Abstract：The metallographic structures of Al-Mn eutectic alloy and its composite were investigated by XRD and SEM. The mass loss, friction coefficient and wear trace of the samples were studied under three different kinds of friction conditions. And their properties of erosion resistance were analyzed by SEM and EDS. The results show that the shapes of brittle Al-Mn compounds are changed as Al2O3 particle is added. The mass loss and friction coefficient of the samples under corrosive liquid and abrasive condition are less than those under corrosive liquid condition, but higher than those under dry sliding condition. The pits of samples under corrosive liquid condition are more than those under corrosive liquid and abrasive condition, and the furrows of samples under corrosive liquid and abrasive condition are deeper than those under dry sliding condition by observing wear traces. As the particle size of abrasive increases, wear rates of erosion samples increase first and then decrease in 7m/s erosion speed, but decrease gradually in 3.5m/s. In addition, the mass of Al-Mn eutectic alloy samples increase after the erosion test under the 3.5m/s erosion speed and 0.15-0.212mm particle size condition.
[1] 樊自立,王喜鹏.新疆平原湖泊(包括人工湖)水质盐化及其防治途径[J].自然资源学报,1990,5(4):311-314.FAN Zi-li, WANG Xi-peng. Water salinization of plain lakes(including man-made lakes) and its prevention and control in Xinjiang[J]. Journal of Natural Resources, 1990, 5(4): 311-314.[2] 王永红,鹿中晖,李英志.西部内陆盐土中铜、铝的腐蚀行为[J].中国腐蚀与防护学报,2005,25(5):303-306.WANG Yong-hong, LU Zhong-hui, LI Ying-zhi. Corrosion behavior of Cu and Al in western inland salty soil[J]. Journal of Chinese Society for Corrosion and Protection, 2005, 25(5): 303-306.[3] 路贵民,王兆文,李冰.铝合金腐蚀与表面处理[M].沈阳:东北大学出版社,2000.[4] HAJIZAMANI M, BAHARVANDI H. Fabrication and studying the mechanical properties of A356 alloy reinforced with Al2O3-10% Vol. ZrO2 nanoparticles through stir casting[J]. Advances in Materials Physics and Chemistry, 2011,(1): 26-30.[5] SHOROWORDI K M, LAOUI T, HASEEB A S M A, et al. Microstructure and interface characteristics of B4C, SiC and Al2O3 reinforced Al matrix composites: a comparative study[J]. Journal of Materials Processing Technology, 2003, 142(3): 738-743.[6] DAOUD A, ABO-ELKHAR M. Influence of Al2O3 or ZrO2 particulate addition on the microstructure aspects of AlNi and AlSi alloys[J]. Journal of Materials Processing Technology, 2002, 120(1-3): 296-302.[7] 李广钦,左秀荣.铸态及均匀化处理3003铝锰合金的组织与性能[J].材料热处理学报,2007,28(3):63-66.LI Guang-qin, ZUO Xiu-rong. Research on microstructure and mechanical properties of as-cast and homogenized 3003 aluminum-manganese alloy[J]. Transactions of Materials and Heat Treatment, 2007, 28(3): 63-66.[8] 郑喜玉,刘建华.新疆盐湖卤水成分及其成因[J].地理科学,1996,16(2):115-124.ZHENG Xi-yu, LIU Jian-hua. The composition and origin of salt lake brines in Xinjiang[J]. Scientia Geographica Sinica, 1996, 16(2): 115-124.[9] 高义民.金属凝固原理[M].西安:西安交通大学出版社,2010.[10] 王吉会,姜晓霞,李曙,等.腐蚀磨损过程中材料的环境脆性[J].材料研究学报,2003,17(5):449-458. WANG Ji-hui, JIANG Xiao-xia, LI Shu, et al. Environment embrittlement of materials in corrosive wear[J]. Chinese Journal of Materials Research, 2003, 17(5): 449-458.[11] JIANG J, STACK M M, NEVILLE A. Modelling the tribo-corrosion interaction in aqueous sliding conditions[J]. Tribology International, 2002, 35(10): 669-679.[12] TAO S, LI D Y. Investigation of corrosion-wear synergy attack on nanocrystalline Cu deposits[J]. Wear, 2007, 263(1-6): 363-370.[13] BINGLEY M S, SCHNEE S. A study of the mechanisms of abrasive wear for ductile metals under wet and dry three-body conditions [J]. Wear, 2005, 258(1-4): 50-61.[14] 布尚.摩擦学导论[M].葛世荣.北京:机械工业出版社,2006.[15] SZKLARSKA-SMIALOWSKA Z. Pitting corrosion of aluminum[J]. Corrosion Science, 1999, 41(9): 1743-1767.[16] 陈平昌,朱六妹,李赞.材料成形原理[M].北京:机械工业出版社,2001.
2013, Vol. 0 