铝合金表面硅烷处理后腐蚀性能的研究

PDF(137 KB)

材料工程 ›› 1999, Vol. 0 ›› Issue (8) : 18-20.

扫码查看或转发全文

研究与应用

铝合金表面硅烷处理后腐蚀性能的研究

陆峰¹, W.J.vanOoij²

作者信息 +

Corrosion Behavior of Al1100 Aluminum Alloy Surface after the Silane Treatment

LU Feng¹, W.J.van Ooij²

Author information +

文章历史 +

摘要

硅烷预处理对环境无污染,有望代替现有的铬酸盐处理,六价铬由于有毒,其使用及排放已受到严格的控制.使用腐蚀测量技术(直流极化、盐雾试验、浸泡试验等)研究BTSE硅烷处理溶液的防护性能,研究结果表明:BTSE硅烷预处理对Al1100铝合金抗腐蚀性能有明显改善.

Abstract

Silane pretreatments were investigated as environmentally friendly replacements for the existing chromating processes.The use and disposal of chromium and chromium compounds have received much attention because of the toxicity of chromium. In order to compare the corrosion protection properties of BTSE silanes solution, using corrosion measurement techniques(DC polarization, SST and Immersion test etc.), BTSE silane pretreatment displayed better corrosion protection for Al1100 aluminum alloy.

导出引用

陆峰, W.J.vanOoij. 铝合金表面硅烷处理后腐蚀性能的研究[J]. 材料工程, 1999, 0(8): 18-20

LU Feng, W.J.van Ooij. Corrosion Behavior of Al1100 Aluminum Alloy Surface after the Silane Treatment[J]. Journal of Materials Engineering, 1999, 0(8): 18-20

中图分类号： TG178

参考文献

[1] W.J.van Ooij. Proposal of Corrosion Protection of Al
Cathodes in Zinc Electrolysis, Dec. 1996.
[2] Nie Tang. Modification of Polymer-Metal Interface for
Corrosion Improvement, Ph.D Thesis, University of
Cincinnati, 1996.
[3] B.C. Zhang. Adsorption of Silane Films on Iron Surface, Ph.D. Thesis, University of Cincinnati, 1997.
[4] V. Subramanian and W.J. van Ooij. Corrosion, 1998,54(3):204.
[5] F.J. Boerio and C.H.Ho. J. Adhesion, 1987, 21(1):25.
[6] W.J. van Ooij and A. Sabata. U.S.Patent 5,108,793, 1992.
[7] W.J. van Ooij, R.A. Edwards and A. Sabata.
U.S.Patent 5,292,549, 1994.
[8] W.J. van Ooij and A. Sabata. U.S.Patent 5,322,713, 1994.
[9] D.A. Jones. Principles and Prevention of Corrosion,
Macmillan Publishing, New York, 1992, 127.