材料工程  2016, Vol. 44 Issue (3): 15-20    DOI: 10.11868/j.issn.1001-4381.2016.03.003
  材料与工艺 本期目录 | 过刊浏览 | 高级检索 |
表面纳米化-微弧氧化复合涂层对铝合金拉伸性能影响机制研究
文磊1, 王亚明2, 金莹1
1. 北京科技大学国家材料服役安全科学中心, 北京 100083;
2. 哈尔滨工业大学特种陶瓷研究所, 哈尔滨 150080
Influence of SNC-MAO Composite Coating on Tensile Properties of Aluminum Alloy
WEN Lei1, WANG Ya-ming2, JIN Ying1
1. National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China;
2. Institute of Advanced Ceramics, Harbin Institute of Technology, Harbin 150080, China
全文: PDF(8660 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 通过表面机械研磨处理(SMAT)在LY12CZ铝合金表面制备表面纳米化(SNC)过渡层,再采用微弧氧化(MAO)技术对纳米晶过渡层进行微结构重构,设计制备出纳米化-微弧氧化(SNC-MAO)复合涂层,并对比研究了表面纳米化、微弧氧化及纳米化-微弧氧化复合处理对基体铝合金拉伸性能的影响。结果表明,微弧氧化处理使基体铝合金的屈服强度和抗拉强度减小,而纳米化-微弧氧化复合处理则增加了基体铝合金的屈服强度和抗拉强度。在拉伸伸长率8%的条件下,相同厚度的纳米化-微弧氧化复合涂层比微弧氧化涂层具有更好的抗拉伸破坏能力,表现出更好的膜基结合性能。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
文磊
王亚明
金莹
关键词 铝合金表面纳米化表面机械研磨处理微弧氧化拉伸性能    
Abstract:A duplex process was designed to modify the alloy surface using surface mechanical attrition treatment (SMAT) prior to microarc oxidation (MAO). A surface nanocrystalline (SNC) layer was formed on the surface of Al alloy by SMAT,on which a ceramic coating grew by MAO,finally the SNC-MAO composite coating are fabricated. The tensile properties of the SMATed alloy,MAO coating and SNC-MAO composite coating were comparatively evaluated. Experimental results show that the yield strength and tensile strength of the substrate Al alloy are reduced after MAO treatment,while those of SNC-MAO treated samples are improved due to the introduction of SMAT pre-treatment. When the elongation is 8%,SNC-MAO coating shows better tensile and adhesion properties compared with MAO coating with the same thickness.
Key wordsaluminum alloy    surface nanocrystallization    surface mechanical attrition treatment    microarc oxidation    tensile property
收稿日期: 2015-04-24      出版日期: 2016-03-22
中图分类号:  TG561  
通讯作者: 文磊(1982-),男,助理研究员,博士,研究方向为表面工程,联系地址:北京市海淀区学院路30号北京科技大学项目建设指挥部(100083),E-mail:wenlei@ustb.edu.cn     E-mail: wenlei@ustb.edu.cn
引用本文:   
文磊, 王亚明, 金莹. 表面纳米化-微弧氧化复合涂层对铝合金拉伸性能影响机制研究[J]. 材料工程, 2016, 44(3): 15-20.
WEN Lei, WANG Ya-ming, JIN Ying. Influence of SNC-MAO Composite Coating on Tensile Properties of Aluminum Alloy. Journal of Materials Engineering, 2016, 44(3): 15-20.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.03.003      或      http://jme.biam.ac.cn/CN/Y2016/V44/I3/15
[1] 汝继刚,伊琳娜.高强铝合金表面强化工艺研究[J].稀有金属,2004,28(1):182-184. RU J G,YI L N. Surface strengthen process for high strength aluminum alloy[J]. Chinese Journal of Rare Metals, 2004,28(1):182-184.
[2] 常红,韩恩厚,王俭秋,等.飞机蒙皮涂层对LY12CZ铝合金腐蚀疲劳寿命的影响[J].中国腐蚀与防护学报,2006,26(1):34-36. CHANG H,HAN E H,WANG J Q,et al. Influence of coating of covering airplane on corrosion fatigue life of aluminium alloy LY12CZ[J]. Journal of Chinese Society for Corrosion and Protection,2006,26(1):34-36.
[3] YEROKHIN A L,VOEVODIN A A,LYUBIMOV V V,et al. Plasma electrolytic fabrication of oxide ceramic surface layers for tribotechnical purposes on aluminium alloys[J]. Surface and Coatings Technology,1998,110(3):140-146.
[4] YEROKHIN A L,LYUBIMOV V V,ASHITKOV R V. Phase formation in ceramic coatings during plasma electrolytic oxidation of aluminium alloys[J]. Ceramics International,1998,24(1):1-6.
[5] GERASIMOV M V,NIKOLAEV V A,SHCHERBAKOV A N. Microplasma oxidation of metals and alloys[J]. Metallurgist, 1994,38(7-8):179.
[6] 夏伶勤, 韩建民, 崔世海, 等. SiCp/A356复合材料微弧氧化陶瓷膜的生长规律与性能[J]. 材料工程, 2016, 44(1):40-46. XIA L Q, HAN J M, CUI S H, et al. Growth law and properties of ceramic coatings on SiCp/A356 composite fabricated by micro-arc oxidation[J]. Journal of Materials Engineering, 2016, 44(1):40-46.
[7] BAXI J,KAR P,LIANG H,et al. Tribological characterization of microarc oxidized alumina coatings for biological applications[J]. Vacuum,2008,83(1):217-222.
[8] SRINIVASAN P B,LIANG J,BLAWERT C,et al. Effect of current density on the microstructure and corrosion behaviour of plasma electrolytic oxidation treated AM50 magnesium alloy[J]. Applied Surface Science,2009,255(7):4212-4218.
[9] LIANG J,SRINIVASAN P B,BLAWERT C,et al. Electrochemical corrosion behaviour of plasma electrolytic oxidation coatings on AM50 magnesium alloy formed in silicate and phosphate based electrolytes[J]. Electrochimica Acta,2009,54(14):3842-3850.
[10] ARSLAN E,TOTIK Y,DEMIRCI E E,et al. High temperature wear behavior of aluminum oxide layers produced by AC microarc oxidation[J]. Surface and Coatings Technology,2009,204(6-7):829-833.
[11] XUE W B,WANG C,LI Y L,et al. Effect of microarc discharge surface treatment on the tensile properties of Al-Cu-Mg alloy[J]. Materials Letters,2002,56(5):737-743.
[12] LU K,LV J. Surface nanocrystallization (SNC) of metallic materials-presentation of the concept behind a new approach[J]. Journal of Materials Science and Technology,1999,15(3):193-197.
[13] WEN L,WANG Y M,JIN Y,et al. Design and characterization of SMAT-MAO composite coating and its influence on the fatigue property of 2024 Al alloy[J]. Rare Metal Materials and Engineering,2014,43(7):1582-1587.
[14] WEN L,WANG Y M,ZHOU Y,et al. Microstructure and corrosion resistance of modified 2024 Al alloy using surface mechanical attrition treatment combined with microarc oxidation process[J]. Corrosion Science,2011,53(1):473-480.
[15] WEN M,LIU G,GU J F,et al. The tensile properties of titanium processed by surface mechanical attrition treatment[J]. Surface and Coatings Technology,2008,202(19):4728-4733.
[16] 薛文斌,邓志威,陈如意,等.微弧氧化表面处理对铝合金拉伸性能的影响[J].金属热处理学报,1999,20(4):1-5. XUE W B,DENG Z W,CHEN R Y,et al. Influence of microarc oxidation surface treatment on the tensile properties of aluminum alloy[J]. Transactions of Metal Heat Treatment,1999,20(4):1-5.
[1] 范淑敏, 陈送义, 张星临, 周亮, 黄兰萍, 陈康华. 多级时效热处理对7056铝合金析出组织与耐蚀性的影响[J]. 材料工程, 2019, 47(6): 136-143.
[2] 王玉洁, 张鹏, 王选, 杜云慧, 王胜林, 张伟一, 鹿红梅. 氧气流量对LY12铝合金微弧氧化膜致密性的影响[J]. 材料工程, 2019, 47(5): 86-92.
[3] 李雅莉, 雷力明, 侯慧鹏, 何艳丽. 热工艺对激光选区熔化Hastelloy X合金组织及拉伸性能的影响[J]. 材料工程, 2019, 47(5): 100-106.
[4] 李惠, 肖文龙, 张艺镡, 马朝利. 多重结构Ti-B4C/Al2024复合材料的组织和力学性能[J]. 材料工程, 2019, 47(4): 152-159.
[5] 常海, 郭雪刚, 文磊, 金莹. SiC纳米颗粒对TC4钛合金微弧氧化涂层组织结构及耐蚀性能的影响[J]. 材料工程, 2019, 47(3): 109-115.
[6] 宋仁国. 微弧氧化技术的发展及其应用[J]. 材料工程, 2019, 47(3): 50-62.
[7] 李卫, 陈康华, 焦慧彬, 周亮, 杨振, 陈送义. 微量Ge对7056铝合金组织和淬火敏感性的影响[J]. 材料工程, 2019, 47(3): 123-130.
[8] 周航, 张峥. AlSi10Mg(Cu)铸铝合金的热疲劳裂纹萌生及早期扩展行为[J]. 材料工程, 2019, 47(3): 131-138.
[9] 陈跃良, 王安东, 卞贵学, 张勇. CF8611/AC531复合材料性能及与7B04铝合金电偶腐蚀的电化学研究[J]. 材料工程, 2019, 47(1): 97-105.
[10] 周梦林, 饶少凯, 周均, 郑照县, 肖衡, 郑靖. 微弧氧化处理镁合金在接骨板服役工况下的微动磨损特性[J]. 材料工程, 2018, 46(9): 80-87.
[11] 马慧媛, 刘慧丛, 石文静, 施丽铭, 李卫平, 朱立群. 应力载荷作用下5A06铝合金薄板材料在盐水中腐蚀行为[J]. 材料工程, 2018, 46(9): 152-159.
[12] 万闪, 姜丹, 蔡光义, 廖圣智, 董泽华. 铝合金超疏水转化膜的制备与性能[J]. 材料工程, 2018, 46(9): 144-151.
[13] 黄元春, 许天成, 肖政兵, 任贤魏, 贾广泽. 弥散相对3003铝合金再结晶晶粒尺寸的影响[J]. 材料工程, 2018, 46(6): 65-72.
[14] 徐勇, 靳鹏飞, 田亚强, 张士宏, 王礼良, 曾一畔. 铝合金局部热处理技术及其在板材成形中的应用发展现状[J]. 材料工程, 2018, 46(5): 44-55.
[15] 王驰, 冉广, 雷鹏辉, 黄金华. SA508 Gr.3 Cl.1钢的疲劳和高温拉伸性能[J]. 材料工程, 2018, 46(5): 151-158.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn