利用TiB2陶瓷材料的高硬度、高耐磨耐热等一系列优异性能,采用低碳钢带制成粉芯线材,用电弧喷涂工艺在Q235基体上制备耐磨涂层。通过添加Cr元素来优化喷涂工艺,改善涂层性能,并对添加Cr元素后涂层的耐磨粒磨损性能等进行了测试,通过多种手段分析Cr元素的加入对涂层耐磨性能的影响以及涂层磨损机理。结果表明,粉芯中添加Cr元素后,涂层韧性得到很大改善,涂层中组织分布也更加均匀弥散,磨粒磨损性能因此得到较大提高。
Abstract
The wear resistant coatings on Q235 substrate were prepared from a cored wire by arc spraying. The cored wire contained TiB2 ceramic enveloped by a low carbon steel. The different contents of Cr element were added to the cored wire to improve performance of the coating. The properties of the coating were measured, wear mechanism was analyzed, and their microstructures were observed. The results showed that the abrasive wear resistance of the coating was significantly improved by adding Cr, and the optimum content of Cr was 11%～15%. The phase distribution of the coatings was uniform and dispersive after adding Cr.
关键词
TiB2陶瓷涂层 /
电弧喷涂 /
粉芯线材 /
磨粒磨损
{{custom_keyword}} /
Key words
TiB2coating /
arc spraying /
cored wires /
abrasive wear
{{custom_keyword}} /
中图分类号：
TG174.442
{{custom_clc.code}}
({{custom_clc.text}})
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 李建明.磨损金属学[M].北京:冶金工业出版社,1990.115-120.
[2] 林福严,曲敬信,陈华辉. 磨损理论与抗磨技术[M].北京:科学出版社,1993.23-29.
[3] 徐滨士,刘世参. 表面工程[M]. 北京:机械工业出版社,2000.
[4] 蔡挺.热喷涂技术的现状和应用[J].广东有色金属学报,1999,9(1):59-63.
[5] 徐滨士.电弧喷涂技术的应用和发展[J].铁道物资科学管理,1997,15(3):34-35.
[6] 高荣发.热喷涂[M].北京:化学工业出版社,1992.49-57.
[7] PIERSON H O, RANDICH E.The chemical vapor deposition of TiB2from diborane[A]. MATTOX D M.Chemical Vapor Depo sition[C]. New York:Academic Press ,1977.304-317.
[8] 鲍昌华,赵建生.TiB2陶瓷防护膜的研究现状和进展[J].材料导报,2001,(3):19-21.
[9] DALLAIRE S, CHAMPAGNE B. Plasma spray synthesis of TiB2-Fe coatings[J].Thin Solid Films, 1984,118(4):477-483.
[10] FUKUBAVASHI,HAROLD. Coated article with improved th-ermal emissivity[P].USA Patent:4975621,1990-12-04.
[11] ANANTHAPADMANABHAN P V, SREEKUMAR K P.El-ectrical resistivity of plasma-sprayed titanium diboride coatings[J].Journal of Materials Science,1990,28(6):1655-1658.
[12] SUE,TUCKER,STAVROS,et al. Method for producing a TiB.sub.2-based coating[P].USA Patent:5837327, 1998-11-17.
[13] 向新,秦岩.TiB2及其复合材料的研究进展[J].陶瓷学报,1999,(6):113-117.
[14] 籍国宝.摩擦磨损原理[M].北京:农业出版社,1992.45-50.
[15] 邵荷生,曲敬信,许小棣.摩擦与磨损[M].北京:煤炭工业出版社,1992.203-255.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}
PDF(307 KB)