Si3N4陶瓷-冷激铸铁在微量润滑条件下的摩擦学特性

PDF(1547 KB)

材料工程 ›› 2006, Vol. 0 ›› Issue (4) : 24-27,32.

扫码查看或转发全文

论文

Si₃N₄陶瓷-冷激铸铁在微量润滑条件下的摩擦学特性

项忠霞¹, 董刚², 林彬¹, 沈兆光¹

作者信息 +

Tribological Characteristics of Silicon Nitride-chilled Cast Iron with Oil-less Lubrication

XIANG Zhong-xia¹, DONG Gang², LIN Bin¹, SHEN Zhao-guang¹

Author information +

文章历史 +

摘要

利用MG-200型高速高温摩擦磨损试验机,采用块-盘式实验方法,对Si₃N₄陶瓷-冷激铸铁摩擦副从室温到150℃进行了微量润滑摩擦磨损实验,得到了该摩擦副的摩擦系数和Si₃N₄陶瓷的磨损率.同时根据试件的SEM照片和能谱成分分析了摩擦磨损机理,并与无润滑时所得实验结果进行了比较.结果表明:微量润滑条件下Si₃N₄陶瓷的磨损率和摩擦系数要比无润滑条件下小的多;Si₃N₄陶瓷的磨损率随载荷和温度的增大而增大,滑动速度的影响要小于载荷的影响;该摩擦副的摩擦系数随环境温度的提高而增大,随速度的增大而减小,载荷的变化对其影响不大;Si₃N₄陶瓷的磨损是化学磨损、机体物质脱落和磨粒磨损共同作用的结果,其中化学磨损是引起其他两类磨损的主要原因.

Abstract

The friction and wear tests for mated couples of silicon nitride(Si₃N₄)and chilled cast iron under the oil-less lubrication were carried out by means of block-on-disc with MG-200 wear machine from room temperature to 150℃,the friction coefficients of mated couples and wear rates of Si₃N₄ were gained,and the friction and wear behaviors were analyzed by the wear rates,friction coefficients,SEM images and percentages of chemical elements on worn surfaces.The results showed that the wear rate of Si₃N₄ and friction coefficient between Si₃N₄ and chilled cast iron with oil-less lubrication are much less than those with dry friction condition;the wear rate of Si₃N₄ increases with the increase of load and temperature,and the effect of sliding speed on wear rate of Si₃N₄ is not as significant as the effect of load;the friction coefficient between Si₃N₄ and chilled cast iron decreases with sliding speed,but increases with temperature,and the load has little effect on friction coefficient;the wear of Si₃N₄ is caused by interaction of chemical wear,abradant wear and particles' peeling off,and chemical wear is origin in other two.

导出引用

项忠霞, 董刚, 林彬, 沈兆光. Si₃N₄陶瓷-冷激铸铁在微量润滑条件下的摩擦学特性[J]. 材料工程, 2006, 0(4): 24-27,32

XIANG Zhong-xia, DONG Gang, LIN Bin, SHEN Zhao-guang. Tribological Characteristics of Silicon Nitride-chilled Cast Iron with Oil-less Lubrication[J]. Journal of Materials Engineering, 2006, 0(4): 24-27,32

中图分类号： TQ174.758

参考文献

[1] 北英纪(日).低摩擦、低磨损陶瓷的开发[J].王冰,梅长虹编译.国外金属加工,2004,25(2):1-4.
[2] GAO Y M,FANG L,SU J Y.The effect of tribofilm formation on the characteristics of ceramic-cast iron sliding pairs[J].Wear,1997,210:1-7.
[3] 翟文杰,王闯.Si₃N₄陶瓷电化学研磨特性及机理分析[J].摩擦学学报,2004,24(4):360-363.
[4] 刘维民.聚乙烯醇及磷酸脂气象润滑下Si₃N₄陶瓷的磨损特性研究[J].摩擦学学报,1998,18(2):108-112.
[5] 斯松华,方亮,高义民,等.Si₃N₄陶瓷与灰铸铁配副的摩擦学性能[J].摩擦学学报,1997,17(1):32-37.
[6] KANO M,TANIOTO I.Wear resistance properties of ceramic rocker arm pads[J].Wear,1991,145:153-165.
[7] 吴明明,肖俊建.Si₃N₄陶瓷在现代制造业中的应用[J].佛山陶瓷,2004,14(5):30-32.
[8] 任靖日,李花,金石三.高温下氮化硅的摩擦学性能研究[J].延边大学学报,2003,29(3):212-215.
[9] OGAWA Y,MACHIDA M,MIYAMURA N,et al.Ceramic rocker arm insert for internal combustion engines[C].New York:Society of Automotive Engineers,1986.
[10] 高义民,方亮,苏俊义,等.蒸馏水润滑下Si₃N₄-冷激铸铁摩擦面上表面膜的分析[J].西安交通大学学报,1997,32(2):77-83.
[11] 项忠霞,陈树昌,王铮,等.Si₃N₄陶瓷/冷激铸铁的摩擦学性能研究[J].摩擦学学报,2000,20(3):183-185.
[12] XIANG Z X,DONG G,ZHANG Y H,et al.Analysis on wear properties and impact factors for Si₃N₄ ceramic mated with chilled cast iron[A].Proceedings of 11th World Congress in Mechanism and Machine Science[C].Beijing:China Machine Press,2004.2306-2310.