7075铝合金瞬时腐蚀速率的计算和试验验证

PDF(228 KB)

材料工程 ›› 2004, Vol. 0 ›› Issue (12) : 43-46.

扫码查看或转发全文

研究与应用

7075铝合金瞬时腐蚀速率的计算和试验验证

陈素晶¹, 袁庆铭², 何建平¹, 周建华¹

作者信息 +

Experimental Evaluation of Computing Method of Instantaneous Corrosion Rate for 7075 Aluminum Alloy

CHEN Su-jing¹, YUAN Qing-ming², HE Jian-ping¹, ZHOU Jian-hua¹

Author information +

文章历史 +

摘要

针对铝合金腐蚀平均速率与瞬时速率的差异,根据腐蚀过程中试样横截面的变化与欧姆电阻的对应关系,建立了新的腐蚀速率计算方法.将试样全浸和半浸在腐蚀溶液中,分别测定了7075铝合金电阻随时间的变化,并由腐蚀速率计算公式获得了对应的腐蚀速率与时间的关系.结果表明,全浸6h前铝合金腐蚀速率随时间线性减小,接下来经历一个平坦区,25h后腐蚀速率又稍微增加.推断全浸6h之前铝合金表面主要发生点蚀,接下来是晶间腐蚀,25h之后进入剥蚀的发展期.铝合金半浸于电解液中的腐蚀速率随时间的变化趋势与全浸于溶液中相似.

Abstract

Based on the relationship between cross section variety and resistance of sample, a new formula was put forward to calculate the instantaneous corrosion rate of aluminum alloy.Ohm resistance of 7075 aluminum alloy was measured while alloy was immersed entirely or half in corrosion electrolyte, then corrosion rate of the alloy was calculated with the new formula. The results showed that corrosion rate of 7075 aluminum alloy in electrolyte linearly decreased before 6h,got to a flat region,and little increased after 25h. These three periods corresponded to pitting, intergranular corrosion and exfoliation of sample. Corrosion rate of aluminum alloy half-immersed in electrolyte with time was similar with that of sample immersed entirely in electrolyte.

导出引用

陈素晶, 袁庆铭, 何建平, 周建华. 7075铝合金瞬时腐蚀速率的计算和试验验证[J]. 材料工程, 2004, 0(12): 43-46

CHEN Su-jing, YUAN Qing-ming, HE Jian-ping, ZHOU Jian-hua. Experimental Evaluation of Computing Method of Instantaneous Corrosion Rate for 7075 Aluminum Alloy[J]. Journal of Materials Engineering, 2004, 0(12): 43-46

中图分类号： TG174.3

参考文献

[1] KETCHAM S J. Localized corrosion-cause of metal failure [A].Exfoliation Corrosion of Aluminum Alloys [M]. ASTM STP 516, 1972.3-16.
[2] HAIDEMENOPOULOS G N. Hydrogen absorption into 2024-T3aluminum alloy during exfoliation and alternate immersion testing [J]. Corrosion, 1998, 54(1):73-78.
[3] CONDE A. Electrochemical modeling of exfoliation corrosion behavior of 8089 alloys [J]. Electrochimica Acta, 1997, 43(8):849-860.
[4] BELLENGER F. Use of acoustic emission technique for the early detection of aluminum alloys exfoliation corrosion [J]. NDT &E International, 2002, 35:385-392.
[5] HABASHI M. Quantitative measurements of the degree of exfoliation on aluminum alloys. Corrosion Science, 1993, 35(1-4):169-183.
[6] ANDRIEU C. Aluminum alloy corrosion detection by magnetic measurement [J]. Journal of Material Science, 1998, 33:3177-3181.
[7] 郭宝兰.LC4铝合金板材在EXCO溶液中的腐蚀行为[J].材料保护,1995,28(6):5-7.
[8] 李荻.硬铝合金剥蚀速率测试方法的研究[J].航空学报,1999,16(3):304-308.
[9] 朱立群.模拟实际飞机腐蚀介质中高强铝合金材料腐蚀行为研究[J].航空学报,1991,17(1):31-36.
[10] 何建平,高亚东,樊蔚勋.评估航空铝合金剥蚀性能新方法的研究[J].腐蚀科学与防护技术,2003,15(1):18-21.
[11] 化学工业部化工机械研究院.腐蚀与防护手册腐蚀理论、实验及监测[M].北京:化学工业出版社,1995.
[12] 谢伟杰.LY12CZ和7075-T7351铝合金在EXCO溶液中腐蚀动力学的统计研究[J].航空学报,1999,20(1):34-38.
[13] 李劲风,张昭,曹发和,等.LC4铝合金剥蚀及其电化学阻抗行为[J].中国有色金属学报,2002,12(6):1189-1193.