利用碳和碱土金属(Ca和Sr)对Mg-3Al合金进行单独或复合细化处理,研究其晶粒细化效果及其晶粒细化对Mg-3Al合金抗拉强度特性的影响规律。结果表明:0.2%C(质量分数,下同)、0.2%Ca及0.2%Sr均可显著细化Mg-3Al合金,而经0.2%C与0.2%Ca或0.2%Sr复合细化可进一步提高细化效果。细化后Mg-3Al合金的拉伸性能明显提高,经复合细化后合金的极限抗拉强度和断裂伸长率分别提高了20%和40%。晶粒细化影响Mg-3Al合金的断裂机制,由具有粗大解理面的解理断裂模式转变为解理和准解理的混合断裂模式。
Abstract
The Mg-3Al alloy was modified by 0.2%C(mass fraction) and/or alkaline-earth elements of 0.2%Ca or 0.2%Sr to refine its grain size.The effect of grain refinement on the tensile properties of the Mg-3Al alloy was investigated.The results show that higher grain refining efficiency can be obtained for the Mg-3Al alloy modified by the combination of carbon and alkaline-earth elements.Compared to the Mg-3Al alloy without any treatment,the tensile properties of the Mg-3Al alloy are remarkably improved after being modified by the combination of carbon and a little addition of alkaline-earth elements.The ultimate tensile strength and elongation to failure are improved by about 20% and 40%,respectively.After being refined either by carbon or by the combination of carbon and a little addition of alkaline-earth elements,the main fracture mechanism is changed from cleavage mode with large cleavage planes for the unrefined Mg-3Al alloy to mixed mode of cleavage and quasi-cleavage fracture.The fracture surfaces are almost composed of small cleavage planes with thin river patterns and quasi-cleavage planes with severe plastic deformation.
关键词
Mg-Al合金 /
晶粒细化 /
碱土元素 /
碳 /
拉伸性能
{{custom_keyword}} /
Key words
Mg-Al alloy /
grain refinement /
alkaline-earth element /
carbon /
tensile property
{{custom_keyword}} /
中图分类号：
TG146.2+2
{{custom_clc.code}}
({{custom_clc.text}})
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 陈礼清,赵志江.从镁合金在汽车及通讯电子领域的应用看其发展趋势[J].世界有色金属,2004,(5):12-20.
[2] DU J D,HAN W J,PENG Y H.Life cycle greenhouse gases,energy and cost assessment of automobiles using magnesium from Chinese Pidgeon process[J].Journal of Cleaner Production,2010,18(2):112-119.
[3] 张世军,黎文献,余琨.添加含碳熔刺细化镁合金晶粒的方法[J].特种铸造及有色合金,2002,(4):18-20.
[4] WANG Z H,KANG Y L,ZHAO H J,et al.Grain refinement of Mg-Al magnesium alloys by carbon inoculation[J].Transactions of Nonferrous Metals Society of China,2006,16 (S3):1851-1854.
[5] ST JOHN D H,MA Q,EASTON M A,et al.Grain refinement of magnesium alloys[J].Metallurgical and Materials Transactions A,2005,36(7):1669-1679.
[6] BAI J,SUN Y S,XUN S,et al.Microstructure and tensile creep behavior of Mg-4Al based magnesium alloys with alkaline-elements Sr and Ca additions[J].Materials Science and Engineering A,2006,419(1/2):181-188.
[7] ZENG X Q,WANG Y X,DING W J,et al.Effect of strontium on the microstructure,mechanical properties,and fracture behavior of AZ31 magnesium alloy[J].Metallurgical and Materials Transactions A,2006,37(4):1333-1341.
[8] LU L,DAHLE A K,ST JOHN D H.Grain refinement efficiency and mechanism of aluminium carbide in Mg-Al alloys[J].Scripta Materialia,2005,53(5):517-522.
[9] TAMURA Y,YANO E,MOTEGI T,et al.Effect of carbon powder on grain refinement of an AZ91E magnesium alloy[J].Materials Transactions,2003,44(1):107-110.
[10] LEE Y C,DAHLE A K,ST JOHN D H.The role of solute in grain refinement of magnesium[J].Metallurgical Materials Transactions A,2000,31(11):2895-2906.
[11] SRNIVASAN A,PILLAI U T S,PAI B C.Microstructure and mechanical properties of Si and Sb added AZ91 magnesium alloy[J].Metallurgical Materials Transactions A,2005,36(8):2235-2243.
[12] KOIKE J,KOBAYASHI T,MUKAI T,et al.The activity of non-basal slip systems and dynamic recovery at room temperature in fine-grained AZ31B magnesium alloys[J].Acta Materialia,2003,51(7):2055-2065.
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}
基金
国家自然科学基金项目(50901034);华南理工大学中央高校基本科研业务费专项资金项目(2009ZM0305);广东省自然科学基金项目(05300139)
{{custom_fund}}
PDF(1542 KB)