Zr元素对AlFeCrCoCuZrx高熵合金组织及腐蚀性能的影响
谢红波1, 刘贵仲1, 郭景杰2
1. 桂林电子科技大学 广西信息材料重点实验室, 广西 桂林 541004;
2. 哈尔滨工业大学 材料科学与工程学院, 哈尔滨 150001
Effect of Zr Addition on Microstructure and Corrosion Properties of AlFeCrCoCuZrx High-entropy Alloys
XIE Hong-bo1, LIU Gui-zhong1, GUO Jing-jie2
1. Guangxi Key Laboratory of Information Materials, Guilin University of Electronic Technology, Guilin 541004, Guangxi, China;
2. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
全文: PDF(7714 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 对铸态AlFeCrCoCuZrx (x=0, 0.5, 1)多组元高熵合金的微观组织、硬度及其在3.5%NaCl溶液中的耐腐蚀性能进行了研究。研究表明:合金微观组织为典型的树枝晶结构,随着Zr元素的加入,枝晶由单一的BCC相转变为由两相组成,而枝晶间由富Cu的FCC相组成并保持不变。合金硬度随Zr元素的增加而提高,AlFeCrCoCuZr合金的硬度达到698HV。合金在3.5%NaCl溶液中的耐蚀性能均优于304L不锈钢,但随着Zr含量的增加,合金的耐蚀性降低。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
谢红波
刘贵仲
郭景杰
关键词 高熵合金组织结构硬度耐蚀性    
Abstract:The microstructure, hardness and the corrosion resistance in 3.5% NaCl solution of the as-cast AlFeCrCoCuZrx(x=0, 0.5, 1) high-entropy alloys were investigated. The results show that typically cast dendrite structure is formed in the alloys. With the increase of Zr addition, phases in the dendrite region change from single BCC structure to two phases, while phase in the interdendrite region is Cu-rich FCC structure and kept unchanged. The hardness of the alloys increases with the increase of Zr addition and hardness AlFeCrCoCuZr alloy reaches the maximum of HV 698. The corrosion resistance of these alloys in 3.5% NaCl solution is better than that of 304L stainless steel, however as the Zr content increases, the corrosion resistance of alloys is degenerated.
Key wordshigh-entropy alloy    microstructure    hardness    corrosion resistance
收稿日期: 2014-06-18      出版日期: 2016-06-13
中图分类号:  TG113.12  
通讯作者: 刘贵仲(1974-),男,博士,副教授,主要从事高熵合金方面的研究工作,联系地址:广西桂林电子科技大学(541004),E-mail:lgzlgz@guet.edu.cn     E-mail: lgzlgz@guet.edu.cn
引用本文:   
谢红波, 刘贵仲, 郭景杰. Zr元素对AlFeCrCoCuZrx高熵合金组织及腐蚀性能的影响[J]. 材料工程, 2016, 44(6): 44-49.
XIE Hong-bo, LIU Gui-zhong, GUO Jing-jie. Effect of Zr Addition on Microstructure and Corrosion Properties of AlFeCrCoCuZrx High-entropy Alloys. Journal of Materials Engineering, 2016, 44(6): 44-49.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.06.007      或      http://jme.biam.ac.cn/CN/Y2016/V44/I6/44
[1] YEH J W. Alloy design strategies and future trends in high-entropy alloys[J]. Metals & Materials Society, 2013, 65:1759-1771.
[2] ZHANG Y, YANG X, LIAW P K. Alloy design and properties optimization of high-entropy alloys[J]. Metals & Materials Society, 2013, 64:831-838.
[3] REN M X, LI B S, FU H Z. Formation condition of solid solution type high-entropy alloy[J]. Transactions of Nonferrous Metals Society of China, 2013, 23:991-995.
[4] 梁秀兵, 魏敏, 程江波, 等. 高熵合金新材料的研究进展[J]. 材料工程, 2009, (12):75-79. LIANG X B, WEI M, CHENG J B, et al. Reaserch progress in advanced materials of high-entropy alloys[J]. Journal of Materials Engineering, 2009, (12):75-79.
[5] 周云军, 张勇, 王艳丽, 等. 多组元AlTiVCrMnFeCoNiCu高熵合金的室温力学性能[J]. 北京科技大学学报, 2008, 30(7):765-769. ZHOU Y J, ZHANG Y, WANG Y L, et al. Room temperature mechanical properties of the AlTiVCrMnFeCoNiCu high-entropy alloy system with multi-principal elements[J]. Journal of University of Science and Technology Beijing, 2008, 30(7):765-769.
[6] 刘恕骞, 黄维刚. AlCoCrNiSi<em>x高熵合金微观组织结构与力学性能[J]. 材料工程, 2012, (1):5-8. LIU S Q, HUANG W G. Microstructure and mechanical performance of AlCoCrNiSix high-entropy alloys[J]. Journal of Materials Engineering, 2012, (1):5-8.
[7] ZUO T T, REN S B, LIAW P K. et al. Processing effects on the magnetic and mechanical properties of FeCoNiAl0.2Si0.2 high entropy alloy[J]. International Journal of Minerals, Metallurgy and Materials, 2013, 20(6):549-555.
[8] WU J M, LIN S J, YEH J W. Adhesive wear behavior of AlCoCrCuFeNi high-entropy alloys as a function of aluminum content[J]. Wear, 2006, 261:513-519.
[9] LI B Y, PENG K, HU A P, et al. Structure and properties of FeCoNiCrCu0.5Alx high-entropy alloy[J]. Transactions of Nonferrous Metals Society of China, 2013, 22:735-741.
[10] HUANG Y S, CHEN L, LIU H W. Microstructure, hardness, resistivity and thermal stability of sputtered oxide films of AlCoCrCu0.5NiFe high-entropy alloy[J]. Materials Science and Engineering:A, 2007, 457(1-2):77-81.
[11] 叶均蔚, 陈瑞凯. 高熵合金的发展概况[J]. 工业材料杂志, 2005, 224:71-75. YEH J W, CHEN S K. Development of high entropy alloys[J]. Journal of Industrial Materials, 2005, 224:71-75.
[12] 张勇, 周云军, 陈国良. 快速发展中的高熵溶体合金[J]. 物理, 2008, 37(8):601-605. ZHANG Y, ZHOU Y J, CHEN G L. Rapid development of high entropy solution alloys[J]. Physical, 2008, 37(8):601-605.
[13] QIU X W, ZHANG Y P, HE L, et al. Microstructure and corrosion resistance of AlCrFeCuCo high entropy alloy[J]. Journal of Alloys and Compounds, 2013, 549:195-199.
[14] 王艳苹, 李邦盛. AlCrFeCoNiCu多组元合金及其复合材料的组织与性能[D]. 哈尔滨:哈尔滨工业大学, 2009. WANG Y P, LI B S. Microstructure and properties of AlCrFeCoNiCu multi-principal-element alloys and its composites[D]. Harbin:Harbin Industrial University, 2009.
[15] INOUE A. Stabilization of metallic supercooled liquid and bulk amorphous alloys[J]. Acta Materialia, 2000, 48:279-306.
[16] 任明星, 李邦盛. CrFeCoNiCu多主元高熵合金的相分析[J]. 材料工程, 2012, (1):9-12. REN M X, LI B S. Phase analysis of CrFeCoNiCu high-entropy alloy[J]. Journal of Materials Engineering, 2012, (1):9-12.
[17] REVIE R, WINSTON U. Corrosion Handbook[M]. New York:J Wiely & Sons, 2005.
[1] 马明星, 王志新, 梁存, 周家臣, 张德良, 朱达川. CeO2掺杂对AlCoCrCuFe高熵合金的组织结构与摩擦磨损性能的影响[J]. 材料工程, 2019, 47(7): 106-111.
[2] 王桂芳, 刘忠侠, 张国鹏. 球磨时间对热压烧结制备TiC-CoCrFeNi复合材料微观组织及力学性能的影响[J]. 材料工程, 2019, 47(6): 94-100.
[3] 范淑敏, 陈送义, 张星临, 周亮, 黄兰萍, 陈康华. 多级时效热处理对7056铝合金析出组织与耐蚀性的影响[J]. 材料工程, 2019, 47(6): 136-143.
[4] 陈林, 陈文静, 黄强, 熊中. 超声振动对EA4T钢激光熔覆质量和性能的影响[J]. 材料工程, 2019, 47(5): 79-85.
[5] 陈刚, 王璐, 杨静, 李强, 吕品, 马胜国. Al0.1CoCrFeNi高熵合金的力学性能和变形机理[J]. 材料工程, 2019, 47(1): 106-111.
[6] 钟蛟, 彭志方, 陈方玉, 彭芳芳, 刘省, 石振斌. P92钢奥氏体化后的冷却方式对650℃时效组织及硬度稳定性的影响[J]. 材料工程, 2019, 47(1): 119-124.
[7] 彭竹琴, 李俊魁, 卢金斌, 马明星, 吴玉萍. 稀土CeO2对AlCoCuFeMnNi高熵合金组织与性能的影响[J]. 材料工程, 2018, 46(8): 91-97.
[8] 杨慧慧, 杨晶晶, 喻寒琛, 王泽敏, 曾晓雁. 激光选区熔化成形TC4合金腐蚀行为[J]. 材料工程, 2018, 46(8): 127-133.
[9] 杨胶溪, 贾无名, 王欣, 文强, 张晏玮, 柏广海, 王荣山. 激光熔凝处理对Zr-1Nb核燃料包壳组织和性能的影响[J]. 材料工程, 2018, 46(8): 120-126.
[10] 郑欢欢, 刘鑫禹, 陈亚楠, 张从林, 吕鹏, 蔡杰, 关庆丰. 20钢强流脉冲电子束表面合金化的微观组织和性能[J]. 材料工程, 2018, 46(7): 127-135.
[11] 刘军, 张金玲, 渠治波, 于彦冲, 许并社, 王社斌. 稀土Gd对AZ31镁合金耐蚀性能的影响[J]. 材料工程, 2018, 46(6): 73-79.
[12] 邓德伟, 牛婷婷, 田鑫, 刘海英, 孙奇, 张林. 水导轴承等离子堆焊Ni60合金组织及其耐腐蚀性能[J]. 材料工程, 2018, 46(5): 106-111.
[13] 龚玉兵, 王善林, 李宏祥, 柯黎明, 陈玉华, 马彬. 脉冲宽度对激光熔覆FeSiB涂层组织与硬度的影响[J]. 材料工程, 2018, 46(3): 74-80.
[14] 肖代红, 刘彧, 余永新, 周鹏飞, 刘文胜, 马运柱. 放电等离子烧结对TiB2/AlCoCrFeNi复合材料组织与性能的影响[J]. 材料工程, 2018, 46(3): 22-27.
[15] 张曼莉, 邱长军, 蒋艳林, 郑文权, 夏琰. 激光原位合成Al2O3-TiO2复合陶瓷涂层组织结构与性能[J]. 材料工程, 2018, 46(2): 57-65.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn