方旭东1,2,3, 王岩1,2, 范光伟2, 夏焱1,2, 王志斌1,2, 韩培德3
1 太原钢铁(集团)有限公司 先进不锈钢材料国家重点实验室, 太原 030003;
2 山西太钢不锈钢股份有限公司 技术中心, 太原 030003;
3 太原理工大学 材料科学与工程学院, 太原 030024
Stress Rupture and Precipitation Behavior of TP310HCbN(HR3C) for Supercritical Boilers
FANG Xu-dong1,2,3, WANG Yan1,2, FAN Guang-wei2, XIA Yan1,2, WANG Zhi-bin1,2, HAN Pei-de3
1 State Key Laboratory of Advanced Stainless Steel Materials, Taiyuan Iron & Steel(Group) Co., Ltd., Taiyuan 030003, China;
2 Technology Center, Shanxi Taiyuan Stainless Steel Co., Ltd., Taiyuan 030003, China;
3 College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China
全文: PDF(7541 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 采用持久试样方法,结合Gleeble、硬度分析、SEM、EDS、TEM等分析手段,对TP310HCbN耐热钢热变形以及在650℃与700℃条件下持久及析出行为进行了分析。结果表明:两种持久温度条件下,硬度变化趋势差别不大;随着持久时间延长,TP310HCbN耐热钢晶内析出物由颗粒状转变为棒状,并存在大量与位错相互作用的蠕虫状NbCrN析出物;太钢生产的TP310HCbN耐热钢650℃/700℃-100000h外推持久强度均满足标准要求。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
方旭东
王岩
范光伟
夏焱
王志斌
韩培德
关键词 TP310HCbN析出相持久硬度    
Abstract:Using persistent experiment method, combined with Gleeble,hardness analysis, SEM, EDS, TEM and other analytical methods, the hot deformation, stress rupture and precipitation behavior of TP310HCbN heat resistance steel was analysed at 650℃ and 700℃, the results show that:the change of the hardness is not obviously under two different stress rupture temperature; with stress rupture time prolongs, TP310HCbN heat-resistant steel intragranular precipitates from granular into rod-shaped, and presence of wormlike NbCrN rich precipitates and dislocation interactions; Taiyuan Iron and Steel production of TP310HCbN heat-resistant steel at 650/700℃-100000h extrapolation lasting strength meet the standard requirements.
Key wordsTP310HCbN    precipitation phase    stress rupture    hardness
收稿日期: 2015-08-28      出版日期: 2017-06-20
中图分类号:  TG113.2  
通讯作者: 方旭东(1975-),男,高级工程师,硕士,从事不锈钢研究,联系地址:山西省太原市尖草坪街2号太钢技术中心(030003),E-mail:fangxd@tisco.com.cn     E-mail: fangxd@tisco.com.cn
引用本文:   
方旭东, 王岩, 范光伟, 夏焱, 王志斌, 韩培德. 超超临界锅炉材料TP310HCbN(HR3C)持久及析出行为[J]. 材料工程, 2017, 45(6): 112-117.
FANG Xu-dong, WANG Yan, FAN Guang-wei, XIA Yan, WANG Zhi-bin, HAN Pei-de. Stress Rupture and Precipitation Behavior of TP310HCbN(HR3C) for Supercritical Boilers. Journal of Materials Engineering, 2017, 45(6): 112-117.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2015.001068      或      http://jme.biam.ac.cn/CN/Y2017/V45/I6/112
[1] RAE C. Alloys by design:modelling next generation superalloys[J]. Materials Science and Technology, 2009, 25(4):479-487.
[2] COWEN C J, DANIELSON P E, JABLONSKI P D. The microstructural evolution of Inconel alloy 740 during solution treatment, aging, and exposure at 760℃[J]. Journal of Materials Engineering and Performance, 2011, 20(6):1078-1083.
[3] VISWANATHAN R, COLEMAN K, RAO U. Materials for ultra-supercritical coal-fired power plant boilers[J]. International Journal of Pressure Vessels and Piping, 2006, 83(11-12):778-783.
[4] 谢锡善,赵双群,董建新,等.超超临界电站用Inconel740镍基合金的组织稳定性及其改型研究[J].动力工程学报,2011,31(8):638-643. XIE X S, ZHAO S Q, DONG J X, et al. Structural stability and improvement of Inconel alloy 740 for ultra supercritical power plants[J]. Power Engineering, 2011, 31(8):638-643.
[5] 赵美兰,孙文儒,杨树林,等.GH761变形高温合金的热变形行为[J].金属学报,2009,45(1):79-83. ZHAO M L, SUN W R, YANG S L, et al. Hot deformation behavior of GH761 wrought Ni base superalloy[J]. Acta Metallurgica Sinica, 2009, 45(1):79-83.
[6] McQUEEN H J.Development of dynamic recrystallization theory[J].Materials Science and Engineering:A,2004,387-389:203-208.
[7] POLIAKT E I,JONASS J J.A one-parameter approach to determining the critical condition for the initiation of dynamic recrystallization[J].Acta Materialia,1996,44(1):127-136.
[8] 李莎,曾莉,苗华军,等.镍基高温合金GH4700的热变形行为及热加工图[J].材料热处理学报,2013,34(9):51-56. LI S, ZENG L, MIAO H J, et al. Hot deformation behavior and processing maps of Ni-based superalloy GH4700[J]. Transactions of Materials and Heat Treatment, 2013, 34(9):51-56.
[9] McQUEEN H J,RYAN N D.Constitutive analysis in hot working[J].Materials Science and Engineering:A,2002,322:43-63.
[10] ROBI P S,DIXIT U S.Application of neural networks in generating processing map for hot working[J].Journal of Materials Processing Technology,2003, 142:289-294.
[11] PARK N K,YOEM J T,NA Y S.Characterization of deformation stability in hot forging of conventional Ti-6Al-4V using processing maps[J].Journal of Materials Processing Technology,2002, 130-131(3):540-545.
[12] QUN Z S, SHAN X X, SMITH G D, et al. Microstructure stability and mechanical properties of a new nickel-based superalloy[J]. Materials Science and Engineering:A, 2003, 355:96-105.
[13] QUN Z S, SHAN X X, SMITH G D, et al. Gamma prime coarsening and age-hardening behaviors in a new nickel base superalloy[J]. Materials Letters, 2004, 58(11):1784-1787.
[14] 杨素宝,刘正东,程世长. 超超临界火电机组用关键锅炉钢性能分析[J]. 钢铁研究学报,2010,22(1):37-42. YANG S B, LIU Z D, CHENG S C. Property analysis of key boiler steels used for ultra-supercritical power plants[J]. Journal of Iron and Steel Research, 2010, 22(1):37-42.
[15] SIMS C T, STOLOFF N S, HAGEL W C. 高温合金[M].赵杰,译.大连:大连理工大学出版社,1992.
[16] 方园园,赵杰,李晓娜. HR3C钢高温时效过程中的析出相[J]. 金属学报,2010,46(7):844-849. FANG Y Y, ZHAO J, LI X N. Precipitates in HR3C steel aged at high temperature[J]. Acta Metallurgica Sinica, 2010, 46(7):844-849.
[1] 范淑敏, 陈送义, 张星临, 周亮, 黄兰萍, 陈康华. 多级时效热处理对7056铝合金析出组织与耐蚀性的影响[J]. 材料工程, 2019, 47(6): 136-143.
[2] 王飞云, 金建军, 江志华, 王晓震, 胡春文. 热处理温度对新型马氏体时效不锈钢微观组织和性能的影响[J]. 材料工程, 2019, 47(6): 152-160.
[3] 陈林, 陈文静, 黄强, 熊中. 超声振动对EA4T钢激光熔覆质量和性能的影响[J]. 材料工程, 2019, 47(5): 79-85.
[4] 赵云松, 郭媛媛, 赵敬轩, 张晓铁, 刘砚飞, 杨岩, 姜华, 张剑, 骆宇时. 微量Hf对大角度晶界含Re双晶合金高温持久性能的影响[J]. 材料工程, 2019, 47(2): 76-83.
[5] 钟蛟, 彭志方, 陈方玉, 彭芳芳, 刘省, 石振斌. P92钢奥氏体化后的冷却方式对650℃时效组织及硬度稳定性的影响[J]. 材料工程, 2019, 47(1): 119-124.
[6] 郑欢欢, 刘鑫禹, 陈亚楠, 张从林, 吕鹏, 蔡杰, 关庆丰. 20钢强流脉冲电子束表面合金化的微观组织和性能[J]. 材料工程, 2018, 46(7): 127-135.
[7] 邓德伟, 牛婷婷, 田鑫, 刘海英, 孙奇, 张林. 水导轴承等离子堆焊Ni60合金组织及其耐腐蚀性能[J]. 材料工程, 2018, 46(5): 106-111.
[8] 龚玉兵, 王善林, 李宏祥, 柯黎明, 陈玉华, 马彬. 脉冲宽度对激光熔覆FeSiB涂层组织与硬度的影响[J]. 材料工程, 2018, 46(3): 74-80.
[9] 李会芳, 赵杰, 程从前, 闵小华, 曹铁山, 许军. 基于Zc参数的HP耐热合金高温蠕变及持久寿命的预测方法[J]. 材料工程, 2018, 46(3): 112-116.
[10] 丁小龙, 胡振峰, 金国, 吕镖, 汪笑鹤. 电刷镀Ni-石墨烯复合镀层的组织结构及性能[J]. 材料工程, 2018, 46(11): 110-117.
[11] 杜际雨, 李方义, 鹿海洋, 商建通, 李振. 大气等离子喷涂NiCrBSi-Mo/Ni涂层中黏结层对NiCrBSi-Mo复合工作层性能的影响[J]. 材料工程, 2017, 45(9): 86-92.
[12] 韩素琦, 刘胜胆, 李承波, 雷越, 邓运来, 张新明. 淬火速率对Al-Zn-Mg-Cu-Cr合金挤压棒材组织及硬度的影响[J]. 材料工程, 2017, 45(4): 9-14.
[13] 王恩青, 岳建岭, 李淼磊, 李栋, 黄峰. Si含量对VAlSiN涂层微结构、力学性能和摩擦磨损性能的影响[J]. 材料工程, 2017, 45(4): 70-76.
[14] 赵龙志, 刘武, 刘德佳, 赵明娟, 张坚. SiC含量对激光熔覆SiC/Ni60A复合涂层显微组织和耐磨性能的影响[J]. 材料工程, 2017, 45(3): 88-94.
[15] 乔及森, 向阳芷, 聂书才, 张涵. 铝镁异种金属复合挤压成形及界面微观组织[J]. 材料工程, 2017, 45(11): 78-83.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn