空气和腐蚀环境下双相不锈钢SAF2507的疲劳性能
俞树荣, 孟恺, 李淑欣
兰州理工大学 石油化工学院, 兰州 730050
Fatigue Properties of Duplex Stainless Steel SAF2507 Under Air and Corrosive Environments
YU Shu-rong, MENG Kai, LI Shu-xin
School of Petrochemical Engineering, Lanzhou University of Technology, Lanzhou 730050, China
全文: PDF(3808 KB)   HTML()
输出: BibTeX | EndNote (RIS)      
摘要 对超级双相不锈钢SAF2507分别在空气和3.5%NaCl溶液中进行旋转弯曲疲劳实验,研究两种介质下SAF2507不锈钢的疲劳性能.结果表明:宏观上,双相不锈钢SAF2507在3.5%NaCl腐蚀环境中的疲劳强度较空气中的下降幅度小,为空气下的90%.但微观上,空气中疲劳断口表现为韧性断裂,在铁素体和奥氏体相上呈现大量疲劳辉纹;腐蚀环境下,奥氏体为韧性断裂,而铁素体呈现解理断裂模式.两相上疲劳辉纹的宽度和间距随着晶粒位向及二次裂纹的开裂而不同.在奥氏体-铁素体双相不锈钢的疲劳断口中,不能根据疲劳辉纹的间距进行相的鉴别.
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
俞树荣
孟恺
李淑欣
关键词 双相不锈钢腐蚀疲劳疲劳辉纹韧性断裂    
Abstract:Rotating bending fatigue tests were conducted on the super duplex stainless steel of SAF 2507 to investigate fatigue properties in both air and 3.5%NaCl aqueous environment. The results show that on the macro scale, compared to the air fatigue, there is no significant reduction in the fatigue strength of SAF2507 under corrosive environment, which is 90% of the air fatigue strength. But on the micro scale, the fatigue failure exhibits ductile fracture with fatigue striations observed in both ferrite and austenite in air. While in 3.5%NaCl, austenites have ductile fracture and ferrites exhibit cleavage fracture mode. The width and space between fatigues striations vary with grain orientations and second cracks, indicating that ferrite and austenite phase on fracture surface could not be identified simply by fatigue striations space.
Key wordsduplex stainless steel    corrosion fatigue    fatigue striation    ductile fracture
收稿日期: 2013-12-13     
1:  TG142.71  
基金资助:国家自然科学基金资助项目(51275225);兰州理工大学红柳杰出青年计划(J201302);国家质检公益性行业科研专项"基于风险管理的海洋石油平台压力管道安全评定研究"(201210026);甘肃省高等学校基本科研经费(2013.116)
通讯作者: 俞树荣(1962-),男,教授,博士,研究方向:承压类特种设备强度与安全,联系地址:甘肃省兰州市七里河区兰工坪路287号兰州理工大学石油化工学院(730050),mengkai117@126.com     E-mail: mengkai117@126.com
引用本文:   
俞树荣, 孟恺, 李淑欣. 空气和腐蚀环境下双相不锈钢SAF2507的疲劳性能[J]. 材料工程, 2015, 43(1): 77-81.
YU Shu-rong, MENG Kai, LI Shu-xin. Fatigue Properties of Duplex Stainless Steel SAF2507 Under Air and Corrosive Environments. Journal of Materials Engineering, 2015, 43(1): 77-81.
链接本文:  
http://jme.biam.ac.cn/jme/CN/10.11868/j.issn.1001-4381.2015.01.014      或      http://jme.biam.ac.cn/jme/CN/Y2015/V43/I1/77
[1] 吴玖. 双相不锈钢[M].北京: 冶金工业出版社, 1999.WU J. Duplex Stainless Steel[M]. Beijing: Metallurgical Industry Press, 1999.
[2] 邹德宁, 韩英, 张威,等. 高温时效对2507超级双相不锈钢组织和性能的影响[J].材料热处理学报,2010, 31(6): 73-76.ZOU D N, HAN Y, ZHANG W, et al. Influence of high temperature aging on microstructure and properties of 2507 super-duplex stainless steel[J]. Transactions of Materials and Heat Treatment, 2010, 31(6): 73-76.
[3] 李少峰, 任学平, 李殊霞, 等. 固溶温度对2205双相不锈钢超塑性的影响[J].塑性工程学报,2013, 20(2):84-88.LI S F, REN X P, LI S X, et al. Effect of solution treatment on superplasticity of 2205 duplex stainless steel[J]. Journal of Plasticity Engineering, 2013, 20(2): 84-88.
[4] CALLIARI I, ZANESCO M, RAMOUS E. Influence of isothermal aging on secondary phases precipitation and toughness of a duplex stainless steel SAF 2205[J]. Journal of Materials Science, 2006, 41(22):7643-7649.
[5] ALVAREZ-ARMAS I, KRUPP U, BALBI M, et al. Growth of short cracks during low and high cycle fatigue in a duplex stainless steel[J]. International Journal of Fatigue, 2012, 41: 95-100.
[6] ALVAREZ-ARMAS I. Lowcycle fatigue behavior on duplex stainless steels[J]. Transactions of the Indian Institute of Metals, 2010, 63(2-3):159-165.
[7] BALBIA M, AVALOSA M, EL BARTALIB A, et al. Microcrack growth and fatigue behavior of a duplex stainless steel[J]. International Journal of Fatigue, 2009, 31(11-12): 2006-2013.
[8] LO I H, TSAI W T. Effect of selective dissolution on fatigue crack initiation in 2205 duplex stainless steel[J]. Corrosion Science, 2007, 49(4): 1847-1861.
[9] 高镇同,熊峻江. 疲劳可靠性[M].北京:北京航空航天大学出版社, 2000.GAO Z T, XIONG J J. Fatigue Reliability[M].Beijing: Beihang University Press, 2000.
[10] 寇生中,张亚男,魏代钢,等. 00Cr25Ni8Mo3CuN双相不锈钢的组织和性能研究[J]. 热加工工艺, 2009, 38(18): 29-31. KOU S Z, ZHANG Y N, WEI D G, et al. Study on microstructure and properties of 00Cr25Ni8Mo3CuN duplex stainless steel[J]. Hot Working Technology, 2009,38(18): 29-31.
[11] MAKHLOUF K, SIDHOM H, TRIGUIA I,et al. Corrosion fatigue crack propagation of a duplex stainless steel X6CrNiMoCu 25-6 in air and in artificial seawater[J]. International Journal of Fatigue, 2003, 25(2): 167-179.
[12] MARROW T J, KING J E. Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels[J]. Fatigue and Fracture of Engineering Materials and Structures, 1994, 17(7): 761-771.
[13] KRISHNAN K N. Mechanism of corrosion fatigue in super duplex stainless steel in 3.5 percent NaCl solution[J]. International Journal of Fracture, 1997, 88(3): 205-213.
[14] PARK C J, SHANKAR-RAO V, KWON H S. Effects of sigma phase on the initiation and propagation of pitting corrosion of duplex stainless steel[J]. Corrosion, 2005, 61(1): 76-83.
[15] 赵志毅, 徐林, 李国平, 等. 超级双相不锈钢σ相析出及对组织性能的影响[J]. 材料热处理学报, 2010, 31(10): 75-79. ZHAO Z Y, XU L, LI G P, et al. Precipitation behavior of σ-phase and its effect on microstructure and properties of a super duplex stainless steel[J]. Transactions of Materials and Heat Treatment, 2010, 31(10): 75-79.
[16] 雒设计,郑新侠. 敏化处理对2205双相不锈钢组织与力学性能的影响[J]. 材料工程, 2011, (5): 76-80. LUO S J, ZHENG X X. Effects of sensitizing treatment on microstructure and mechanical properties of 2205 duplex stainless steel[J]. Journal of Materials Engineering, 2011, (5): 76-80.
[1] 马少华, 回丽, 周松, 许良, 朱永辉. 腐蚀环境对预腐蚀铝合金腐蚀疲劳性能的影响[J]. 材料工程, 2015, 43(2): 91-95.
[2] 陈影, 付宁宁, 沈长斌, 葛继平. 5083铝合金搅拌摩擦焊搭接接头研究[J]. 材料工程, 2012, 0(6): 24-27.
[3] 雒设计, 郑新侠. 敏化处理对2205双相不锈钢组织与力学性能的影响[J]. 材料工程, 2011, 0(5): 76-80.
[4] 赵才, 江海涛, 唐荻, 赵松山, 程知松. Q&P钢塑性变形机制及组织-性能研究[J]. 材料工程, 2009, 0(2): 19-23.
[5] 韩志诚, 王少刚, 胡经洪, 徐风林. 焊接工艺对2205双相不锈钢接头组织与性能的影响[J]. 材料工程, 2008, 0(8): 48-51,56.
[6] 张建勋, 李庆琰, 李为卫, 张田宏, 刘亚旭. 热模拟2205DSS焊接HAZ的点蚀实验研究[J]. 材料工程, 2006, 0(8): 28-32.
[7] 姜忠良, 吴严, 陈秀云, 白飞明, 刘秀赢, 黄铁光. 热处理细化δ/γ双相不锈钢晶粒的研究[J]. 材料工程, 2002, 0(5): 30-33.
[8] 张峥, 苏梅, 钟群鹏. 鼓风机转子叶轮失效分析[J]. 材料工程, 2001, 0(5): 41-43,33.
[9] 丁传富, 李谦. 腐蚀环境和孔挤压强化对300M超高强度钢疲劳性能的影响[J]. 材料工程, 1997, 0(5): 15-19.
[10] 陈美英, 牛康民, 尹和云. 几种高强度钢腐蚀疲劳裂纹扩展行为的研究[J]. 材料工程, 1994, 0(3): 38-41,44.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
版权所有 © 2015《材料工程》编辑部
地址:北京81信箱44分箱 邮政编码: 100095
电话:010-62496276 E-mail:matereng@biam.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn