Preparation and properties of TiO2 blended silk fibroin grafted PAN filtration membrane
LI Shu-wen1,2, ZHAO Kong-yin1, CHEN Kang1, LI Jin-gang1, ZHAO Lei1, WANG Xiao-lei1, WEI Jun-fu1,2
1. State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China;
2. School of Chemical and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387, China
Abstract：Using organic solvent in traditional polymer filtration membrane is easy to cause environ-mental pollution.The silk was uniformly grafted with polyacrylonitrile using zinc chloride aqueous sol-ution as the solvent. The nano-TiO2 was blended into the mixture and the casting solution was pre-pared. The TiO2 blended silk fibroin grafted PAN (SF-g-PAN/TiO2) filtration membrane was pre-pared using water as the coagulation bath. The membrane was characterized by scanning electron micr-oscopy and infrared spectroscopy. The hydrophilic, anti-fouling and mechanical properties of SF-g-PAN membranes with different TiO2contents were studied. The rejection performance of dyes with different molecular weight by the SF-g-PAN/TiO2 membrane was investigated. The results show that the mechanical properties of the SF-g-PAN/TiO2 filtration membranes increase firstly and then dec-rease with the increase of TiO2 content. When the content of TiO2 is 1%(mass fraction), the mech-anical and hydrophilic properties of the SF-g-PAN/TiO2 membrane are the best; the rejection of the dyes whose molecular weight is more than 660 is greater than 96%, with the flux of 80 L/(m2·h) at 0.10 MPa.
[1] 刘雷艮,王育玲,陈建广.静电纺纳米/亚微米纤维膜对染料的过滤性能研究[J].膜科学与技术,2017,37(1):100-106. LIU L G,WANG Y L,CHEN J G. Filtration properties of electrospun nano-diameter/submicro-diameter fibrous membrance for dyes[J]. Membrane Science and Technology,2017,37(1):100-106.
[2] 王循,丁玉梅,余韶阳,等.熔体微分电纺PLA/OMMT可降解纳米纤维膜制备及污染处理[J].材料工程,2019,47(7):99-105. WANG X,DING Y M,YU S Y,et al. Preparation and pollution treatment of degradable PLA/OMMT nanofiber membrane by melt differential electrospinning[J]. Journal of Materials Engineering,2019,47(7):99-105.
[3] YE W Y,LIN J Y,BORREG R,et al.Advanced desalination of dye/NaCl mixtures by a loose nanofiltration membrane for digital ink-jet printing[J].Separation and Purification Technology,2018,197(3):27-35.
[4] ZHAO K,ZHANG X,WEI J,et al.Calcium alginate hydrogel filtration membrane with excellent anti-fouling property and controlled separation performance[J].Journal of Membrane Science,2015,492:536-546.
[5] 李亮,肖长发,黄庆林,等.PTFE/PAN共混中空纤维膜的制备与性能[J].材料工程,2013(1):12-15,20. LI L,XIAO C F,HUANG Q L,et al. Preparation and properties of PTFE/PAN blend hollow fiber membrane[J]. Journal of Materials Engineering,2013(1):12-15,20.
[6] MAJEED S,FIERRO D,BUHR K,et al.Multi-walled carbon nanotubes(MWCNTs) mixed polyacrylonitrile(PAN) ultrafiltration membranes[J].Journal of Membrane Science,2012,403/404(3):101-109.
[7] 高翔宇,贺高红,梁健.多壁碳纳米管(MWNT)/聚丙烯腈(PAN)共混复合膜的制备及性能研究[J].膜科学与技术,2013,33(3):17-22. GAO X Y,HE G H,LIANG J.Fabrication and characterization of raw multi-walled carbon nanotube(MWNT)/polyacrylonitrile(PAN) blending membrane[J].Membrane Science and Technology,2013,33(3):17-22.
[8] YOSHIKAWA M,FUJIMOTO K,KINUGAWA H,et al.Selective permeation of carbon dioxide through synthetic polymeric membranes having amine moiety[J].Chemistry Letters,1994,23:243-246.
[9] SUN Y Y,SHAO Z Z,HU P,et al.Hydrogen bonds in silk fibroin-poly (acrylonitrile-co-methyl acrylate) blends:FT-IR study[J].Journal of Polymer Science,1997,35(9):1405-1414.
[10] 李秋莲,赵仕余,张蓉.丙烯腈-丝朊蛋白接枝共聚反应的研究[J].四川大学学报(工程科学版),2000,32(3):116-118. LI Q L,ZHAO S Y,ZHANG R.Study on graft copolymerization of AN/fibroin[J].Journal of Sichuan University(Engineering Science Edition),2000,32(3):116-118.
[11] LI J G,LI S W,WANG X H,et al.Biologically inspired silk fibroin grafted polyacrylonitrile filtration membrane prepared in ZnCl2 aqueous solution[J].Chinese Chemical Letters,2019,30(1):239-242.
[12] WEI S X,ZHAO K Y,ZHANG X X,et al.Adsorption and photocatalytic degradation of dyes on polyacrylamide/calcium alginate/TiO2 composite film[J].Functional Materials Letters,2015,8(3):1-5.
[13] ZHAO K Y,FENG L Z,LIN H Q,et al.Adsorption and photocatalytic degradation of methyl orange imprinted composite membranes using TiO2/calcium alginate hydrogel as matrix[J].Catalysis Today,2014,236:127-134.
[14] ZHAO K Y,FENG L Z,LI Z H,et al.Preparation,characterization and photocatalytic degradation properties of TiO2/calcium alginate composite film and the recovery of TiO2 nanoparticle[J].RSC Advances,2014,93(4):51321-51329.
[15] 朱墨书棋,林春香,骆微,等.离子液体中纤维素/TiO2复合材料的制备及其性能[J].材料工程,2016,44(12):67-73. ZHU M S,LIN C X,LUO W,et al.Ionic liquid-assisted synthesis of cellulose/TiO2 composite and photocatalytic performance[J].Journal of Materials Engineering,2016,44(12):67-73.
[16] 刘建华,杨蓉,李松梅.TiO2/ACF光催化再生复合材料的研究进展[J].材料工程,2006(8):61-65. LIU J H,YANG R,LI S M.Progress in research of TiO2/ACF composite photocatalyst[J].Journal of Materials Engineering, 2006(8):61-65.
[17] 郝勇敢,邵先坤,唐海娣,等.石蜡/TiO2/活性炭复合相变材料的制备及其性能[J].材料工程,2016,44(11):51-55. HAO Y G,SHAO X K,TANG H D,et al.Preparation and properties of paraffin/TiO2/active-carbon composite phase change materials[J].Journal of Materials Engineering,2016,44(11):51-55.
[18] CAO X,MA J,SHI X,et al.Effect of TiO2 nanoparticle size on the performance of PVDF membrane[J].Applied Surface Science,2006,253(4):2003-2010.
[19] WEI Y,CHU H Q,DONG B Z,et al.Effect of TiO2,nanowire addition on PVDF ultrafiltration membrane performance[J].Desalination,2011,272(1):90-97.
[20] 张志箭,徐安厚,赵孔银,等.聚羟基丁酸酯纳米纤维支撑海藻酸钙纳滤膜制备及抗污染性能[J].高分子材料科学与工程,2017,33(7):179-183. ZHANG Z J,XU A H,ZHAO K Y,et al.Preparation and anti-fouling properties of polyhydroxybutyrate nanofiber supported calcium alginate nanofiltration membrane[J].Polymer Materials Science & Engineering,2017,33(7):179-183.
[21] SUN J Y,ZHAO X H,WIDUSHA R K,et al.Highly stretchable and tough hydrogels[J].Nature,2012,489(7414):133-136.
2020, Vol. 48 