烧结颈分布对3D打印覆膜Al2O3零件强度的影响
赵枢明, 薛铠华, 杨通, 张雪, 姚山
大连理工大学 材料科学与工程学院, 辽宁 大连 116024
Effect of sintered neck distribution on strength of 3D printing coated Al2O3 parts
ZHAO Shu-ming, XUE Kai-hua, YANG Tong, ZHANG Xue, YAO Shan
School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, Liaoning, China
全文: PDF(7516 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 从烧结颈的尺寸及分布入手,研究覆膜Al2O3粉末的粒径分布对零件强度的影响。使用UV激光对覆膜粉末进行原位加热,在影像测量仪下测量并获得烧结颈束腰直径与颗粒直径之间的关系。建立颗粒堆积模型,将烧结颈分布与颗粒配位点对应,计算得出某一截面上被断开的烧结颈的投影面积比例。结果表明:对于2%(质量分数)树脂含量的覆膜Al2O3粉末,随着颗粒直径从75μm增长至375μm,烧结颈的束腰直径从40μm增长至100μm。而堆积模拟结果显示,随着颗粒直径从75~107μm区间增加至300~375μm区间,烧结颈的投影面积比例从0.2557降低至0.0823,与实验测量的覆膜Al2O3粉末的抗拉强度的趋势一致。将70/100,100/140目的颗粒按照质量比0:10,1:9,2:8,3:7,4:6,5:5,6:4,7:3,8:2,9:1,10:0混合后计算,发现投影面积比例从0.1772降低至0.1264,孔隙率从0.4511升高至0.4633。综合考虑抗拉强度及透气性,得出优化结果为两者比例为7:3时,投影面积比为0.1481,堆积孔隙率为0.4596。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
赵枢明
薛铠华
杨通
张雪
姚山
关键词 烧结颈颗粒堆积覆膜Al2O3粉末抗拉强度3D打印激光选区烧结    
Abstract:The influence of the particle size distribution on the strength of the coated Al2O3 parts was studied, through the size and distribution of the sintered neck. The powder was heated in situ by a UV laser, and the relationship between the sintered neck waist diameter and the particle diameter was obtained under an image measuring apparatus. A particle packing model was established, and the distribution of the sintered neck was corresponding to the particle coordination point, then the projected area ratio of the sintered neck that was broken in a certain section was calculated. As for the coated Al2O3 powder with the resin content of 2%(mass fraction), the results indicate that the sintered neck waist diameter increases from 40μm to 100μm as the particle diameter increases from 75μm to 375μm. The packing simulation results show that the projected area ratio decreases from 0.2557 to 0.0823, as the particle diameter increases from 75-107μm to 300-375μm, which is consistent with the experimentally measured tensile strength of the coated Al2O3 powder. The 70/100, 100/140 mesh powder are mixed to simulate based on the mass ratios of 0:10, 1:9, 2:8, 3:7, 4:6, 5:5, 6:4, 7:3, 8:2, 9:1, 10:0. The projected area ratio decreases from 0.1772 to 0.1264 and the porosity increases from 0.4511 to 0.4633. Considering the tensile strength and gas permeability, the optimization result is that the ratio is 7:3, the projected area ratio is 0.1481 and the porosity is 0.4596.
Key wordssintered neck    particle packing    coated Al2O3 powder    tensile strength    3D printing    select-ive laser sintering
收稿日期: 2018-09-17      出版日期: 2019-08-22
中图分类号:  TB332  
通讯作者: 姚山(1966-),男,教授,硕士,从事砂型激光3D打印技术及应用研究,联系地址:辽宁省大连市甘井子区凌工路2号大连理工大学铸造中心311室(116024),E-mail:yaoshan@dlut.edu.cn     E-mail: yaoshan@dlut.edu.cn
引用本文:   
赵枢明, 薛铠华, 杨通, 张雪, 姚山. 烧结颈分布对3D打印覆膜Al2O3零件强度的影响[J]. 材料工程, 2019, 47(8): 132-140.
ZHAO Shu-ming, XUE Kai-hua, YANG Tong, ZHANG Xue, YAO Shan. Effect of sintered neck distribution on strength of 3D printing coated Al2O3 parts. Journal of Materials Engineering, 2019, 47(8): 132-140.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2018.001092      或      http://jme.biam.ac.cn/CN/Y2019/V47/I8/132
[1] GUSTAFSON R,SPADA A T.Prototyping process produces sand molds,cores for production castings[J].Journal of Applied Probability,2002,92(2):38-39.
[2] CHHABRA M,SINGH R.Rapid casting solutions:a review[J].Rapid Prototyping Journal,2011,17(5):328-350.
[3] 张学军,唐思熠,肇恒跃,等.3D打印技术研究现状和关键技术[J].材料工程,2016,44(2):122-128. ZHANG X J,TANG S Y,ZHAO H Y,et al.Research status and key technologies of 3D printing[J].Journal of Materials Engineering,2016,44(2):122-128.
[4] PHAM D T,DIMOV S,LACAN F.Selective laser sintering:applications and technological capabilities[J].Proceedings of the Institution of Mechanical Engineers Part B Journal of Engineering Manufacture,1999,213(5):435-449.
[5] 纪宏超,张雪静,裴未迟,等.陶瓷3D打印技术及材料研究进展[J].材料工程,2018,46(7):19-28. JI H C,ZHANG X J,PEI W C,et al.Research progress in ceramic 3D printing technology and material development[J].Journal of Materials Engineering,2018,46(7):19-28.
[6] 陈敬炎,吴甲民,陈安南,等.基于激光选区烧结的煤系高岭土多孔陶瓷的制备及其性能[J].材料工程,2018,46(7):36-43. CHEN J Y,WU J M,CHEN A N,et al.Preparation and prop-erties of porous coal-series kaolin ceramics by selective laser sint-ering[J].Journal of Materials Engineering,2018,46(7):36-43.
[7] WEN S F,SHEN Q W,WEI Q S,et al.Material optimization and post-processing of sand molds manufactured by the selective laser sintering of binder-coated Al2O3 sands[J].Journal of Materials Processing Technology,2015,225:93-102.
[8] XU Z F,LIANG P,YANG W,et al.Effects of laser energy density on forming accuracy and tensile strength of selective laser sintering resin coated sands[J].China Foundry,2014,11(3):151-156.
[9] CASALINO G,FILIPPIS L A C D,LUDOVICO A.A technical note on the mechanical and physical characterization of selective laser sintered sand for rapid casting[J].Journal of Materials Processing Technology,2005,166(1):1-8.
[10] VISSCHER W M,BOLSTERLI M.Random packing of equal and unequal spheres in two and three dimensions[J].Nature,1973, 239(5374):504-507.
[11] JODREY W S,TORY E M.Simulation of random packing of spheres[J].Simulation Transactions of the Society for Modeling & Simulation International,1979,32(1):1-12.
[12] ZHOU J H,ZHANG Y W,CHEN J K.Numerical simulation of random packing of spherical particles for powder-based additive manufacturing[J].Journal of Manufacturing Science & Engineering,2009,131(3):031004.
[13] SHI Y,ZHANG Y W.Simulation of random packing of spherical particles with different size distributions[J].Applied Physics A, 2008,92(3):621-626.
[14] DOU X,MAO Y J,ZHANG Y W.Effects of contact force model and size distribution on microsized granular packing[J].Journal of Manufacturing Science & Engineering,2014,136(2):021003.
[15] ZHOU J H,ZHANG Y W,CHEN J K.Numerical simulation of laser irradiation to a randomly packed bimodal powder bed[J].International Journal of Heat and Mass Transfer,2009,52(13/14):3137-3146.
[16] CHENG Y F,GUO S J,LAI H Y.Dynamic simulation of random packing of spherical particles[J].Powder Technology,2000, 107(1/2):123-130.
[17] JIA T,ZHANG Y,CHEN J K,et al.Dynamic simulation of granular packing of fine cohesive particles with different size distributions[J].Powder Technology,2012,218(1):76-85.
[18] HITTI K,BERNACKI M.Optimized dropping and rolling (ODR) method for packing of poly-disperse spheres[J].Applied Mathematical Modelling,2013,37(8):5715-5722.
[19] BERTEI A,CHUEH C C,PHAROAH J G,et al.Modified collective rearrangement sphere-assembly algorithm for random packings of nonspherical particles:towards engineering applic-ations[J].Powder Technology,2014,253:311-324.
[20] PARTELI E J R,POSCHEL T.Particle-based simulation of powder application in additive manufacturing[J].Powder Technology,2016,288:96-102.
[21] TOPIC N,POSCHEL T.Steepest descent ballistic deposition of complex shaped particles[J].Journal of Computational Physics,2016,308:421-437.
[1] 陈鹏, 朱小刚, 吴甲民, 王联凤, 史玉升. 基于SLS/CIP工艺SiC陶瓷的制备及其性能[J]. 材料工程, 2019, 47(3): 87-93.
[2] 纪宏超, 张雪静, 裴未迟, 李耀刚, 郑镭, 叶晓濛, 陆永浩. 陶瓷3D打印技术及材料研究进展[J]. 材料工程, 2018, 46(7): 19-28.
[3] 陈敬炎, 吴甲民, 陈安南, 肖欢, 李国锐, 刘梦月, 李晨辉, 史玉升. 基于激光选区烧结的煤系高岭土多孔陶瓷的制备及其性能[J]. 材料工程, 2018, 46(7): 36-43.
[4] 许婧, 邢悦, 郝思嘉, 任志东, 杨程. 石墨烯/聚合物基复合材料3D打印成型研究进展[J]. 材料工程, 2018, 46(7): 1-11.
[5] 王一博, 赵九蓬. 3D打印柔性可穿戴锂离子电池[J]. 材料工程, 2018, 46(3): 13-21.
[6] 王楠, 燕绍九, 彭思侃, 陈翔, 戴圣龙. 3D打印石墨烯制备技术及其在储能领域的应用研究进展[J]. 材料工程, 2017, 45(12): 112-125.
[7] 张学军, 唐思熠, 肇恒跃, 郭绍庆, 李能, 孙兵兵, 陈冰清. 特约3D打印技术研究现状和关键技术[J]. 材料工程, 2016, 44(2): 122-128.
[8] 王重, 林万明, 马胜国, 杨慧君, 梁红玉, 乔珺威. 冷轧对Al10Cu25Co20Fe20Ni25高熵合金组织结构及力学性能的影响[J]. 材料工程, 2015, 43(8): 50-55.
[9] 闫世兴, 董世运, 徐滨士, 王玉江, 任维彬, 方金祥. 预热温度对灰铸铁表面激光熔覆镍基涂层组织与性能的影响[J]. 材料工程, 2015, 43(1): 30-36.
[10] 葛茂忠, 项建云, 张永康. 激光冲击处理对AZ31B镁合金力学性能的影响[J]. 材料工程, 2013, 0(9): 54-59.
[11] 游国强, 王向杰, 齐冬亮, 郭强, 龙思远. 线能量对挤压AZ91D镁合金GTAW焊接接头组织与性能的影响[J]. 材料工程, 2013, 0(10): 57-63,70.
[12] 刘丽荣, 祖国庆, 李晓宇, 金涛, 胡壮麒. Ru对单晶高温合金拉伸性能的影响[J]. 材料工程, 2012, 0(6): 76-79.
[13] 王晓旭, 陈利. Z-pin的拔出强度试验研究[J]. 材料工程, 2011, 0(11): 1-4.
[14] 张伟, 刘慧, 梁芳慧, 黄永玲. 定向结晶对多孔股骨柄室温拉伸性能的影响[J]. 材料工程, 2009, 0(9): 13-15,19.
[15] 金玉花, 王希靖, 李常锋, 马宁宁. 不同基体组织对搅拌摩擦焊接接头性能的影响[J]. 材料工程, 2008, 0(9): 60-63.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn