材料工程  2014, Vol. 0 Issue (7): 55-59    DOI: 10.11868/j.issn.1001-4381.2014.07.011
  测试与表征 本期目录 | 过刊浏览 | 高级检索 |
喷射成形GH738合金的疲劳裂纹扩展行为
杨冬野1,2,3, 曹福洋1,2, 许文勇3, 左欣1,2, 李周3, 张国庆3, 孙剑飞1,2
1. 哈尔滨工业大学 材料科学与工程学院, 哈尔滨 150001;
2. 哈尔滨工业大学 金属精密热加工国防科技重点实验室, 哈尔滨 150001;
3. 北京航空材料研究院 先进高温结构材料重点实验室, 北京 100095
Fatigue Crack Growth Behavior of Spray Formed GH738 Alloy
YANG Dong-ye1,2,3, CAO Fu-yang1,2, XU Wen-yong3, ZUO Xin1,2, LI Zhou3, ZHANG Guo-qing3, SUN Jian-fei1,2
1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001, China;
3. Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China
全文: PDF(1592 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 进行了不同温度、频率和应力比条件下喷射成形GH738合金紧凑拉伸(CT)试样的疲劳裂纹扩展试验,分析了相应条件下的疲劳裂纹扩展速率及其对疲劳裂纹扩展行为的影响规律。结果表明:随着温度的升高,裂纹扩展速率略有加快;加载频率降低,疲劳裂纹扩展加速;裂纹扩展速率da/dN随应力比R的增大而增大。疲劳断口呈现多裂纹源特征,裂纹稳定扩展为疲劳条带机制。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
杨冬野
曹福洋
许文勇
左欣
李周
张国庆
孙剑飞
关键词 喷射成形GH738疲劳裂纹扩展    
Abstract:The fatigue crack growth tests of spray formed GH738 superalloy with compact tension (CT) specimens were carried out at different temperatures, loading frequency and R-ratios. The effects of temperatures, loading frequency and R-ratios on fatigue crack growth behaviors were investigated .The results show that the crack propagation rate increases with the increase of temperature; Fatigue crack propagation increases with the decrease of loading frequency; Fatigue crack growth rate da/dN is also found to increase with the larger R-ratios. The crack initiates multi-sites, and the fatigue fracture individually exhibits a series of fatigue striations mode in the crack steady growth region.
Key wordsspray formed    GH738    fatigue crack growth
收稿日期: 2012-12-12     
1:  TG146.1  
基金资助:国家自然科学基金资助项目(51074145);国家 973 计划资助项目 (2010CB631205)
通讯作者: 孙剑飞(1962-)男,教授,主要从事喷射成形、镁铝合金、非晶等方面的研究工作,联系地址:哈尔滨工业大学材料与工程学院金属精密热加工国家级重点实验室612房间(150001),E-mail:jfsun@hit.edu.cn     E-mail: jfsun@hit.edu.cn
引用本文:   
杨冬野, 曹福洋, 许文勇, 左欣, 李周, 张国庆, 孙剑飞. 喷射成形GH738合金的疲劳裂纹扩展行为[J]. 材料工程, 2014, 0(7): 55-59.
YANG Dong-ye, CAO Fu-yang, XU Wen-yong, ZUO Xin, LI Zhou, ZHANG Guo-qing, SUN Jian-fei. Fatigue Crack Growth Behavior of Spray Formed GH738 Alloy. Journal of Materials Engineering, 2014, 0(7): 55-59.
链接本文:  
http://jme.biam.ac.cn/jme/CN/10.11868/j.issn.1001-4381.2014.07.011      或      http://jme.biam.ac.cn/jme/CN/Y2014/V0/I7/55
[1] SHEN G, SEMIATIN S L, SHIVPURI R. Modeling microstructural development during the forging of Waspaloy[J].Metallurgical and Materials Transactions: A, 1995,26:1795-1803.
[2] LIU N, LI Z, ZHANG G Q. Hot deformation behavior and microstructure evolution of spray formed GH738 superalloy[J].Rare Metals, 2011,30:388-391.
[3] YUAN H, LI Z, ZHANG G Q, et al. The study of microstructures and properties of spray formed superalloy GH738 ring[J].Journal of Iron and Steel Research, 2011,23:271-273.
[4] 孙剑飞,沈军.喷射成形镍基高温合金的研究进展[J].材料导报, 1999,13(2):10-12.SUN J F,SHEN J. Development of spray formed nickel base superalloys[J]. Materials Review, 1999,13(2):10-12.
[5] DAVIDSON D L, TRYON R G, OJA M, et al. Fatigue crack initiation in Waspaloy at 20℃[J].Metallurgical and Materials Transactions: A, 2007,38:2214-2225.
[6] LIU X B, MA L Z, CHANG K M, et al. Fatigue crack propagation of Ni-base superalloys[J]. Acta Metallurgica Sinica :A, 2005,18:55-64.
[7] XU W Y, ZHANG G Q, LI Z. Low cycle fatigue behavior of spray formed superalloy rings[J]. Advanced Materials Research, 2012,399:1937-1941.
[8] YANG D Y, XU W Y, LI Z, et al. Quantitative analysis on fatigue fracture of spray formed GH738 alloy[J]. Materials Science Forum, 2013,747-748:564-568.
[9] 钟群鹏,赵子华. 断口学[M].北京: 高等教育出版社,2006.268-270.
[10] 赵国荣,罗希延,任璐璐,等.航空发动机涡轮盘用GH4133B合金疲劳裂纹扩展行为研究[J].机械工程学报, 2011,47(18):55-65. ZHAO G R, LUO X Y, REN L L,et al. Research on fatigue crack propagation behavior of GH4133B superalloy used in turbine disk of aero-engine[J]. Journal of Mechanical Engineering, 2011,47(18):55-65.
[11] 刘维维,唐定中,李嘉荣,等.抽拉速率对DD6单晶高温合金650℃低周疲劳性能的影响[J]. 航空材料学报,2012,32(2):8-12. LIU W W,TANG D Z, LI J R, et al. Effects of withdrawing rate on low cycle fatigue properties of single crystal superalloy DD6 at 650℃[J]. Journal of Aeronautical Materials, 2012,32(2):8-12.
[12] LIAW P K, SAXENA A, SWAMINATHAN V P, et al. Effects of load ratio and temperature on the near-threshold fatigue crack propagation behavior in a CrMoV steel[J]. Metallurgical and Materials Transactions: A, 1983,14(8):1631-1640.
[13] 高文柱,吴欢,赵永庆.金属材料疲劳裂纹扩展研究综述[J].钛工业进展,2007, 24(6):33-37. GAO W Z,WU H,ZHAO Y Q.Summary of fatigue crack growth of study on metallic materials[J]. Titanium Industry Progress, 2007, 24(6):33-37.
[14] GHONEM H, FOERCH R. Frequency effects on fatigue crack growth behavior in a near-α titanium alloy[J]. Materials Science and Engineering: A, 1991,138(1):69-81.
[15] 沙桂英,韩玉,刘腾,等.应力幅对退火态Mg-3Al-2Sc合金疲劳行为的影响[J].材料工程,2012,(12):24-28. SHA G Y,HAN Y,LIU T, et al. Influences of stress amplitude on fatigue behavior of as-annealed Mg-3Al-2Sc alloy[J]. Journal of Materials Engineering,2012,(12):24-28.
[16] 刘新灵,张峥,陶春虎.疲劳断口定量分析[M].北京: 国防工业出版社,2010.78-80.
[1] 许天旱, 王荣, 冯耀荣, 雒设计, 王党会, 杨宝. 应力比对K55套管钻井钢疲劳裂纹扩展性能的影响[J]. 材料工程, 2015, 43(6): 79-84.
[2] 张勇, 李周, 袁华, 许文勇, 张国庆, 付书红, 王涛. 双扫描喷射成形高速钢SFT15性能研究[J]. 材料工程, 2013, 0(4): 45-49.
[3] 严益民, 胡正飞, 林富生, 赵双群. 汽轮机转子30Cr1Mo1V钢长期服役状态下的高温疲劳行为[J]. 材料工程, 2012, 0(11): 38-41,96.
[4] 宫玉辉, 刘铭, 张坤, 黄敏, 伊琳娜, 戴圣龙. 不同腐蚀环境对7475-T7351铝合金疲劳性能及裂纹扩展速率的影响[J]. 材料工程, 2010, 0(9): 71-73.
[5] 刘敬福, 李荣德, 谢懿, 吴德枫. 喷射成形高锰ZA35合金的工艺及组织研究[J]. 材料工程, 2010, 0(6): 63-67.
[6] 袁华, 李周, 张国庆, 许文勇, 姚瑞平, 田世藩. 热处理对喷射成形GH742y合金组织与性能的影响[J]. 材料工程, 2008, 0(1): 61-63,67.
[7] 杨胜, 易丹青, 杨守杰, 钟利. 腐蚀环境下2E12航空铝合金疲劳裂纹扩展行为研究[J]. 材料工程, 2007, 0(12): 26-29,34.
[8] 曲迎东, 崔成松, 曹福洋, 陈善本, 李庆春. 喷射沉积坯体特征尺寸的神经网络模型建立与仿真[J]. 材料工程, 2005, 0(8): 15-19.
[9] 李小军, 吴建生, 章靖国, 史海生, 林一坚. 喷射成形超高碳钢超塑性变形后的微观组织[J]. 材料工程, 2004, 0(6): 20-23.
[10] 许富民, 朱世杰, 赵杰, 王富岗. SiCp/Al梯度复合材料疲劳裂纹扩展和亚临界扩展行为[J]. 材料工程, 2003, 0(10): 11-13.
[11] 周灿栋, 樊俊飞, 林一坚, 孙德生, 乐海荣, 章靖国. 喷射成形轧辊材料组织和性能分析[J]. 材料工程, 2003, 0(10): 42-45.
[12] 杨林, 田冲, 陈桂云, 赵九洲, 张永昌, 叶恒强. 喷射沉积AlZn12Mg2Cu2合金的组织结构及力学性能[J]. 材料工程, 2002, 0(2): 23-26.
[13] 马康民, 宣建光, 康进兴. 30CrMnSi2A钢飞机主梁疲劳断裂分析[J]. 材料工程, 2001, 0(10): 42-44.
[14] 许凤和, 薛建高. 有机玻璃疲劳裂纹扩展试验分析[J]. 材料工程, 1999, 0(10): 40-41.
[15] 王建强, 常新春, 郝云彦, 侯万良, 胡壮麒. 喷射成形过程的实时监测与智能控制技术[J]. 材料工程, 1998, 0(2): 47-49.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn