大秀, 刘金云, 王玉欣, 尚杰, 刘钢, 刘宜伟, 张辉, 陈清明, 刘翔, 李润伟. 柔性阻变存储器材料研究进展[J]. 材料工程, 2020, 48(7): 81-92.
[5] 张梦清, 于鹤龙, 王红美, 尹艳丽, 魏敏, 乔玉林, 张伟, 徐滨士. 感应熔覆原位合成TiB增强钛基复合涂层的微结构与力学性能[J]. 材料工程, 2020, 48(7): 111-118.
[6] 冯景鹏, 余欢, 徐志锋, 蔡长春, 王振军, 胡银生, 王雅娜. 2.5D浅交直联Cf/Al复合材料的显微组织及弯曲和剪切性能[J]. 材料工程, 2020, 48(6): 132-139.
[7] 李和奇, 王晓民, 曾宏燕. 热处理对FeCrMnNiCox合金微观组织及力学性能的影响[J]. 材料工程, 2020, 48(6): 170-175.
[8] 赵辉, 赵菲, 杨长龙, 韩钰, 靳东, 李红英. 时效处理对Al-Zr-Sc(-Er)合金组织和性能的影响[J]. 材料工程, 2020, 48(5): 112-119.
[9] 李淑文, 赵孔银, 陈康, 李金刚, 赵磊, 王晓磊, 魏俊富. TiO2共混丝朊接枝聚丙烯腈过滤膜制备及性能研究[J]. 材料工程, 2020, 48(3): 47-52.
[10] 赵新龙, 金鑫, 丁成成, 俞娟, 王晓东, 黄培. 热处理时间对聚甲基丙烯酰亚胺(PMI)泡沫结构和性能的影响[J]. 材料工程, 2020, 48(3): 53-58.
[11] 叶寒, 黄俊强, 张坚强, 李聪聪, 刘勇. 纳米WC增强选区激光熔化AlSi10Mg显微组织与力学性能[J]. 材料工程, 2020, 48(3): 75-83.
[12] 姚小飞, 田伟, 李楠, 王萍, 吕煜坤. 铜导线表面热浸镀PbSn合金镀层的组织与性能[J]. 材料工程, 2020, 48(3): 148-154.
[13] 刘也川, 张松, 谭俊哲, 关锰, 陶邵佳, 张春华. 机械滚压对A473M钢疲劳性能的影响[J]. 材料工程, 2020, 48(3): 163-169.
[14] 李昊卿, 田玉晶, 赵而团, 郭红, 方晓英. S32750双相不锈钢相界与晶界特征对其力学性能和耐蚀性能的影响[J]. 材料工程, 2020, 48(2): 133-139.
[15] 李国伟, 梁亚红, 陈芙蓉, 韩永全. 7075铝合金脉冲变极性等离子弧焊接头的双级时效行为[J]. 材料工程, 2020, 48(2): 140-147.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn