约束条件下天然橡胶硫化胶疲劳现象分析
袁远, 栗付平, 孙霞容
北京航空材料研究院, 北京 100095
Analysis on Fatigue Behavior of Vulcanized Natural Rubber Under Constrained Condition
YUAN Yuan, LI Fu-ping, SUN Xia-rong
Beijing Institute of Aeronautical Materials, Beijing 100095, China
全文: PDF(2184 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 通过凝胶色谱分析、衰减全反射傅里叶红外光谱分析及气相色谱-质谱联用分析等手段,对天然橡胶硫化胶在约束条件下剪切疲劳的产物进行了研究。结果表明,在一维受压状态下,剪切疲劳过程中橡胶分子链首先主要发生力断裂现象,进而发生氧老化作用,同时疲劳过程中部分低分子量降解产物和游离态填料会向应力集中的部位迁移集聚。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
关键词 天然橡胶剪切疲劳疲劳    
Abstract:The shear fatigue behavior of vulcanized natural rubber (NR) under constrained condition was investigated by Gel Permeation Chromatography(GPC), Attentuated Total Reflectance-Fourier Transform InfraRed(ATR-FTIR) spectroscopy, and Gas Chromatography-Mass Spectrometry(GC-MS). The results showed that in the shear fatigue process molecular chains were first broken under one-dimensional compression load, and then oxygen aging occurred.At the same time, some of the low-molecular mass degradation products and free state fillers migrated and agglomerated at the stress concentration regions.
Key wordsnatural rubber    shear fatigue    fatigue
收稿日期: 2012-03-27      出版日期: 2013-07-20
中图分类号: 

TQ330.1+4

 
作者简介: 袁远(1985—),女,硕士,研究方向为高分子材料专业,联系地址:北京81信箱70分箱(100095),E-mail:yyfanfan85@126.com
引用本文:   
袁远, 栗付平, 孙霞容. 约束条件下天然橡胶硫化胶疲劳现象分析[J]. 材料工程, 2013, 0(7): 40-43,49.
YUAN Yuan, LI Fu-ping, SUN Xia-rong. Analysis on Fatigue Behavior of Vulcanized Natural Rubber Under Constrained Condition. Journal of Materials Engineering, 2013, 0(7): 40-43,49.
链接本文:  
http://jme.biam.ac.cn/CN/10.3969/j.issn.1001-4381.2013.07.008      或      http://jme.biam.ac.cn/CN/Y2013/V0/I7/40
[1] BARTENEV G M, GALIL-OGLY F A. Dynamic fatigue of rubber and the mechanism of failure by reported deformation[J].Rubber Chemistry and Technology, 1956, 29(2):504-508.

[2] WANG B, LU H B, KIM G A damage model for fatigue life of elastomeric materials[J]. Mechanics of Materials, 2002, 34:475-483.

[3] BHOWMICK A K. Fractographic investigation of tensile and fatigue fracture surfaces of rubber containing inhomogeneous inclusions[J]. Journal of Materials Science Letters, 1986,(5):1042-1044.

[4] 徐世清. 飞机用橡胶软管爆破失效的形貌特征及原因分析[J].航空工艺技术,1997,(1):33-35.

[5] THAVAMANI P, KHASTGIR D, BHOWMICK AK. Microscopic studies on the mechanisms of wear of NR, SBR and HNBR vulcanizates under different conditions[J]. Journal of Materials Science,1993, 28:6318-6322.

[6] 谷辛亥. 交联体系对疲劳寿命的影响[J].世界橡胶工艺,1999,26(1):8-10.

[7] KIM J H, JEONG H Y. A study on the material properties and fatigue life of natural rubber with different carbon blacks[J]. International Journal of Fatigue,2005,27:263-272.

[8] 肖建斌,郭红革.炭黑/白炭黑补强硫化胶的疲劳过程及使用寿命预测[J].世界橡胶工业,2006,(1):29-32.

[9] ISAYEV A I, DENG J S. Non-isothermal vulcanization of rubber compounds[J]. Rubber Chemistry and Technology, 1988, 61(2):340-381.

[10] 藤本邦彦,西敏夫.分析技术的进展橡胶的分析—结构与物性[J].日本橡胶协会志,1965,38:843.

[11] 张士齐.用现代物理表征技术研究高聚物的力化学反应[J].合成橡胶工业,1995,18(5):257-259.

[12] 张士齐,黄爱华.用电子自旋共振研究硫化橡胶疲劳历程[J].橡胶工业,1991,38(12):739-742.

[13] GENT A N. Rubber elasticity:basic concepts and behavior[J].Journal of Applied Polymer Science, 1962,6:497.

[14] KUZUMINSKII A S. Fatigue of rubber [J].Rubber Chemistry and Technology,1955,28:429.

[15] 范耀华,王光埙, 邓春森.溶剂手册[M].2版.北京:中国石化出版社,2002.56.
[1] 王欣, 许春玲, 李臻熙, 裴传虎, 汤智慧. 喷丸强度和表面覆盖率对TC4钛合金室温疲劳性能的影响[J]. 材料工程, 2020, 48(9): 138-143.
[2] 王欣, 陈星, 胡仁高, 胡博, 许春玲, 汤智慧, 古远兴. 冷挤压GH4169合金孔结构疲劳性能与断口分析[J]. 材料工程, 2020, 48(6): 156-162.
[3] 王志远, 邢志国, 王海斗, 单德彬. 非金属夹杂物特性对钢铁材料疲劳性能影响的研究进展[J]. 材料工程, 2020, 48(5): 1-12.
[4] 赵慧生, 陈国清, 盖鹏涛, 李志强, 周文龙, 付雪松. 拉-拉疲劳载荷下钛合金湿喷丸的残余应力松弛及再次喷丸工艺[J]. 材料工程, 2020, 48(5): 136-143.
[5] 刘也川, 张松, 谭俊哲, 关锰, 陶邵佳, 张春华. 机械滚压对A473M钢疲劳性能的影响[J]. 材料工程, 2020, 48(3): 163-169.
[6] 董建民, 李嘉荣, 韩梅. 检验腐蚀对镍基单晶高温合金高周疲劳性能的影响[J]. 材料工程, 2020, 48(1): 77-83.
[7] 刘凯, 崔荣洪, 侯波, 何宇廷, 牛欢. PVD薄膜传感器裂纹检测概率测定与分析[J]. 材料工程, 2019, 47(9): 160-166.
[8] 刘石双, 仇平, 蔡建明, 李娟, 黄旭, 于辉, 刘利刚. Ti60钛合金室温保载疲劳性能及断裂行为[J]. 材料工程, 2019, 47(7): 112-120.
[9] 郭军, 杨卯生, 卢德宏, 李新宇. Cr4Mo4V轴承钢旋转弯曲疲劳寿命及疲劳裂纹萌生机理[J]. 材料工程, 2019, 47(7): 134-143.
[10] 韩梅, 谢洪吉, 李嘉荣, 董建民, 岳晓岱, 喻健, 杨亮. 再结晶对DD6单晶高温合金轴向高周疲劳性能的影响[J]. 材料工程, 2019, 47(6): 161-168.
[11] 张先炼, 何晓聪, 邢保英, 曾凯. TA1纯钛与1420铝锂合金异质薄板自冲铆接微动疲劳特性[J]. 材料工程, 2019, 47(4): 143-151.
[12] 周航, 张峥. AlSi10Mg(Cu)铸铝合金的热疲劳裂纹萌生及早期扩展行为[J]. 材料工程, 2019, 47(3): 131-138.
[13] 山泉, 张亚峰, 张哲轩, 李祖来, 蒋业华, 王鹏飞. 钨含量对WCP/钢基表层复合材料压缩性能及热疲劳行为的影响[J]. 材料工程, 2019, 47(2): 115-121.
[14] 赵玲, 刘光磊, 张思源, 李茂军, 刘简宁, 李明辉. 固溶时效深冷复合处理对ZCuAl10Fe3Mn2合金微观组织和热疲劳性能的影响[J]. 材料工程, 2019, 47(12): 63-70.
[15] 许良, 黄双君, 回丽, 王磊, 周松, 赵晴. TB6钛合金疲劳小裂纹扩展行为[J]. 材料工程, 2019, 47(11): 171-177.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn