材料工程  2014, Vol. 0 Issue (5): 86-90    DOI: 10.11868/j.issn.1001-4381.2014.05.015
  测试与表征 本期目录 | 过刊浏览 | 高级检索 |
基于RVM表征热障涂层孔隙率与孔隙形貌对超声纵波声速的影响
马志远1, 罗忠兵1, 林莉1,2
1. 大连理工大学 无损检测研究所, 辽宁 大连 116085;
2. 船舶制造国家工程研究中心, 辽宁 大连 116085
Characterization of Ultrasonic Longitudinal Velocity Evolution in TBCs with Different Porosity and Void Morphology Based on Random Void Model
MA Zhi-yuan1, LUO Zhong-bing1, LIN Li1,2
1. NDT & E Laboratory, Dalian University of Technology, Dalian 116085, Liaoning, China;
2. National Engineering Research Center of Shipbuilding, Dalian 116085, Liaoning, China
全文: PDF(1988 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 依据由电子束物理气相沉积法(Electron Beam Physical Vapor Deposition,EB -PVD)制备的ZrO2-7%(质量分数)Y2O3(Yttria Stabilization Zirconia,YSZ)涂层显微分析结果,采用统计学方法和随机介质理论建立了涂层的随机孔隙模型。针对孔隙率分别为0%,5%,10%且具有不同孔隙形貌的涂层模拟结果,采用数值计算方法得到不同孔隙率及孔隙形貌差异引起的纵波声速变化。结果表明:含孔隙涂层纵波声速明显减小,与致密涂层相比,孔隙率为5%和10%的YSZ涂层,纵波声速分别减小14.4%和23.9%。此外,孔隙率恒定时,孔隙形貌变化也会引起超声纵波速度波动,对于孔隙率5%和10%的涂层,声速波动分别为5.0%和6.8%,该模拟计算结果与对应孔隙率的实验测量结果5.9%和7.5%是相当的。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
马志远
罗忠兵
林莉
关键词 热障涂层孔隙率孔隙形貌纵波声速随机孔隙模型    
Abstract:To describe the non-uniform microstructure of ZrO2-7% (mass fraction) Y2O3 deposited by EB-PVD, a novel YSZ random void model (RVM) was proposed based on the random media theory and statistical analysis method. The ultrasonic testing of YSZ coatings, whose porosities were 0%, 5% and 10%, respectively, were simulated with finite difference time domain (FDTD) method. The variation of the longitudinal wave velocity caused by the porosity and void morphology was analyzed. Results show that the velocity decreases with the increase of porosities in YSZ coatings. In the case of 5% and 10% porosity, the decreased values are 14.4% and 23.9%, respectively, compared with that of the dense coating. Furthermore, the corresponding velocity fluctuations caused by the difference of void morphology are 5% and 6.8%, respectively, which match with 5.9% and 7.5% of experimental results.
Key wordsTBCs    porosity    void morphology    ultrasonic longitudinal velocity    RVM
收稿日期: 2013-02-04      出版日期: 2014-05-20
中图分类号:  TB52  
通讯作者: 林莉(1970- ),女,博士,教授,博士生导师,从事材料无损检测与评价研究,联系地址:辽宁省大连市甘井子区凌工路2号大连理工大学材料科学与工程学院230室(116085),E-mail:linli@dlut.edu.cn     E-mail: linli@dlut.edu.cn
作者简介: 马志远(1986- ),男,博士研究生,从事材料无损检测与评价研究,联系地址:辽宁省大连市甘井子区凌工路2号大连理工大学材料科学与工程学院234室(116085),E-mail:dahai2296@sina.com
引用本文:   
马志远, 罗忠兵, 林莉. 基于RVM表征热障涂层孔隙率与孔隙形貌对超声纵波声速的影响[J]. 材料工程, 2014, 0(5): 86-90.
MA Zhi-yuan, LUO Zhong-bing, LIN Li. Characterization of Ultrasonic Longitudinal Velocity Evolution in TBCs with Different Porosity and Void Morphology Based on Random Void Model. Journal of Materials Engineering, 2014, 0(5): 86-90.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2014.05.015      或      http://jme.biam.ac.cn/CN/Y2014/V0/I5/86
[1] 张红松, 王富耻, 马壮. 等离子涂层孔隙研究进展[J]. 材料导报, 2006, 20(7): 16-26. ZHANG H S, WANG F C, MA Z. Research development of pores in plasma sprayed coatings[J]. Materials Review, 2006, 20(7): 16-26.
[2] 杨晓光, 耿瑞, 熊昌炳. 航空发动机热端部件隔热陶瓷涂层应用研究[J]. 航空动力学报, 1997, 12(2): 183-188. YANG X G, GENG R, XIONG C B. A survey on application of TBC for aeroengine hot sections[J]. Journal of Aerospace Power, 1997, 12(2): 183-188.
[3] LESCRIBAA D, VINCENT A. Ultrasonic characterization of plasma sprayed coatings[J]. Surface and Coatings Technology, 1996, 81(3): 297-306.
[4] ROGE B, FAHR A, GIGUERE J S R, et al. Nondestructive measurement of porosity in thermal barrier coatings[J]. Journal of Thermal Spray Technology, 2003, 12(4): 530-535.
[5] LEIGH S H, BERNDT C C. Modeling of elastic constants of plasma spray deposits with ellipsoid-shaped voids[J]. Acta Materialia, 1999, 47(5): 1575-1586.
[6] ALLEN A, ILAVSKY J, LONG G G, et al. Microstructural characterization of yttria-stabilized zirconia plasma-sprayed deposits using multiple small-angle neutron scattering[J]. Acta Materialia, 2001, 49(9): 1661-1675.
[7] SEVOSTIANOV I, KACHANOV M. Is the concept of "average shape" legitimate for a mixture of inclusions of diverse shapes?[J]. International Journal of Solids and Structures, 2012, 49(23-24): 3242-3254.
[8] ZHAO Y, LIN L, LI X M, et al. Simultaneous determination of the coating thickness and its longitudinal velocity by ultrasonic nondestructive method[J]. NDT & E International, 2010, 43(7): 579-585.
[9] LI J C, LIN L, LI X M, et al. Ultrasonic characterization of modified Cr2O3 coatings by reflection coefficient spectroscopy[J]. Trans Nonferrous Met Soc China, 2010, 20(3): 418-424.
[10] ZHAO Y, LIN L, LI X M, et al. Measurements of coating density using ultrasonic reflection coefficient phase spectrum[J]. Ultrasonics, 2011, 51(5): 596-601.
[11] ZHAO Y, MA Z Y, LIN L,et al. Correlating ultrasonic velocity and porosity using FDTD method based on random pores model[J]. Materials Science Forum, 2011, 675-677: 1221-1224.
[12] 赵扬, 林莉, 马志远, 等. 基于随机介质理论的热障涂层随机孔隙模型构建[J]. 中国表面工程, 2010, 23(2): 78-81. ZHAO Y, LIN L, MA Z Y, et al. Establishing TBC random pore model based on random media theory[J]. China Surface Engineering, 2010, 23(2): 78-81.
[13] 牟云飞. 基于随机孔隙模型的CFRP孔隙率超声检测研究[D]. 大连: 大连理工大学, 2009.
[14] CHOI S R, ZHU D M, MILLER R A. Mechanical properties/database of plasma-sprayed ZrO2-8wt%Y2O3 thermal barrier coatings[J]. Applied Ceramic Technology, 2004, 1(4): 330-342.
[1] 曾威, 毛杰, 马景涛, 邓畅光, 邓子谦, 邓春明, 宋鹏. 表面粗糙度对PS-PVD热障涂层陶瓷层沉积的影响[J]. 材料工程, 2019, 47(8): 161-168.
[2] 李可峰, 尹晓燕. 聚苯醚纳米纤维锂电隔膜的制备[J]. 材料工程, 2018, 46(10): 120-126.
[3] 杜际雨, 李方义, 鹿海洋, 商建通, 李振. 大气等离子喷涂NiCrBSi-Mo/Ni涂层中黏结层对NiCrBSi-Mo复合工作层性能的影响[J]. 材料工程, 2017, 45(9): 86-92.
[4] 袁佟, 邓畅光, 毛杰, 邓春明, 邓子谦. 等离子喷涂-物理气相沉积制备7YSZ热障涂层及其热导率研究[J]. 材料工程, 2017, 45(7): 1-6.
[5] 王逸群, 宋鹏, 季强, 廖红星, 陆建生. H2O和Y(O)对NiCoCrAl热障涂层高温氧化的影响[J]. 材料工程, 2017, 45(4): 65-69.
[6] 陈文龙, 刘敏, 张吉阜, 宋进兵. 燃气热循环下7YSZ热障涂层的微结构演变与阻抗谱特征[J]. 材料工程, 2017, 45(10): 79-87.
[7] 赵立英, 刘平安. 氧燃比对爆炸喷涂碳化钨涂层结构和性能的影响[J]. 材料工程, 2016, 44(6): 50-55.
[8] 张海军, 周储伟. 基于显微CT图像的细编穿刺碳/碳复合材料细观力学模型[J]. 材料工程, 2016, 44(5): 65-71.
[9] 张伟, 马志远, 赫丽华, 高剑英, 罗文, 林莉, 雷明凯. 基于声压反射系数幅度谱匹配分析的薄层厚度和超声纵波声速双参数反演[J]. 材料工程, 2016, 44(10): 74-79.
[10] 徐立新, 管厚兵, 杨智伟, 郝向忠. 真空吸浆法制备C/SiC复合材料及力学性能研究[J]. 材料工程, 2015, 43(12): 10-16.
[11] 黄亮亮, 孟惠民, 唐静. 纳米结构热障涂层研究进展[J]. 材料工程, 2014, 0(8): 105-114.
[12] 齐红宇, 马立强, 李少林, 杨晓光, 王亚梅, 魏洪亮. 等离子热障涂层构件高温热疲劳寿命预测研究[J]. 材料工程, 2014, 0(7): 67-72.
[13] 董建民, 李嘉荣, 牟仁德, 赵金乾, 史振学, 刘世忠. 高温热处理对带热障涂层DD6单晶高温合金互扩散行为及持久断裂特征的影响[J]. 材料工程, 2014, 0(6): 51-55.
[14] 何箐, 屈轶, 汪瑞军, 王伟平. DZ40M合金表面纳米和垂直裂纹结构热障涂层的抗燃气热腐蚀性能[J]. 材料工程, 2014, 0(5): 66-72.
[15] 何箐, 吴鹏, 屈轶, 汪瑞军, 王伟平. 一种新型CMAS耦合条件下热障涂层热循环实验方法[J]. 材料工程, 2014, 0(12): 92-98.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn