铝含量对Ni3Al基合金IC6E微观组织和力学性能的影响

PDF(1857 KB)

材料工程 ›› 2006, Vol. 0 ›› Issue (4) : 52-55.

扫码查看或转发全文

测试与表征

铝含量对Ni₃Al基合金IC6E微观组织和力学性能的影响

乔敏¹, 李树索¹, 马文有¹, 宋尽霞², 韩雅芳²

作者信息 +

Effect of Content of Al on Microstructure and Mechanical Properties of Ni₃Al Base Alloy IC6E

QIAO Min¹, LI Shu-suo¹, MA Wen-you¹, SONG Jin-xia², HAN Ya-fang²

Author information +

文章历史 +

摘要

为了确定Ni₃Al基合金IC6E中最佳的铝含量,在成分为Ni-14.0Mo-7.2Al-0.025B(质量分数/%,下同)的母合金中,分别加入了四种不同含量的铝(0%,0.4%,0.6%,0.8%),测定了这些合金的室温拉伸和1050℃/90MPa高温持久性能,并采用扫描电镜分析了这些合金的微观组织.综合考虑这些合金的微观组织以及力学性能,确定了在IC6E合金中最佳的铝含量为7.8%.

Abstract

In order to determine the optimum content of Al,alloys with the different amounts of Al(0%,0.4%,0.6%,0.8%)based on the master alloy composition of Ni-14.0Mo-7.2Al-0.025B(mass fraction/%) were prepared.The tensile strength at room temperature and stress rupture life at 1050℃/90MPa have been determined. The microstructures of the alloys have been studied by scanning electron microscopy.On the basis of the compromise of the microstructures and mechanical properties,the optimum content of Al was determined to be 7.8%.

导出引用

乔敏, 李树索, 马文有, 宋尽霞, 韩雅芳. 铝含量对Ni₃Al基合金IC6E微观组织和力学性能的影响[J]. 材料工程, 2006, 0(4): 52-55

QIAO Min, LI Shu-suo, MA Wen-you, SONG Jin-xia, HAN Ya-fang. Effect of Content of Al on Microstructure and Mechanical Properties of Ni₃Al Base Alloy IC6E[J]. Journal of Materials Engineering, 2006, 0(4): 52-55

中图分类号： TG146

参考文献

[1] 肖程波,韩雅芳,殷克勤,等.定向凝固Ni₃Al基合金IC6的高温蠕变行为[J].材料工程,1996,(3):6-8.
[2] 肖程波,韩雅芳,张行安.定向凝固Ni₃Al基高温结构材料IC6A合金的研究[J].材料工程,2001,(6):3-6.
[3] 刘庆泉.Ni₃Al基IC6高温合金工程应用研究[J].航空材料学报,2003,23(增刊):209-214.
[4] 赵希宏,韩雅芳,谭永宁,等.定向凝固Ni₃Al基合金IC6[J].材料工程,1997,(9):13-15.
[5] 韩雅芳,李孙华.定向凝固铸造Ni₃Al基合金IC6[J].燃气涡轮试验与研究,1994,(1):48-51.
[6] 宋尽霞,肖程波,李树索,等.950℃长期时效对Ni₃Al基合金IC6的组织及力学性能的影响[J].金属学报,2002,38(3):250-254.