Mn对22%Cr双相不锈钢700℃时效σ相及韧性的影响
白于良, 杨银辉, 曹建春, 顾洋, 普靖
昆明理工大学 材料科学与工程学院, 昆明 650093
Effect of Mn on σ Phase and Toughness of 22%Cr Duplex Stainless Steel by Aging Treatment at 700℃
BAI Yu-liang, YANG Yin-hui, CAO Jian-chun, GU Yang, PU Jing
School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China
全文: PDF(5442 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 利用光学显微镜(OM)、X射线衍射仪(XRD)、扫描电镜(SEM)、透射电镜(TEM)结合析出动力学和冲击实验,研究了不同Mn含量(4.3%,6.9%,9.7%,质量分数,下同)对22%Cr节镍型双相不锈钢700℃时效析出相形成和韧性的影响。结果表明:随Mn含量由4.3%增加至9.7%,时效76h,析出形貌分别为铁素体/奥氏体(δ/γ)界面细小σ相颗粒析出和铁素体晶内σ相/二次奥氏体(γ2)共析组织。Mn含量增加使Avrami指数n减小,反应常数B增大,Mn元素参与并促进σ相析出,σ相开始析出和完全析出时间均提前,开始析出与完全析出的时间间隔增大,析出速率降低。时效过程中δ相分解量低于1%(体积分数,下同)对冲击韧度影响不大,δ相分解量由1%增至5%会显著降低冲击韧度。Mn含量增加在时效前期对冲击韧度有利,时效中期则会促使δ相分解量更早超过1%,导致冲击韧度快速下降。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
白于良
杨银辉
曹建春
顾洋
普靖
关键词 Mn含量时效σ析出动力学冲击韧度    
Abstract:The effect of different Mn contents on the σ phase and toughness of 22%Cr (mass fraction, the same below) low-nickel DSS by means of OM, XRD, SEM, TEM, precipitation kinetics and Charpy impact tests was studied. The results show that the morphology of precipitated phases changes from tiny granulated σ phase in δ/γ phase boundary to σ/γ2 eutectoid structure within δ phase with the addition of Mn from 4.3% to 9.7% and 76 hours aging. The increase of Mn content can decrease Avrami exponent n and increase reaction constant B, and the accelerating of σ-phase precipitation with higher Mn addition is due to the participation of Mn. Increasing Mn content can make initial time and ending time of σ-phase precipitation earlier and expand the interval between the initial time and ending time of σ-phase precipitation, that is, the more Mn addition, the earlier precipitation beginning time of σ-phase and the lower precipitation rate of it. The impact toughness is not sensitive to 1% transformation fraction of δ-ferrite, but it drops rapidly while the transformation fraction of δ-ferrite increases from 1% to 5%. More addition of Mn is good to impact toughness at the early stage of aging treatment, but the impact toughness decreases rapidly by accelerating the transformation fraction of δ-ferrite more than 1% earlier at the middle stage of aging time.
Key wordsMn content    aging treatment    σ phase    precipitation kinetics    impact toughness
收稿日期: 2016-09-22      出版日期: 2017-05-17
中图分类号:  TG142  
通讯作者: 杨银辉(1975-),男,副教授,博士,主要从事节镍型双相不锈钢方面研究,联系地址:云南省昆明市一二一大街文昌路68号昆明理工大学材料科学与工程学院(650093),E-mail:yyhyanr@sina.com     E-mail: yyhyanr@sina.com
引用本文:   
白于良, 杨银辉, 曹建春, 顾洋, 普靖. Mn对22%Cr双相不锈钢700℃时效σ相及韧性的影响[J]. 材料工程, 2017, 45(5): 71-79.
BAI Yu-liang, YANG Yin-hui, CAO Jian-chun, GU Yang, PU Jing. Effect of Mn on σ Phase and Toughness of 22%Cr Duplex Stainless Steel by Aging Treatment at 700℃. Journal of Materials Engineering, 2017, 45(5): 71-79.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.001134      或      http://jme.biam.ac.cn/CN/Y2017/V45/I5/71
[1] 王永强, 李娜, 杨滨, 等. 核电管道不锈钢中σ相的退火消除及脆性恢复[J]. 材料工程, 2016, 44(5): 29-36. WANG Y Q, LI N, YANG B, et al. Annealing induced removing of σ phase and recovery of embrittlement in stainless steel used for nuclear power plant pipes[J]. Journal of Materials Engineering, 2016, 44(5): 29-36.
[2] SARLAK H, ATAPOUR M, EAMAILZADEH M. Corrosion behavior of friction stir welded lean duplex stainless steel[J]. Materials & Design, 2015, 66(66): 209-216.
[3] WAN J Q, RAN Q X, LI J, et al.A new resource-saving, low chromium and low nickel duplex stainless steel 15Cr-xAl-2Ni-yMn[J]. Materials & Design, 2014, 53(1): 43-50.
[4] 雒设计, 郑新侠. 敏化处理对2205双相不锈钢组织与力学性能的影响[J]. 材料工程, 2011, (5): 76-80. LUO S J, ZHENG X X. Effects of sensitizing treatment on microstructure and mechanical properties of 2205 duplex stainless steel[J]. Journal of Materials Engineering, 2011, (5): 76-80.
[5] WESTIN E M, BROLUND B, HERTZMAN S. Weldability aspects of a newly developed duplex stainless steel LDX 2101[J].Steel Research International, 2008, 79(6): 473-481.
[6] TSENG C M, LION H Y, TSAI W T. The influence of nitrogen content on corrosion fatigue crack growth behavior of duplex stainless steel[J]. Materials Science and Engineering: A, 2003, 344(1-2): 190-200.
[7] LOTHONGKUM G, WONGPANYA P, MORITO S, et al. Effect of nitrogen on corrosion behavior of 28Cr-7Ni duplex and micro duplex stainlesss steels in air-saturated 3.5wt%NaCl solution[J]. Corrosion science, 2006, 48(1):137-153.
[8] PARDO A, MERINO M C, COY A E, et al.Effect of Mo and Mn additions on the corrosion behaviour of AISI 304 and 316 stainless steels in H2SO4[J]. Corrosion Science, 2008, 50(3): 780-794.
[9] CHOI J Y, JI J H, HWANG S W, PARK K T. TRIP aided deformation of a near-Ni-free, Mn-N bearing duplex stainless steel[J]. Materials Science and Engineering: A, 2011, 535(7): 32-39.
[10] EZUBER H M, EL-HOULD A, EL-SHAWESH F. Effects of sigma phase precipitation on seawater pitting of duplex stainless steel[J].Desalination, 2007, 207(1-3): 268.
[11] 吴玖. 双相不锈钢[M]. 北京: 冶金工业出版社, 1999. WU J. Duplex Stainless Steel[M]. Beijing: Metallurgy Industry Press, 1999.
[12] 向红亮,何福善,刘东. 时效温度对铸造超级双相不锈钢析出相的影响[J]. 金属学报, 2009, 45(12): 1456-1460. XIANG H L, HE F S, LIU D. Effects of aging temperature on precipitation phase of a cast super duplex stainless steel[J]. Acta Metallurgica Sinica, 2009, 45(12): 1456-1460.
[13] 罗照银,李静媛. S32760超级双相不锈钢中σ相的析出规律[J]. 材料热处理学报,2015, 36(4): 110-115. LUO Z Y, LI J Y. Precipitation behavior of σ phase in UNS S32760 super duplex stainless steel[J]. Transactions of Materials and Heat Treatment, 2015, 36(4): 110-115.
[14] HUANG C S, SHIH C C. Effects of nitrogen and high temperature aging on sigma phase precipitation of duplex stainless steel[J]. Materials Science and Engineering: A, 2005, 402(1-2): 66-75.
[15] BADJI R, KHERROUBA N, MEHDI B,et al. Precipitation kinetics and mechanical behavior in a solution treated and aged dual phase stainless steel[J].Materials Chemistry and Physics, 2014, 148(3): 664-672.
[16] MARTINS M, NOQUEIRA FORTIB L R. Effect of aging on impact properties of ASTM A890 Grade 1C super duplex stainless steel[J].Materials Characterization, 2008, 59(2): 162-166.
[17] MOURA VS, LIMA LD, PARDAL JM, et al. Influence of microstructure on the corrosion resistance of the duplex stainless steel UNSS31803[J].Materials Characterization, 2008, 59(8): 1127-1132.
[18] ZHANG W, JIANG L Z, HU J C, et al. Effect of ageing on precipitation and impact energy of 2101 economical duplex stainless steel[J].Materials Characterization, 2009, 60(1): 50-55.
[19] LI J, XU Y L, XIAO X S, et al.A new resource-saving, high manganese and nitrogen super duplex stainless steel 25Cr-2Ni-3Mo-xMn-N[J].Materials Science and Engineering: A, 2009, 527(1): 245-251.
[20] HSIEH C C, LIN D Y, WU W T. Precipitation behavior of sigma phase in 19Cr-9Ni-2Mn and 18Cr-0.75Si stainless steels hot-rolled at 800 degrees C with various reduction ratios[J].Materials Science and Engineering: A, 2007, 467(1-2): 181-189.
[21] 雍岐龙.钢铁材料中的第二相[M].北京: 冶金工业出版社, 2006. 303. YONG Q L. Secondary Phases in Steels[M]. Beijing: Metallurgy Industry Press, 2006. 303.
[22] YANG Y H, CAO J C, GU Y. Investigation on the solution treated behavior of economical 19Cr duplex stainless steels by Mn addition[J].Materials & Design, 2015, 83: 820-828.
[23] JANG Y H, KIM S S, LEE J H. Effect of different Mn contents on tensile and corrosion behavior of CD4MCU cast duplex stainless steels[J]. Materials Science and Engineering: A, 2005, 396(1-2): 302-310.
[24] LEE K M, CHO H S, CHOI D C. Effect of isothermal treatment of SAF 2205 duplex stainless steel on migration of delta/gamma interface boundary and growth of austenite[J].Journal of Alloys and Compounds, 1999, 285(1-2): 156-161.
[25] LO H K, LAI J K L, SHEK C H, et al. Effects of pre-treatment on the ac magnetic susceptibility and ageing behaviour of duplex stainless steels[J]. Materials Science and Engineering: A, 2007, 452: 78-86.
[26] MOMENI A, DEHGHANI K. Effect of hot working on secondary phase formation in 2205 duplex stainless steel[J]. Journal of Materials Science & Technology, 2010, 26(9): 851-857.
[27] KASHIWAR A, PHANI VENNELA N, KAMATH S L, et al. Effect of solution annealing temperature on precipitation in 2205 duplex stainless steel[J]. Materials Characterization, 2012, 74(4): 55-63.
[28] LARA N O, RUIZ A, RUBIO C, et al.Nondestructive assessing of the aging effects in 2205 duplex stainless steel using thermoelectric power[J].NDT&E International, 2011, 44(5): 463-468.
[29] ELMER J W, PALMER T A, SPECHT E D. Direct observations of sigma phase formation in duplex stainless steels using in-situ synchrotron X-ray diffraction[J].Metallurgical and Materials Transactions A, 2007, 38(3):464-475.
[30] YAMAMOTO Y, SANTELLA M L, LIU C T, et al. Evaluation of Mn substitution for Ni in alumina-forming austenitic stainless steels[J]. Materials Science and Engineering: A, 2009,524(1-2): 176-185.
[31] AHN Y S, KANG J P. Effect of aging treatments on microstructure and impact properties of tungsten substituted 2205 duplex stainless steel[J].Materials Science and Technology, 2000, 16(4): 382-388.
[1] 党莹樱, 赵新宝, 尹宏飞, 鲁金涛, 袁勇, 杨珍, 谷月峰. Inconel 740H合金750℃长期时效后的组织稳定性[J]. 材料工程, 2016, 44(9): 58-62.
[2] 任魏巍, 邹林池, 张兴峰, 符殿宝, 陈俊锋. 7050铝合金时效成形中应力松弛行为与回弹方程[J]. 材料工程, 2016, 44(9): 89-95.
[3] 乔瑞芳, 毕洪运, 陈玉喜. Ti,Nb和W复合强化超纯铁素体不锈钢的高温析出行为[J]. 材料工程, 2016, 44(5): 22-28.
[4] 谢孝昌, 李旭东, 汤春峰, 付书红. 直接时效对GH4169合金应力集中敏感性的影响[J]. 材料工程, 2016, 44(2): 88-93.
[5] 杨守杰, 邢清源, 于海军, 王玉灵, 臧金鑫, 戴圣龙. 一种新型高锌Al-Zn-Mg-Cu合金的热处理工艺[J]. 材料工程, 2016, 44(12): 41-47.
[6] 马娅娜, 杜林秀, 胡军. Mn含量对热轧超低碳钛低合金钢组织与力学性能的影响[J]. 材料工程, 2015, 43(9): 1-5.
[7] 何正林, 高文理, 陆政, 冯朝辉. 热处理对7A85铝合金组织和性能的影响[J]. 材料工程, 2015, 43(8): 13-18.
[8] 冯柳, 周邦新, 彭剑超, 王均安. RPV模拟钢中纳米富Cu析出相的复杂晶体结构表征[J]. 材料工程, 2015, 43(7): 80-86.
[9] 杨海青, 李青, 肖程波, 胡聘聘, 林山峰. Re及时效时间对耐腐蚀镍基定向合金组织和持久寿命的影响[J]. 材料工程, 2015, 43(6): 31-37.
[10] 辛星, 张新明, 刘胜胆, 宋丰轩, 陈彬. 回归再时效中预时效温度对7050铝合金应力腐蚀性能的影响[J]. 材料工程, 2014, 0(5): 29-34.
[11] 胡春燕, 刘新灵, 陶春虎. 时效温度对0Cr17Ni4Cu4Nb钢组织及力学性能的影响[J]. 材料工程, 2014, 0(11): 73-78.
[12] 黄本生, 刘阁, 黄龙鹏, 刘辉, 张怀辉. 不同焊材匹配与时效处理对异种钢焊接接头显微结构与力学性能的影响[J]. 材料工程, 2013, (8): 75-84.
[13] 杨林, 黄婷, 林立, 刘正. 室温压缩AZ91镁合金显微组织及β-Mg17Al12相析出动力学[J]. 材料工程, 2012, 0(4): 68-71.
[14] 赵秀明, 杨金峰, 张永健, 惠卫军, 于同仁, 王章忠. 贝氏体型冷作强化非调质钢的氢致延迟断裂行为[J]. 材料工程, 2012, 0(3): 47-51.
[15] 甄睿, 孙扬善, 王章忠, 方信贤, 石卫. 热处理对GWZ661变形镁合金组织与性能的影响[J]. 材料工程, 2012, 0(12): 39-44.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn