1 College of Material and Mineral Resources, Xi'an University of Architecture and Technology, Xi'an 710055, China 2 School of Mechanical and Electrical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China
The friction and wear characteristics of Fe-0.03Te-0.3Pb-0.9Mn free-cutting stainless steel were investigated using a lubricated rolling wear testing apparatus. The wear morphology, hardness, friction coefficient and wear volume of alloy surface were compared in different wear time, its mechanism of lubricated rolling wear was studied further. The results show that, at the beginning of wear, the performance of alloy surface wear is relatively stable, under the interaction of free-cutting phase, such as MnS and Pb, that cracks occur at the alloy surface plough bottom; When the wear is stable, the performance of alloy surface changed gradually, the cracks of plough bottom continue growing, interweaved cracks begin to generate flake or block convex parts; When the wear is over, the alloy surface lubrication film and exfoliation numerous are flaking off, exfoliation formed abrasive wear, plough disappeared step by step, the alloy surface system is collapsed rapidly.
LOU D, CUI K, JIA Y Study on the machinability of resulfurized composite free-cutting steels[J]. Journal of Materials Engineering and Performance, 1997, 6 (2): 215- 218.
2
IWAMOTO T, MURAKAMI T Bar and wire steels for gears and valves of automobiles-eco-friendly free cutting steel without lead addition[J]. JFE GIHO, 2004, (4): 64- 69.
XIAO L R, ZHANG L H, SHU X P, et al Research of rolling technique of unleaded brass containing stibium[J]. Journal of Materials Engineering, 2009, (1): 288- 292.
4
WU D, LI Z A new Pb-free machinable austenitic stainless steel[J]. Journal of Iron and Steel Research, International, 2010, 17 (1): 59- 63.
WANG X, YIN S C, HE L, et al The cleanliness and modification behavior of nonmetallic inclusions in 0[J]. 05C-0.3Si- 2.0Mn-xCe molten steel[J]. Journal of Materials Engineering, 2013, (3): 42- 50.
6
LI Y, SUZUKI T, TANG N, et al Microstructure evolution of SUS303 free-cutting steel during hot compression process[J]. Materials Science and Engineering: A, 2013, 583 (7): 161- 168.
WANG Z, WANG F Z, WANG X, et al Three-dimensional modelling of numerical simulation on segregation during Fe-Pb alloy solidification in a multiphase system[J]. Acta Physica Sinica, 2014, 63 (7): 1011- 10115.
WANG Z, WANG F Z, HE Y H, et al Numerical study on free-cutting phase precipitation behavior in Fe-Bi-Mn ternary alloy multiphase transformation-diffusion system[J]. Acta Metallurgica Sinica, 2014, :50 (11): 1393- 1402.
9
NAZABAL J L, URCOLA J J, FUENTES M Hot ductility of leaded free-cutting steels[J]. Metallography, 1984, 17 (4): 439- 453.
10
MURAKAMI Y, MINE K, USUKI H Fatigue strength of annealed 0[J]. 45% carbon leaded-free-cutting steel[J]. Tetsuto Hagane, 1988, 74 (6): 1113- 1118.
11
BERNSMANN G, BLEYMEHL M, EHL R, et al The making of free cutting steels with additions of lead, bismuth, tellurium, selenium and tin[J]. Stahl und Eisen, 2001, 121 (2): 87- 91.
12
KOUMOTO T, NISHI T, MORI M, et al Development of non-lead-added free-cutting steel for automobile parts[J]. SAE Technical, 2004, 42 (1): 1527- 1538.
13
GUDURU R K, SCATTERGOOD R O, KOCH C C, et al Mechanical properties of nanocrystalline Fe-Pb and Fe-Al2O3[J]. Scripta Materialia, 2006, 54 (11): 1879- 1883.
14
ZHU M, GAO Y, CHUNG C Y, et al Improvement of the wear behaviour of Al-Pb alloys by mechanical alloying[J]. Wear, 2000, 242 (1): 47- 53.
15
POURASIABI H M D, SAGHAFIAN H, POURASIABI H Effect of austempering process on microstructure and wear behavior of ductile iron containing Mn-Ni-Cu-Mo[J]. Metals and Materials International, 2013, 19 (1): 67- 76.
WANG Z S, GUO J T, ZHOU L Z, et al High temperature wear behavior of NiAl-Cr(Mo)-Ho-Hf eutectic alloy[J]. Acta Metallurgica Sinica, 2009, 45 (3): 297- 301.
YANG J H, ZHANG Y Z, QIU M, et al Wearing characteristic of Ti6Al4V in high dry sliding friction[J]. Journal of Materials Engineering, 2006, (1): 35- 38.