材料工程  2014, Vol. 0 Issue (7): 1-4    DOI: 10.11868/j.issn.1001-4381.2014.07.001
  材料与工艺 本期目录 | 过刊浏览 | 高级检索 |
新型复合挤压工艺中温度对AZ61组织和性能的影响
张丁非1,2, 耿青梅1, 杨绪盛1, 余大亮1, 潘复生1,2
1. 重庆大学 材料科学与工程学院, 重庆 400045;
2. 国家镁合金材料工程技术研究中心, 重庆 400044
Effects of Temperature in the New Compound Extrusion on Microstructures and Properties of AZ61
ZHANG Ding-fei1,2, GENG Qing-mei1, YANG Xu-sheng1, YU Da-liang1, PAN Fu-sheng1,2
1. College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China;
2. National Engineering Research Center for Magnesium Alloys, Chongqing 400044, China
全文: PDF(1963 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 针对镁合金棒材的工业化制备和加工,提出了一种新型的复合挤压方式,将正挤压(Extrusion)和剪切(Shear)结合(简称ES)。对经过不同温度下ES变形后AZ61镁合金棒材进行微观组织观察、硬度测试、室温拉伸性能测试及SEM,研究了ES变形工艺中变形温度对AZ61挤压棒材组织及性能的影响。结果表明:温度由380℃升至400℃时,动态再结晶进行得更充分,组织为细小等轴晶粒,但温度升至440℃时,晶粒出现长大;三个温度下断口均呈现塑性断裂特征,400℃时棒材的综合力学性能最好,其抗拉强度为296.7MPa,屈服强度为158.9MPa,伸长率为15.4%。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
张丁非
耿青梅
杨绪盛
余大亮
潘复生
关键词 AZ61镁合金ES变形微观组织力学性能    
Abstract:A new composite extrusion (shorten ES) combining extrusion and shear was presented, for the industrial preparation and process of magnesium alloy rods. Microstructures, hardness test, tensile test and SEM experiments were used to investigate the effects of temperature on microstructure and properties of AZ61 magnesium alloy deformed by ES. The results show that, when the temperature increases from 380℃ to 400℃,dynamic recrystallization becomes more fully and more recrystallized grains are generated. But when the temperature rises to 440℃, grains grow up. The fractography shows ductile fracture characteristics under these three temperatures. And at the temperature of 400℃, the bars have the best comprehensive mechanical properties with tensile strength of 296.7MPa, yield strength of 158.9MPa and elongation of 15.4%.
Key wordsAZ61 magnesium alloy    ES    microstructure    mechanical property
收稿日期: 2013-03-27     
1:  TG146.2  
基金资助:国家973重大基础研究项目(2013CB632200);国家十二五科技支撑计划项目(2011BAE22B01-3);科技部国际合作项目(2010DFR50010);国家自然科学基金(51101176)
通讯作者: 张丁非(1963-)男,教授,博导,从事轻合金材料及加工技术研究,联系地址:重庆市沙坪坝区重庆大学材料科学与工程学院(400044),E-mail:zhangdingfei@cqu.edu.cn     E-mail: zhangdingfei@cqu.edu.cn
引用本文:   
张丁非, 耿青梅, 杨绪盛, 余大亮, 潘复生. 新型复合挤压工艺中温度对AZ61组织和性能的影响[J]. 材料工程, 2014, 0(7): 1-4.
ZHANG Ding-fei, GENG Qing-mei, YANG Xu-sheng, YU Da-liang, PAN Fu-sheng. Effects of Temperature in the New Compound Extrusion on Microstructures and Properties of AZ61. Journal of Materials Engineering, 2014, 0(7): 1-4.
链接本文:  
http://jme.biam.ac.cn/jme/CN/10.11868/j.issn.1001-4381.2014.07.001      或      http://jme.biam.ac.cn/jme/CN/Y2014/V0/I7/1
[1] LI B, JOSHI S, AZEVEDO K, et al. Dynamic testing at high strain rates of an ultrafine-grained magnesium alloy processed by ECAP [J]. Materials Science and Engineering: A, 2009, 517(1-2): 24-29.
[2] HORITA Z, MATSUBARA K, MAKII K, et al. A two-step processing route for achieving a superplastic forming capability in dilute magnesium alloys [J]. Scripta Materialia, 2002, 47(4): 255-260.
[3] YAMASHITA A, HORITA Z, LANGDON T G. Improving the mechanical properties of magnesium and a magnesium alloy through severe plastic deformation [J]. Materials Science and Engineering: A, 2001, 300(1-2): 142-147.
[4] HU H J, ZHANG D F, ZHANG J P. Microstructures in an AZ31 magnesium alloy rod fabricated by a new SPD process based on physical simulator [J]. Trans Nonferrous Met Soc China, 2010,(3): 478-483.
[5] 陈振华, 夏伟军, 严红革, 等. 变形镁合金 [M]. 北京:化学工业出版社, 2005.
[6] XU S W, KAMADO S, MATSUMOTO N, et al. Recrystallization mechanism of as-cast AZ91 magnesium alloy during hot compressive deformation [J]. Materials Science and Engineering: A, 2009, 527(1-2): 52-60.
[7] CHINO Y, SASSA K, MABUCHI M. Texture and stretch formability of a rolled Mg-Zn alloy containing dilute content of Y [J]. Materials Science and Engineering: A, 2009, 513-514: 394-400.
[8] SHI B Q, CHEN R S, KE W. Effects of forging processing on the texture and tensile properties of ECAEed AZ80 magnesium alloy [J]. Materials Science and Engineering: A, 2012, 546: 323-327.
[9] 张广俊, 龙思远, 曹凤红. AZ61镁合金在不同挤压温度下的组织与力学性能 [J]. 特种铸造及有色合金, 2009,(3): 270-272.ZHANG G J,LONG S Y,CAO F H. Microstructures and mechanical properties of AZ61 magnesium alloy extruded at different temperatures[J]. Special Casting & Nonferrous Alloys, 2009,(3): 270-272.
[10] 钟皓, 陈琪, 闫蕴琪, 等. AZ31镁合金的热挤压组织与力学性能分析 [J]. 轻金属, 2007,(3): 52-55. ZHONG H,CHEN Q,YAN Y Q,et al. Analysis of microstructures and mechanical properties of hot extruded AZ31 magnesium alloy[J]. Light Metals, 2007,(3): 52-55.
[1] 林翠, 赵晴, 文庆杰. TC1钛合金的腐蚀加工及其对基体性能影响[J]. 材料工程, 2015, 43(7): 48-55.
[2] 李龙, 祝志超, 张心金, 刘会云. 利用控轧控冷技术开发热轧不锈钢复合板的实验研究[J]. 材料工程, 2015, 43(7): 62-67.
[3] 江陆, 孙新军, 李昭东, 雍岐龙, 王长军. 两相区回火温度对Mn-Mo系微合金钢亚稳奥氏体形成及力学性能的影响[J]. 材料工程, 2015, 43(5): 1-7.
[4] 万同, 杨光瑞, 张婕, 王彪. 柠檬酸醚酯增塑剂的合成及增塑聚乳酸[J]. 材料工程, 2015, 43(5): 67-74.
[5] 刘铭, 汝继刚, 臧金鑫, 张坤, 何维维, 王亮, 陈高红. 新型Al-Zn-Mg-Cu铝合金热稳定性研究[J]. 材料工程, 2015, 43(4): 13-18.
[6] 马彦, 陈朝辉. 1800℃热处理对PIP法C/SiC复合材料结构和性能的影响[J]. 材料工程, 2015, 43(4): 98-101.
[7] 傅田, 李文亚, 杨夏炜, 李锦锋, 高大路. 搅拌摩擦点焊技术及其研究现状[J]. 材料工程, 2015, 43(4): 102-114.
[8] 彭建, 彭毅, 韩韡, 潘复生. 挤压温度对Mg-2Zn-Mn-0.5Nd镁合金组织和性能的影响[J]. 材料工程, 2015, 43(3): 23-27.
[9] 张同环, 周仕学, 牛海丽, 肖成柱, 王乃飞. 碳助磨制备纳米镁铝储氢合金的结构及储氢性能研究[J]. 材料工程, 2015, 43(3): 48-53.
[10] 刘鹏, 李士凯, 张元彬, 刘燕. 非晶增强铝基复合材料的微观结构及腐蚀性能[J]. 材料工程, 2015, 43(3): 67-71.
[11] 刘正, 董阳, 毛萍莉, 于金程. 轧制AZ31镁合金板材(4mm)动态压缩性能与失效行为[J]. 材料工程, 2015, 43(2): 61-66.
[12] 李万青, 魏红梅, 何鹏, 高丽娇, 林铁松, 李小强, 赫兰春. Ti3Al和Ti2AlNb合金扩散连接界面的组织及力学性能[J]. 材料工程, 2015, 43(1): 37-43.
[13] 王艳晶, 柳乐, 宋玫锦. Y微合金化高铌TiAl基合金微观组织研究[J]. 材料工程, 2015, 43(1): 66-71.
[14] 王洁, 聂宝华, 蔡成, 张峥. 加氢反应器环境服役的2.25Cr1Mo钢性能退化研究[J]. 材料工程, 2015, 43(1): 82-88.
[15] 杜红燕, 李亚江. AZ31/7005异种材料填丝GTAW焊接接头的组织与性能[J]. 材料工程, 2014, 0(9): 14-19.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn