小角度晶界对DD5镍基单晶高温合金中、高温条件下力学性能的影响
秦健朝, 崔仁杰, 黄朝晖
中国航发北京航空材料研究院 先进高温结构材料重点实验室, 北京 100095
Effect of low angle grain boundaries on mechanical properties of DD5 single crystal Ni-base superalloy at medium temperature and high temperature
QIN Jian-chao, CUI Ren-jie, HUANG Zhao-hui
Key Laboratory of Advanced High Temperature Structural Materials, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
全文: PDF(5476 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 采用双籽晶制备第二代镍基单晶高温合金DD5合金双晶试板并加工成力学试样,研究小角度晶界对DD5合金中、高温条件下拉伸、持久性能的影响。结果表明:在760℃拉伸条件下,晶界角度小于14.8°时,试样抗拉强度大于1100 MPa,伸长率大于8%,断面收缩率大于14%,晶界角度大于14.8°后,抗拉强度、伸长率以及断面收缩率随着晶界角度的增大而下降,屈服强度则没有显著变化;在980℃拉伸中,晶界角度小于19.4°时,试样抗拉强度大于760 MPa,屈服强度大于630 MPa,伸长率以及断面收缩率则随晶界角度的增大而快速下降,至19.4°时,伸长率下降至1.4%,断面收缩率下降至2.8%;在870℃/551 MPa持久条件下,当晶界角度小于7.8°时,试样持久寿命大于110 h,伸长率大于19.8%,断面收缩率大于23.1%,当晶界角度大于7.8°后,试样持久寿命、伸长率以及断面收缩率随晶界角度的增大而快速下降。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
秦健朝
崔仁杰
黄朝晖
关键词 高温合金小角度晶界持久寿命拉伸性能    
Abstract:The effects of low angle grain boundaries on the tensile properties and stress rupture properties of second generation single crystal superalloy DD5 at medium temperature and high temperature were investigated. The test plates were prepared by using seeds and processed into mechanical samples. The results show that the tensile strength at 760 ℃ is higher than 1100 MPa, the elongation is higher than 8% and the percentage reduction of area is higher than 14% when the angle is below 14.8°. The tensile strength, elongation and percentage reduction of area are decreased when the angle is above 14.8°. But the yield strength shows no difference. The tensile strength at 980 ℃ is higher than 760 MPa, the yield strength is higher than 630 MPa, the elongation and percentage reduction of area are decreased quickly when the angle is below 19.4°. The elongation is 1.4%, the percentage reduction of area is 2.8% when the angle is 19.4°. The rupture life at 870 ℃/551 MPa is higher than 110 h, the elongation is higher than 19.8% and the percentage reduction of area is higher than 23.1% when the angle is below 7.8°.But they are decreased quickly when the angle is above 7.8°.
Key wordssuperalloy    low angle grain boundary    rupture life    tensile property
收稿日期: 2020-01-02      出版日期: 2020-10-17
中图分类号:  TG292  
通讯作者: 黄朝晖(1968-),女,研究员,博士,现从事单晶高温合金的研究工作,联系地址:北京市海淀区环山村8号北京航空材料研究院(100095),E-mail:huangzhaohui621@163.com     E-mail: huangzhaohui621@163.com
引用本文:   
秦健朝, 崔仁杰, 黄朝晖. 小角度晶界对DD5镍基单晶高温合金中、高温条件下力学性能的影响[J]. 材料工程, 2020, 48(10): 114-122.
QIN Jian-chao, CUI Ren-jie, HUANG Zhao-hui. Effect of low angle grain boundaries on mechanical properties of DD5 single crystal Ni-base superalloy at medium temperature and high temperature. Journal of Materials Engineering, 2020, 48(10): 114-122.
链接本文:  
http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2020.000002      或      http://jme.biam.ac.cn/CN/Y2020/V48/I10/114
[1] GELL M, DUHL D N, GIAMEI A F. The development of single crystal superalloy turbine blades[C]//Superalloys 1980. Metals Park, OH:American Society for Metals, 1980:205-214.
[2] BROOMFIELD R W, FORD D A, BHANGU J K, et al. Development and turbine engine performance of three advanced rhenium containing superalloys for single crystal and directionally solidified blades and vanes[J]. Transactions of the ASME, 1998,120(3):596-608.
[3] WALSTON W S, O'HARA K S, ROSS E W, et al. ReneN6:Third generation single crystal superalloy[C]//Superalloys 1996. Warrendale, PA:TMS, 1996:27-34.
[4] HARRIS K, ERICHSON G L. Development of the rhenium containing superalloys CMSX-4& CM186LC for single crystal blade and directionally solidified vane applications in advanced turbine engines[C]//Superalloys 1992. Warrendale, PA:TMS, 1992:297-306.
[5] HARRIS K, WAHL J B. Improved single crystal superalloys CMSX-4(SLS)[La+Y] and CMSX-486[C]//Superalloys 2004. Warrendale, PA:TMS, 2004:45-52.
[6] 陈荣章,王罗宝,李建华. 铸造高温合金发展的回顾与展望[J]. 航空材料学报,2000,20(1):55-61. CHEN R Z, WANG L B, LI J H. Review and prospect on developments of cast superalloys[J]. Journal of Aeronautical Materials,2000, 20(1):55-61.
[7] KOIZUMI Y, KOBAYASHI T, YOKOKAWA T, et al. Development of next-generation Ni-base single crystal superalloy[C]//Superalloys 2004. Warrendale, PA:TMS, 2004:35-43.
[8] POLLOCK T M, MURPHY W H, GOLDMAN E H, et al. Grain defect formation during directional solidification of nickel base single crystals[C]//Superalloys 1992. Warrendale, PA:TMS, 1992:125-134.
[9] CHEN Q Z, JONES N, KNOWLES D M. The grain boundary microstructures of the base and modified RR2072 bicrystal superalloys and their effects on the creep properties[J]. Materials Science and Engineering, 2004,385(1/2):402-418.
[10] ROSS E W, O'HARA K S. Rene N4:a first generation single crystal turbine airfoil alloy with improved oxidation resistance, low angle boundary strength and superior long time rupture strength[C]//Superalloys 1996. Warrendale, PA:TMS, 1996:19-25.
[11] 史振学,李嘉荣,刘世忠,等. DD6单晶高温合金扭转小角度晶界的拉伸性能[J].航空材料学报, 2009,29(3):88-92. SHI Z X, LI J R, LIU S Z, et al. Tensile properties of twist low angle boundary DD6 of single crystal superalloy[J]. Journal of Aeronautical Materials, 2009,29(3):88-92.
[12] 赵金乾,李嘉荣,刘世忠,等.小角度晶界对单晶高温合金DD6拉伸性能的影响[J]. 材料工程, 2008(8):73-76. ZHAO J Q, LI J R, LIU S Z, et al. Effects of low angle grain boundaries on tensile properties of single crystal superalloy DD6[J]. Journal of Materials Engineering, 2008(8):73-76.
[13] CUI R J, HUANG Z H. Microstructural evolution and stability of second generation single crystal nickel-based superalloy DD5[J]. Transactions of Nonferrous Metals Society of China,2016,26(8):2079-2085.
[14] 崔仁杰,黄朝晖,张毅鹏,等.980℃长期时效对第二代镍基单晶高温合金DD5组织与性能的影响[J].材料热处理学报,2016,37(6):78-83. CUI R J, HUANG Z H, ZHANG Y P, et al. Effect of 980℃ long-term aging on microstructure and properties of DD5 single crystal Ni-base superalloys[J]. Transactions of Materials and Heat Treatment, 2016,37(6):78-83.
[15] 曹亮,周亦胄,金涛,等. 晶界角度对一种镍基双晶高温合金持久性能的影响[J]. 金属学报, 2014,50(1):11-18. CAO L, ZHOU Y Z, JIN T, et al. Effect of grain boundary angle on stress rupture properties of a Ni-based crystal superalloy[J]. Acta Metallurgica Sinica, 2014,50(1):11-18.
[16] 秦健朝,崔仁杰,黄朝晖,等.小角度晶界对DD5镍基单晶高温合金力学性能的影响[J]. 航空材料学报, 2017,37(3):24-29. QIN J C, CUI R J, HUANG Z H, et al. Effect of low angle grain boundaries on mechanical properties of DD5 single crystal Ni-base superalloy[J]. Journal of Aeronautical Materials, 2017,37(3):24-29.
[17] 刘志义,雷毅,傅恒志. DD8镍基高温合金单晶制备中的杂晶长大机制[J].金属学报, 2000,36(1):1-6. LIU Z Y, LEI Y, FU H Z. A study on mechanism of misoriented grain growth in single-crystal manufacture of DD8 nickel based superalloy[J].Acta Metallurgica Sinica,2000,36(1):1-6.
[18] 周亦胄,金涛,孙晓峰.双晶镍基高温合金定向凝固过程的结构演化[J].金属学报, 2010,46(11):1327-1334. ZHOU Y Z, JIN T, SUN X F. Structure evolution in directionally solidified bicrystals of nickel base superalloy[J]. Acta Metallurgica Sinica, 2010,46(11):1327-1334.
[19] GOLDSCHMIDT D, PAUL U, SAHM P R. Porosity clusters and recrystallization in single-crystal components[C]//Superalloys 1992. Warrendale, PA:TMS, 1992:155-164.
[20] LIU L R, JIN T, ZHAO N R, et al. Microstructural evolution of a single crystal nickel-base superalloy during thermal exposure[J]. Materials Letters, 2003,57(29):4540-4546.
[21] CHEN Q Z, KONG Y H, JONES C N, et al. Porosity reduction by minor additions in RR2086 superalloy[J]. Scripta Materialia, 2004,51(2):155-160.
[1] 李慧中, 杨雷, 王岩, 谭钢, 黄钲钦, 刘敏学. 热挤压态Ni-Co-Cr基粉末高温合金热加工行为[J]. 材料工程, 2020, 48(9): 115-123.
[2] 曲敬龙, 易出山, 陈竞炜, 史玉亭, 毕中南, 杜金辉. GH4720Li合金中析出相的研究进展[J]. 材料工程, 2020, 48(8): 73-83.
[3] 王彦菊, 姜嘉赢, 沙爱学, 李兴无. 新型高温合金材料建模及涡轮盘成形工艺模拟[J]. 材料工程, 2020, 48(7): 127-132.
[4] 杨万鹏, 李嘉荣, 刘世忠, 赵金乾, 史振学, 王效光. 一种第三代单晶高温合金中高温横向持久性能[J]. 材料工程, 2020, 48(7): 139-145.
[5] 石磊, 雷力明, 王威, 付鑫, 张广平. 热等静压/热处理工艺对激光选区熔化成形GH4169合金微观组织与拉伸性能的影响[J]. 材料工程, 2020, 48(6): 148-155.
[6] 王旭青, 彭子超, 罗学军, 马国君, 武丹. 时效制度对挤压+锻造工艺路线FGH95粉末高温合金组织和性能的影响[J]. 材料工程, 2020, 48(5): 120-126.
[7] 刘成, 彭志方, 彭芳芳, 陈方玉, 刘省. P92钢625℃持久实验过程中试件特征部位相参量的变化[J]. 材料工程, 2020, 48(3): 98-104.
[8] 刘也川, 张松, 谭俊哲, 关锰, 陶邵佳, 张春华. 机械滚压对A473M钢疲劳性能的影响[J]. 材料工程, 2020, 48(3): 163-169.
[9] 齐业雄, 姜亚明, 李嘉禄. 混杂比对碳/芳纶纤维混杂纬编双轴向多层衬纱织物增强复合材料力学性能的影响[J]. 材料工程, 2020, 48(2): 71-78.
[10] 黄敏, 张功, 王栋, 李辉, 董加胜, 楼琅洪. 复杂镍基单晶铸件显微孔洞的形成机理[J]. 材料工程, 2020, 48(2): 123-132.
[11] 董建民, 李嘉荣, 韩梅. 检验腐蚀对镍基单晶高温合金高周疲劳性能的影响[J]. 材料工程, 2020, 48(1): 77-83.
[12] 刘承林, 苏海军, 张军, 刘林, 傅恒志. 静磁场对定向凝固镍基高温合金组织影响的研究进展[J]. 材料工程, 2019, 47(9): 13-20.
[13] 韩梅, 喻健, 李嘉荣, 谢洪吉, 董建民, 杨岩. 喷丸对DD6单晶高温合金拉伸性能的影响[J]. 材料工程, 2019, 47(8): 169-175.
[14] 罗亮, 肖程波, 陈晶阳, 李青, 戴圣龙. 工业燃气轮机涡轮叶片用铸造高温合金研究及应用进展[J]. 材料工程, 2019, 47(6): 34-41.
[15] 韩梅, 谢洪吉, 李嘉荣, 董建民, 岳晓岱, 喻健, 杨亮. 再结晶对DD6单晶高温合金轴向高周疲劳性能的影响[J]. 材料工程, 2019, 47(6): 161-168.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn